The production and processing of new materials are an important part of our economy. The engineers must design products and the processes needed for its manufacture. The raw materials (materials) are transformed to products into processes. It is important to know the structure and properties of materials in order to select the most suitable materials for each application and develop the best methods for processing. The research and development engineers working to create new materials or to modify existing properties, the design engineers and others use some materials to design and create new products and systems [1] .

Composite materials are classified based on matrix used. There are composite materials using metals, polymers or ceramics as matrix. In the present research was obtained a new composite material which uses polyester resin as polymeric matrix. Another classification of composite materials is according to the form of reinforcement or filler. Some composite materials could be classified as particulates, short fibers, continuous fibers or layered sheet [2] . High density polyethylene particulates were added as filler material in the developed polymeric concrete.

The polymer mixtures are mechanical combinations of polymers; such combinations do not depend on chemical bonds, but typically require compatibilizers that prevent the segregation of components. Typically maintained in the mixtures are some of the individual properties (impact resistance, weather resistance, better performance at low temperatures and flame delay) and in many cases the objective is to find two or more components which improve one or more of them. Recent researches are focused on the combination of polymers to obtain polymer mixtures and plastic alloys by use of coupling agents or compatibilizers as silanes, titanates and thermoplastic rubbers [3] .

The polymer concrete (PC) developed is a new composite material (CM) considered as an alternative material in the construction industry. The reinforcement particles have approximately the same dimensions in all directions. The particles can be rods, spheres, flake and many other shapes whose size are about 10 microns. Size, shape and distribution can affect the properties of the CM.

Thermogravimetric analysis (TGA) was based on the measurement of the temperature changes that occur in a substance, either by chemical reactions or physical changes. TGA is a technique by which a sample is weighed and continuously heated at a controlled rate. The weights of samples change when the temperature increases. The resulting curve is called thermogram. The thermogram provides information about the thermal stability and composition of the original sample, the composition and stability of intermediates and the waste composition. Each material has its corresponding thermogram allowing identification [4] .

Raw material: polyethylene microparticles mechanically recycled high density, polyester resin, calcium carbonate.

Sample preparation RM CP with PET: a homogeneous mixture is made containing polyester resin and calcium carbonate microparticles recycled HDPE mechanically conventional mill in proportion (1:1:1) is poured into molds of polyethylene high density and allowed to dry at room temperature (28˚C) for about 6 hours. Figure 1 presents a flow chart for sampling with HDPE RM CP and testing or analysis for the characterization of the composite.

Thermogravimetric analysis (TGA): in an alumina crucible placed 0.01 g of powder with HDPE CP RM, which is placed in the sample holder for thermogravimetric analysis team flag previously calibrated SDT Q600 model, which is shown in Figure 2. The computer software program using temperature records begin in the range of 20˚C to 180˚C at a rate of heating 1˚C/minute.

Differential thermal analysis (DTA).

Figure 3 shows the thermogravimetric analysis of the raw material (filler in polymer concrete) particulates of recycled high density polyethylene mechanically.

Figure 4 shows the thermogravimetric analysis of composite materials (polymer concrete with recycled high density polyethylene mechanically).

Microparticles HDPE mechanically recycled have a glass transition temperature (T_g) at 38˚C. The polymer concrete has a T_g of 46˚C.

Microparticles of high density polyethylene obtained by mechanical recycling have an initial weight loss at 59˚C (T_WP) and the end weight loss at 126˚C (T_WT). The final weight loss of HDPE sample was 4˚C before melting temperature.

The PC has partial weight loss at 86˚C (T_WP). The T_WP of PC probably increases due to content of calcium carbonate as inert material.

The HDPE particulates have a melting temperature (T_f) of 130˚C and HDPE-PC have a T_f = 128˚C.

The polymer concrete with high density polyethylene (HDPE-PC) is classified as a polymeric composite and

is considered as a thermoplastic. HDPEPC developed can be softened, processed and reprocessed by the temperature and pressure modification, allowing the desired shape.

The thermal analysis methods are of great importance for the characterization of the thermoplastic materials, due to the large ratio between their properties and temperature. The thermogravimetric analysis measures the weight change of sample under isothermal conditions, or under programmed heating, usually in a linear behavior.

In the SDT-600 equipment the deflection of the balance scale is automatically compensated by an electrical modulator unit by suitable sensors typically thermocouples; it is achieved that the electrical signal is directly proportional to the variation in weight of the sample.

This method is used primarily to investigate mixtures of organic substances as in many cases. The range of the decomposition temperature makes possible the identification and characterization of the specimen by recording the glass transition temperature and weight loss.