Most applications in engineering do deal with minimum shielding effectiveness. For this singular reason, the understanding and selection of materials for effective shielding are vital in both design and fabrication. Material behaviour to electromagnetic interference field is of immense importance, especially in areas of medical applications, military hardware, electronics, telecommunication industries and other shielding applications. Most casing or packaging for electrical and electronic devices is polymeric in nature. High amongst polymer characteristics are simplicity of fabrication, light weight, low cost, and excellent insulating property and these have made plastics one of the most suitable materials for electrical and electronics applications. The function of plastics in electrical and electronic applications was limited to no-load bearing general-purpose applications [1].

Based on this quality of polymer, the scientific community has delved into numerous researches to understanding polymeric compounds and substrates. With this development, polymer composite is the major player in the fabrication of novel materials good for a variety of different applications, such as electrical engineering and high frequency devices like microwave especially to shielding applications, microwave absorption and electromagnetic interference (EMI), electrodes and sensors [2].

The reinforcement of polymers using different types of organic or inorganic fillers is common practice in the production of systems with improved mechanical, dielectric properties [3]. Micrometer-sized inorganic particles are commonly used for the reinforcement of polymer matrices to improve thermal conductivity, and meet mechanical requirements. Properties of the polymer composites are affected by factors, like inherent characteristics of each component, contact, dimension and shape of the fillers, and the nature of their interfaces [4].

Knowledge of materials behavior placed in an electromagnetic field is of immense importance especially when it relates to military hardware, electronics, communication, and industrial applications and shielding [5]. The measurement of transmission coefficient of materials in the microwave frequency range is found in several areas. It is vital that transmission coefficient measurement is fully understood so as to enable satisfactory attenuation measurements of materials good for microwave absorption. Attenuation is a function which can be affected by a group of factors. For this study, concentration is based on the effect of the filler content on the matrix.

In this work, wood-polymer composite structures were synthesized, and investigation on electromagnetic propagation, absorption properties of the substrate at 8 - 12 GHz with thickness of 10 mm was carried out. The microwave properties of samples were investigated by using rectangular waveguide connected with vector network analyzer via coaxial cable. Attenuation of wood-PCL micro-composites at filler contents of (12.5%, 22.5%, 37.5%, 50%, and 62.5%) were investigated in this work. The total volume fraction of the composites was set at 40 g.

Wood polymer composites materials were prepared via melt-blend technique by mixing the wood filler to PCL. The materials were weighed according required composition (Table 1). For the preparation of the samples used in this study, the followings were used; wood dust (99.9%) purity, (Sigma, Aldrich), Polycaprolactone, PCL (C₆H₁₀O₂) 97.0% purity, with density of 1.146 g/cm³ (Sigma Aldrich).

The wood-PCL composites was prepared via the melt blend technique using the Thermo Haake extruder Polydrive three-phase motor with a drive of 1.5 kW, 3 × 230 V, 40 A and speed range of 0 - 120 rpm. In this method, the Thermo Haake machine is set to desire heating temperature and allowed to heat up. All other components of the machine are set following recommended settings. For our method, the machine is set to 90˚C for heating, the rotation of the rotors was set to 50 rpm. After the machine has reached the required temperature (80˚C) because it was close to the melt point (60 - 70)˚C of PCL.

The polycaprolactone (PCL) is poured into the vial of the Thermo Haake heating block. After 5 minutes, the wood dust is introduced into the vial. The mixture is left for another 20 minutes before taken out and fabricated into desired dimension using hot and cold press. Table 1 illustrates the ratio of blending.

The material under test is inserted in a piece of transmission line, and the properties of the material are deduced on the basis of the rejection from the material and the transmission through the material [6] [7]. The fringes of the field of reflection due to this material are used to calculate its transmission and reflection coefficients. The method of using transmission lines in measurement is for accuracy of results since microwave guides have field focusing ability [8]. For this study, sample is placed between two waveguides and excited with electromagnetic radiation.

For the transmission coefficient measurement, a 10 mm sample was placed carefully inside the RWG which then connected via a coaxial cable to network

analyzer (Agilent 8570B). For instrument validity, the waveguide was used to measure air and PTFE since both are standard materials. The specimen dimensions are machined to fit as tightly as possible into the waveguide removing any possibility for air gap between the sample and the guide around the sample walls.

Shown in Figure 1 is the measurement set up, showing the RWG.

Figure 2 is the measured scattering parameter for the standard material (air). The result showed that the transmission coefficient is higher in magnitude than the reflection coefficient. Theoretically, the value of the transmission coefficient should be close to unity [9].

The scattering or S parameters of a two-port network are defined in terms of the wave variables [10].

Of importance is the nomenclature used for the scattering parameters. The parameters S₁₁ and S₂₂ are called the reflection coefficients, whereas S₁₂ and S₂₁ are called the transmission coefficients. These are the parameters directly measurable at microwave frequencies. Generally, the S parameters are written in complex form as [10] ;

S g g = b g a g ( g = 1 , 2 ) (1)

S p g = b p a p   ( p ≠ g ; p = 1 , 2 ; g = 1 , 2 )

The reflection coefficient;

Γ g = S g g = b g a g (2)

The transmission coefficient;

T g → p = S P P = b p a p (3)

The result obtained via the Vector Network Analyzer (VNA) for the transmission coefficients (S₂₁) is then used to compute the attenuation of the material under study using Equation (4).

A t t e n u a t i o n ( d B ) = − 20 log ( S 21 ) (4)

After carrying out the measurements, the raw data were used to plot a graph of S₂₁ against frequency.

Careful observation on Figure 3, shows that the transmission coefficients with respect to wood filler content sequential decreases as content increases. Thus, transmission coefficient decreases with increased wood content. This behavior is in agreement with theory that states that denser materials decrease transmission [11]. The highest value of transmission coefficients is recorded for the lowest ratio of filler at 5 g wood filler with the least value recorded for the highest ratio of filler at 25 g content. This result is in agreement with impedance mismatch theory, where materials with the highest permittivity depict lower transmission coefficient values [12].

Further observation in Figure 3 showed that transmission coefficient decreases as frequency increases for all samples. This might be attributed to perfect dispersion of the filler in the matrix. So the result, confirmed homogeneity of the particles dispersion in the matrix which will tend to increase or decrease the transmission of the electromagnetic radiation depending on the dispersion of wood dust in the matrix. However, the general result shows that the increase in

filler content decreases the magnitude of the transmission coefficient for all filler composition at all frequency ranges as evident in Figure 4.

Furthermore, the sinusoidal-like wave form over all frequency ranges was attributed to the impedance mismatched between the input impedance of the waveguide and the surface impedance of the sample as well as the characteristic impedance of the coaxial cable [13] [14].

To calculate the attenuation of the different wood-polymer pellets, raw data of the transmission coefficients was used. Equation (4) was then used to calculate the attenuation. The calculated result is then interpreted in Figure 5. Observation on Figure 5 shows that the least attenuation was calculated for the 12.5% wood filler content whereas the highest attenuation was calculated for the 62.5% filler content.

This result is in agreement with S₂₁ since the least transmitted composites have the largest absorption.

Figure 6 depicts the mean value of attenuation for all filler percentage. The graph shows a continued increase in attenuation as filler content increases. This behavior is in agreement with theory that states that, denser materials decrease transmission [15]. This behaviour might be attributed to the perfect dispersion

of the filler in the matrix, as the homogeneity of the particle dispersion in the matrix will tend to increase or decrease the attenuation of the EM radiation depending on the dispersion of the wood particles in the matrix [16].

The filler composites were analyzed using scanning electron microscopy (SEM) with a field emission gun and an accelerating voltage of 10 kV. Shown in Figure 7 is the micrographs for the 50% filler content. Complete dispersion of the wood dust into the polymer can be observed and this is attributed to good sample preparation technique.

Further observation reveals that wood particles are indeed dispersed as discrete particles in the polymer matrix. The compact wood particles are fully integrated in the composites on the entire fractured surface. The morphology indicates that wood particles have indeed reacted with the PCL evenly to produce wood-PCL composites [17].

The synthesis of wood-polymer was successfully achieved in this work. Investigation on the propagation of electromagnetic radiation through an RWG and

determination of material attenuation were carried out at microwave frequency. The work was limited to transmission coefficient, attenuation and surface morphology of the samples prepared.

Since shielding effectiveness is the process of using specialized materials to reduce EMI field or waves that enter a specific enclosure.

It is concluded that the material produced is good for microwave shielding applications in the range of 3.4 to 6.5 dB.

Based on the results obtained, the materials produced in this work can be tailored for electronics, telecommunication and medical industries.

The authors declare no conflicts of interest regarding the publication of this paper.

Yakubu, A., Abbas, Z. and Sirajo, A. (2020) Attenuation and Shielding Performance of Wood-Polymer Composites Synthesized via Melt-Blend Technique. Open Access Library Journal, 7: e5444. https://doi.org/10.4236/oalib.1105444