Phthalocyanines are regarded as optical materials. The optical film properties analysis explains the identity of materials and the correlation between theoretical and experimental work [1] . Inorganic materials have attracted attention as novel material due to their chemical stability, low heat conduction, and diversity of optical properties and wide application in optoelectronic devices [2] [3] . Phthalocyanine can be considered as active materials in different light processes [4] . By discovering phthalocyanine since 1907, many studies on the optical properties have been achieved [5] [6] . There is a great interest in studying the electronic structure of phthalocyanine because of its high absorption in the visible region [7] [8] [9] [10] . Phthalocyanine happens in three phases (α, β, γ); the molecules are distributed in a parallel to each other leading to forming vertical structure in α phase and β phase, and in α-phase, phthalocyanine contains crystalline grain with 10 nm of diameter, whereas β phase contains bigger crystalline grain and fiber optical structure and this phase is formed at higher temperature. Many methods have been used to prepare metal phthalocyanine films [11] . Most of the metals have been able to coordinate with the phthalocyanine. Metal phthalocyanine (MPc) has great attractive as catalysts for organic chemical sensor and solar cell application due to simple prepared technique, low cost and stability for chemical and thermal properties [8] . NiPCs have α-phase and monoclinic structure, with β = 123.46˚ and lattice constant a = 1.513 nm, b = 0.462 nm, c = 2.03 nm [9] . Organic semiconductor NiPCs contain single bond and double bonds [10] . The microscopic characteristic of the material can be known by studying optical measurements of film and this gives important information to build electronic devices [12] . The objectives of this work are the synthesis of thermally evaporated NiPc film using thermal evaporation technique, to study some of the properties at various T_s, also to prepare solar cell from n-Nickel Phthalocyanine: p-Silicon HJ and to study their properties.

NiPc thin films at different substrate (300 - 450 K) were prepared by thermal evaporation (Edwards 306 systems) on (glass, n-Silicon) by using NiPc powder obtained from Aldrich chemical company. NiPc thin films were grown with a thicknesses of (50, 110, 265 and 350) nm on glass and on Si wafer substrates at room temperature. Also NiPCs film was grown in T_s (300, 325, 350, 400, 450) K with a thickness 265 nm, under vacuum pressure 10^–5 torr.

Fourier-transformed Infra-red spectra for NiPc as a powder were measured by (Shimadzu FTIR spectrometer). The optical property of NiPc film was determined in the range (200 - 1000) nm by using UV/V is spectrometer. Photoluminescence was measured (Renishaw 2000) system, and at excitation wavelengths of 300 nm. Electrical properties were measured, concentration and mobility of carrier and Hall effect of film were determined. NiPc/Si heterojunction has been fabricated as in Figure 1. Single crystal n-type Silicon wafer was used with phosphor doping, crystal orientation (100), thickness 380 μm and electrical resistivity of 5 - 10 Ω.cm. The wafer from VSM company, USA, Silicon wafer was cleaned using etching process by immersed Si wafer and stirrer them in a solution containing 3 ml HNO₃, 1 ml HF, 2 ml H₂O for (1 - 3) minutes, then immersed in distilled water for several times. Finally, it was dried by blower and swab in special paper. I-V and C-V(at1kHz) characteristic in the case of darkness and light were achieved for the NiPc/Si Hj cell by digital Keithley, power supply and LRC meter. Solar cell properties and there parameters (β, φ, V_oc, I_sc, Im, Vm, η etc..) have been achieved at light to the NiPc/Si HJ with optimum thickness and substrate temperature at forward and reverse conditions with intensity 55 mW/cm² by using Halogen lamp type Philips of 120 W.

The FT-IR spectra to NiPc as a material were recorded at RT, a comparison between these spectra of NiPc and H₂Pc spectra as in Figure 2. It is observed in the range (400 - 2000) cm⁻¹ bond bending whereas in the range (2000 - 4000) cm⁻¹ the bond stretching. Weak peaks in the range (600 - 400) cm⁻¹ which indicate the presence of (metal-Nitrogen) bond vibration at (508 - 578) cm⁻¹ which assigned for (Nickel-Nitrogen). The band C-N at (1334 - 1320) 1/cm is, and the peak bond C=C at (1612) cm⁻¹ and the peak (1533) cm⁻¹ represents Benzene ring band. The spectrum shows the absent of stretching band (N-H) which appears in (H₂Pc) spectrum.

The incident light (I_o) and transmission intensity (I_T) is given by [12] [13] :

I T = I o e − α t (1)

The absorption coefficient α and t is thickness of films. The α of film was calculated by absorption and transmission spectra according to:

α = ln T − 1 / t (2)

I_T/I_o is defined as the transmittance (T) [1] .

Figure 3 represents the absorbance for Nickel phthalocyanine film at various T_s, it is observed substrate temperature increasing causes absorbance decreases, normally, except in the range (350 - 400) K where there is inverse behavior for Q band and B band, and the variations in (Q) bands less than in B band and minor changes happens in flat area, this behavior because of a good crystal arrangement at high substrate temperatures. It is observed that band of absorption B higher from band of absorption Q. Effect of substrate temperature on absorbance is shown in Figure 4. A red shift in B, Q₁ bands peak positions with substrate temperature increasing has been seen while no change in Q₂ peak position as shown in Table 1.

Substrate temperature effect on transmittance was studied for NiPc thin films and shows that maximum transmittance was in the range (400 - 500) nm wavelength and clear variations happened in B and Q bands, while the small variations are in flat area. The transmittance spectra for NiPc film at various T_s, are shown in Figure 3 and Table 1.

Effect of substrate temperature on transmittance has been studied, one can see the transmittance increases normally with substrate temperature increase, except in the range of (350 - 400) K where there is a reverse behaviour, and Q band variation in transmittance is smaller than that for B band for same values of T_s as shown in Figure 3 and Table 1.

The reflectance spectra for NiPc film at Ts (300 - 450) K have been done, reflectance was calculated by

R = 1 − ( A + T ) (3)

the B and Q bands have high variations in R while the flat area has still minimum variations. At 450 K substrate temperature R takes the same values for wide range and for both bands. The reflectance spectra for NiPc film at various T_s were given in Figure 3 and Table 1.

Substrate temperature variations effect on reflectance of NiPc thin films, where reflectance increases by increase in T_s for B and Q bands except for the range of T_s (350 - 400) K. The reflectance of flat also plotted with T_s it seems to be that it behaves inversely. The effect of T_s on reflectance was given in Figure 4. The behaviour in Figure 4 may be due to recrystalization by increasing temperature and phase transition from β-phase to α-phase [15] [16] .

Figure 5 represents the variations in absorption coefficient (α) with wavelengths at various temperatures, the following equation gives α:

α = ( 2.303 ) A ⋅ t − 1 (4)

Absorption represents by (A), and (t) thickness, it is observed the flat area at the range (400 - 500) nm having the same values of absorption coefficient approximately, because this range is the high transmission range; while for B band, absorption coefficient becomes greater than 10⁴ cm⁻¹ which means high probability for direct transition. The high absorption coefficient in Q band is due to traps inside energy gap.

Effect of T_s for NiPc film was given in Figure 6, absorption coefficient decreases with substrate temperature increases, normally, except in the range (350 - 400) nm a reverse behaviour has been seen that is due to enhancement in crystal structure.

The absorption coefficient (α), and types of transition can be deduced from Tauc relation [14] :

α h υ = const . ( h υ − E g ) r (5)

where r is empirical constant depending on the transition types, where r is equal to 1/2 for allowed direct transition, and hυ represent photon energy which equals to [13] [14] :

h υ ( eV ) = 1.24 ⋅ λ − 1 ( μm ) (6)

Plank constant was h, υ is frequency, λ represents wavelength. By polting (αhυ)² against hυ for allowed direct transition, and the absorption coefficient α ≥ 10⁴ m^–1, the straight line indicating the transition is allowed direct. Extrapolation of the linear portion of the plot to the x axis (αhυ = 0) represent the values of energy gap as shown in Figure 7 [15] [16] .

Values of Eg increases with increasing substrate temperature slightly as given in Table 2. This is due to the decrease of defects and improvement in crystal structure of thin prepared films [15] [16] .

The optical constants for NiPc thin films at wavelength equal to 500 nm at different substrate temperatures were shown in Table 3.

The refractive index (n) can be evaluated from equations [13] [14] .

n = [ ( 4 R / ( R − 1 ) 2 ) − k 2 ] 1 / 2 − ( R + 1 ) / ( R − 1 ) (7)

where (R) is the reflectance. The extinction coefficient (k) is calculated from [13] [14] .

k = α λ / 4 π (8)

The dielectric constant is:

ε = ε 1 − i ε 2 = 1 + 4 π φ (9)

(φ) is the sum of polarizabilities resulting from free carries. So that [14]

ε 1 = n 2 − k 2 (10)

ε 2 = 2 n k (11)

Photoluminese spectra have an important role because they give information about the optical properties, likes Eg, excitons, traps and levels of energy. The E_g which calculated from photoluminese spectra (pL) is more precision from Tauc equation. Figure 8 represents (pL) spectra for Nickel phthalocyanine film at various T_s, Table 4 gives energy gap obtained by PL spectra and by Tauc method at different substrate temperatures with excitation wavelength 315 nm. The lowest value for E_g is at T_s 400 K, it is the same result found by Tauc equation. All E_g values found by PL spectra are greater than that found by Tauc equation method for all studied range of substrate temperatures. Traps in energy gap take part in an important role in organic material conductivity, to study the behavior of traps inside energy gap, two photoluminescence spectra were recorded for NiPc thin films at 110 nm thickness, one using excitation wavelengths 315 nm (where photons energy greater than E_g), and the other about half of energy gap (600 nm). Photoluminescence spectra for two excitation wavelengths are shown in Figure 9. It shows the ordinary behavior when NiPc excited by a photon with energy 3.93 eV (excitation wavelength 315 nm) which gives emitting photon with 3.29 eV (wavelength 376 nm). The small peak gives emitting photons with 3 eV which is the Eg approximately. An extra ordinary behavior also happened when NiPc thin film excited by a photon with energy 2.06 eV (wavelength 600 nm) and gives emitting photon with energy 3.6 eV (wavelength 344 nm). The abnormal behavior may refer to nonlinear properties. Photoluminescence spectra for NiPc thin films at thicknesses (110) nm were done using exciting wavelength 600 nm as shown in Figure 10. We can see both of two thin films give emitting photon energy about 3.6 eV (wavelength 344 nm). As a result the traps which represented by Q band has great importance in conductivity of NiPc film [15] [16] .

The D.C. conductivity for NiPc thin films was calculated as listed in Table 5, the room temperature conductivity increase as film Ts increases for the (325 - 450) K about five times and this is attributed to better crystallinity (grain size). By plotting Lnσ versus of 10³/T as shown in Figure 11, activation energy (E_a) can be determined. The electronic transport mechanism is influenced by the intergrain boundaries. As it is observed from Figure 11, there are three activation energies within the range (298 - 473) K as in Figure 11 and Table 5 and this conformed by [17] [18] .

As shown in Figure 12, the activation energy (E_a) values vary with T_s due to variations crystalline structure of the prepared film [17] .

Carrier concentration (n) can be calculated which decreases from (10 - 0.302) cm⁻³ for Ts (325 - 450) K except at 300 K, and P-types films have been observed by Hall effects, whereas the carriers mobility (µ) up from 0.03 (cm²/v.s.) to 99.42 (cm²/v.s.) by increasing T_s from (325 - 450) K for prepared films except at 300 K, and this is given in Table 6. From the Table the carrier mobility increases with substrate temperature except at 300 K while the carrier concentration decreases with increases of substrate temperature [17] [18] .

p-NiPc/n-Si solar cells have been fabricated thermally by deposited the organic material NiPc on n-type silicon wafer, at substrate temperatures of (300, 400) K with 265 nm thickness. The characteristic of Capacitance (C)-Voltage (V) have been described at RT for P-NiPc/n-Si HJ at substrate temperatures of (300, 400) K. It is observed from Figure 13. By increasing of bias voltage the values of C are decreases, due to the higher values of depletion width (W) leading to increase of built-in voltage (V_bi). By plotting C⁻² with reverse voltage bias (Figure 14) the intersection C⁻² = 0 represent V_bi. It is observed from this figure increase in built-in potential with high temperatures, Reason for this is improvement in structural defects and the progress films during deposition (i.e. grain boundaries, stacking faults), as shown in Table 7.

Figure 15 represents the current-voltage characterization for NiPc-Silicon HJ for both biases in the dark at substrate temperatures of (300, 400) K. These curves showed the conduct of the current at two bias of voltage. From Figure 15, two regions have been observed at forward current. From (0 - 0.2 V) for recombination current, and from 0.2 V to 0.4 V represents the tunneling current. Also the current at reverse bias voltage contains two regions for generation and diffusion process.

Figure 16 gives the semi logarithmic plot of the current-voltage Curve, the initial part voltage range (0 - 0.2) Volt could be approximated by an expression of the type I~exp(qV/βk_BT). So the ideality factor β has been calculated and it is about 0.613 - 0.734 which indicate on the mechanism of conduction is generation and diffusion.

The series resistance (R_s) and shunt resistance (R_sh) of the junction can be evaluated by plotting resistance of junction (R_j) versus applied voltage as in Figure 17 and Table 8 gives these parameters of two NiPc/Si HJ samples.

The main factor for working of solar cell is photocurrent (Iph). The photocurrent for NiPc/Si HJ at substrate temperatures of (300, 400) K were plotted against reveres and forward bias as shown in Figure 18, V_oc, I _sc were determined by the intersect of photocurrent curve with x and y axis. Also maximum voltage (V_m) and current (I_m) for solar cell were found, full factor (F.F) and efficiency (η) have been calculated. For HJ under illumination, the photocurrent increases with increasing of voltage which leads to separate electrons and holes and then increases the photocurrent to higher values. The light current depends on the processes of generation and diffusion. The results comparison tabulated in Table 9 leads to that the selected thickness and substrate temperatures are a good choice, where the results of photocurrent parameters increase with increasing substrata temperatures.

Thermally evaporated Ni-Pc film with various substrate temperatures was prepared excellently. It was found that all E_g values found by PL spectra are greater than those found by Tauc equation method for all studied range of substrate temperatures. Fluorescence spectra confirmed the splitting of soret band. The energy gap values are increased by raising the base temperature. There are three activation energies increasing with the increase of substrate temperatures. P-types films have been observed by Hall effects. Carrier concentration and mobility have been reduced by increasing of substrate temperatures. Results of photocurrent parameters increase with increasing substrate temperatures. The maximum efficiency was obtained around 5% at thickness of 265 nm and 400 K. The results indicate that the selected thickness and substrate temperatures are a good choice for solar cell applications.

The authors declare no conflicts of interest regarding the publication of this paper.

Nasir, E.M., Hussein, M.T. and Al-Aarajiy, A.H. (2019) Investigation of Nickel Phthalocyanine Thin Films for Solar Cell Applications. Advances in Materials Physics and Chemistry, 9, 158-173. https://doi.org/10.4236/ampc.2019.98013