At first, 15 mL of the aqueous solutions of titanium tetraisopropoxide (Ti[OCH(CH₃)₂]₄ 98+% purity, Fisher Scientific, USA) was slowly added to 30 mL of acetic acid (HCOOH 99.9% purity, Fisher Scientific, USA) in a three-neck flask, and the mixture was stirred for 5 minutes to avoid agglomeration. The mixture of deionized water (4 mL) and isopropanol (CH₃CH(OH)CH₃ 99.9%, solution BDH Ltd Poole, England) (15 mL) was added dropwise to the solution, and then stirred vigorously for another 10 minutes. After complete mixing of the solution, 4 mL of nitric acid (HNO₃) as added to the solution as stabilizer and the mixture further subjected to vigorous stirring for 20 minutes. TiO₂ colloid in the nanometer range was formed from the hydrolysis and condensation reactions of titanium alkoxide precursors. In the presence of water, titanium alkoxide hydrolyzed and subsequently polymerized to form a 3-dimensional TiO₂ network which was dispersed on the thoroughly cleaned borosilicate glass substrates, and spin at 4000 rpm for 30 seconds at room temperature. After the spin-coating step, the films were subjected to post thermal treatment at 300˚C, 400˚C and 500˚C in air for 1 hour, and then cooled at room temperature naturally.

TTIP + isoPrOH + AcOH → Ti ( OR ) 4 + 4H 2 O → 2Ti ( OH ) 4 + 4ROH ( hydrolysis ) (10)

2Ti ( OH ) 4 → TiO 2 + TiO 2 ⋅ 2H 2 O + 2H 2 O ( condensation ) (11)

After the preparation of the samples, different characterization techniques were used to investigate their structural and optical properties. The optical transmittance, T, and reflectance, R, of the films were measured by a UV-Vis (Lambda 950) spectrophotometer, equipped with an integrating sphere, in the wavelength range 400 - 800 nm. Porosity, optical conductivity, refractive index and extinction coefficient were calculated from the data obtained. The surface microstructure of the films was viewed using AP200 MTI optical microscope at magnification 1000 × Jeol (Tokyo, Japan) JSM 5600 LV (low vacuum) scanning electron microscope (SEM) was used to get the surface morphology of the samples.

UV-vis transmittance spectra of TiO₂ nanostructure films for annealing temperatures at 300˚C, 400˚C and 500˚C in the wavelength range 300 - 800 nm are shown in Figure 1. As can be seen, all the spectrums exhibit interference fringes, which are due to the multiple reflections at the two film edges, i.e. at the film/air and the film/substrate interfaces. This indicates that the film surface is relatively

smooth, uniform and exhibits a good transparency in the visible region [5] [6] . The excellent surface quality and good homogeneity of the film were confirmed from the appearance of interference fringes in the transmission spectra. The amplitude of interference spectra and the transmission percent of the TiO₂ films increase with the increase in annealing temperature. This can be due to the formation stage of anatase and with the increase in the grain size [2] . The results obtained are synonymous to the previous studies by Le et al. [9] .

Figure 2 shows the absorption coefficient-photon energy plot for the annealed TiO₂ nanostructure films at 300˚C, 400˚C and 500˚C temperatures range. As seen from Figure 2, the optical band gap was determined by extrapolating the straight-line part of the plot to the photon energy axis. From the result, it reveals that there is a gradual increase in the absorption coefficient with increasing photon energy for different annealing temperature [1] [10] . The bandgap energy of the synthesized TiO₂ nanostructure thin film decreases with the increase in annealing temperature which was found to be 3.7 eV, 3.6 eV and 3.4 eV for 300˚C, 400˚C and 500˚C, respectively as shown in Table 1. This decrease was correlated with grains size decreases with temperature, and this can be linked with the formation of anatase stage [11] . These results obtained are in agreement with the previous studies by Ximello-Quiebras et al. [12] , and also near the value of 3.85 eV, found by Oh et al. [13] for TiO_x with a thickness of 38 nm. The decrease of the band gap cannot be due to the change of the crystallite size, since the latter decreases with the film thickness, but rather to oxygen defect band states formed in the band gap. The values of the optical band gap energy are in good agreement with those published by other authors [1] [10] . However, they are still higher than the optimum range for solar energy conversion.

Figure 3 shows the reflectance-wavelength plot of TiO₂ nanostructure annealed at 300˚C, 400˚C and 500˚C in the wavelength range 300 - 800 nm. The reflectance is considerably high in the wavelength range of 410 - 500 nm, and a gradual fall in the reflectance in the wavelength range of 510 - 600 nm was observed. In TiO₂ nanostructure annealed at 500˚C, the band gap absorption onset

shifted 420 nm from 500 nm for the TiO₂ annealed at 300˚C, extending the absorption up to 420 nm, as shown in Figure 3. The optical absorption of TiO₂ annealed at 500˚C in the visible light region was primarily located between 400 and 500 nm. TiO₂ annealed at 500˚C had increased optical response compared to the case of TiO₂ nanostructure film annealed at 300˚C in the visible region.

The reflectance percentage of the titanium dioxide thin film decreases with the increase in annealing temperature. This can be linked with the formation of anatase stage and with the decrease in the grain size [11] .

Figure 4 shows the porosity-wavelength plot of synthesized TiO₂ nanostructure films after annealed at 300˚C, 400˚C, and 500˚C for an hour. The result shows that the porosity of the synthesized TiO₂ nanostructure film gradually decreases with increasing wavelength, and increases with increasing temperature, which agrees with the result in other literature. The density of the TiO₂ nanostructure film increases as the porosity decreases. Higher porosity was observed at 500˚C.

Figure 5 shows conductivity against photon energy plot of TiO₂ thin film for different annealing temperatures. The optical conductivity of the titanium dioxide nanostructure films increases as the temperature increases from 300˚C to 500˚C, and the optical responsiveness of the transparent nanostructure films were steady at a very low energy. This can be linked with the formation of anatase stage and with the decrease in the grain size [11] .

The refractive index of synthesized TiO₂ nanostructure thin films was calculated from measured UV-visible transmittance spectrum. The evaluation method used in this work is based on the analysis of UV-visible transmittance spectrum of a weakly absorbing film deposited on a non-absorbing substrate. From the result, it shows that there is a increase in the refractive index in the wavelength range 400 nm to 510 nm, and considerable attenuation is observed in the range 500 nm to 600 nm. It is noted that the refractive index and the density of nanostructure thin films of titanium oxide increases with increasing annealing temperature; due to phase transition (anatase, anatase-brookite), which increases grain sizes and/or the density of layers. The refractive index of the synthesized TiO₂ nanostructure shows better curve as the temperature increases from 300˚C to 500˚C as shown in Figure 6. This can be linked with the formation of anatase stage and with the decrease in the grain size [11] .

The extinction coefficient of titanium dioxide thin films is shown in Figure 7. The extinction coefficient is high at the photon energy 4.0 eV and low at the photon energy range of 3.4 - 4.0 eV. The steady fall in the extinction coefficient may be due to the absorption of light at the grain boundary. The curve of synthesized TiO₂ nanostructure is steady at a lower extinction coefficient which agrees with the extinction coefficient of TiO₂ in other literature [1] [14] . The extinction coefficient of the titanium dioxide nanostructure films increases with the decrease in annealing temperature. This can be linked with the formation of anatase stage and with the decrease in the grain size [1] [15] .

Figure 8 shows optical microscope morphology of TiO₂ nanostructures at magnification 1000×, after post thermal treatment for one hour in an oven at 300˚C, 400˚C and 500˚C, and the cooled naturally in the air. It was observed that the surface morphology of the nanostructure films show good uniformity, high homogeneity, smooth and cracks free, indicating good adhesion and regularity

among the layers of the prepared films.

The particles are approximately in spherical form. The bigger crystalline size was observed at 300˚C. By increasing the annealing temperature from 300˚C up to 500˚C, it was found that the size becomes smaller and the agglomeration becomes increasingly attenuated. The effects of annealed treatment on the microstructure of the TiO₂ nanostructures were studied in a scanning electron microscope (SEM), and the obtained SEM micrographs are shown in Figure 9. Highly dense and well-aligned TiO₂ interpore structures constructed by near uniform grains of elliptical shapes were formed. It was observed that the grain size decreased with the increase in the annealing temperature. Smaller grain sizes were observed in the nanostructures at elevated temperature as shown in Table 1.

Grain boundaries are clearly seen in the SEM micrographs. Similar nanostructure surface has been observed by Le et al. [9] . At 300˚C, the grain size was around 6 nm; at 400˚C, the grain size decreased to 5 nm. Smaller grain sizes were observed at elevated temperature.

At 500˚C, the grain size had already increased to around 4 nm. The pore density decreased in this temperature range of 300˚C - 500˚C, which meant better densification could be achieved. This result is consistent with what was obtained in the densification study in the literature [1] [10] [15] .