This study demonstrated that the changes in functional properties of both woven and knit cotton fabrics were determined to evaluate the performance of different special finishes. Here, 100% cotton fabrics were treated with different types of finishing chemicals at different formulations. To assess the performance of different finishes on fabric properties, GSM, bursting strength, tensile strength, dimensional stability, absorbency, crease recovery angle with ASTM and AATCC methods were done. The results showed that the functional properties of the finished cotton fabrics both woven and knit depend to a great extent on the type of finish.
Cotton is a versatile fibre with outstanding quality regards comfort ability. Softness, water repellency, wrinkle free, silky soft, antistatic property are some of the most common functional properties that are needed for protective clothing without affecting the comfort of the cotton fabric. Generally different special types of finishes are applied on cotton fabric to impart various functional properties. Here ninth types of special finishes are applied on both cotton woven and knit fabrics.
The first finish is antistatic finish with siligen softener SIH (
The second finish is polyurethane finish with perapret additive PU New (
The third and forth finishes are soft finishes named as silicon (Micro) and silicon (Macro) both of which are generally polysiloxane derivatives of low molecular weight (
Both silicon (Micro) and silicon (Macro) finishes are done by using siligen softener SIE (
The fifth finish is polyethylene finish with perapret additive PEP (
The sixth finish is water repellent finish which is the ability of a textile material to resist wetting [
All water repellent chemicals are usually available as water emulsions and are used to fabric by the pad-dry-cure method with a curing temperature around 150-1700C for a couple of minutes [
Cotton is intermolecularly linked by many hydroxyl groups in two different regions: one is crystalline region and another is amorphous region. Cellulose chains are closed packed in crystalline region which limits their mobility and accessibility of molecules, whereas they are temporarily held with weak hydrogen bonds in the amorphous region. When a force is applied onto the fibre during wear and laundering process, hydrogen bonds are easily broken and slippage
occurred between the cellulose chains. When slippage occurs, new hydrogen bonds formed at different location and tend to maintain the fibre in wrinkled or bent state. For this reason, wrinkles are occurred in fabric appearance. Moreover, as cotton fibre is hydrophilic, the absorption of water breaks the hydrogen bonds and allow the fibre to shrink by preventing the chains from returning to their original positions, even after the applied forces or water are removed. Due to this reason, cotton fibre is easily wrinkled and shrinked after laundering which is one of the main drawback of cotton fibre that make them inconvenience for users [
To overcome wrinkles, cotton fabrics are treated with chemicals by applying a special type of finish named wrinkle resistant finish by crosslinking of hydroxyl groups of cellulose. Various types of resins have been developed to improve wrinkle or crease resistant of cotton fabrics. Dimethylol dihydroxy ethylene urea (DMDHEU) resin was mainly used among different types of resins as it is commercially widely accepted in industry due to its superior crease recovery property and low cost [
The seventh finish is wrinkle free finish by using fixapret ECO (
The eighth finish is paper touch finish which is done by using perapret VA finishing agent. It is a nonionic dispersion of polyvinyl acetate. It is generally used for filling and stiffening effects on cotton fabrics and their blends with synthetic fibres. High add on of this agent allow a very stiff handle.
The ninth finish is silky soft finish which is done by perapret F-PEB finishing agent which is a secondary polyethylene dispersion.
In the literature, a considerable number of studies on different finishing chemicals, their application procedure, methods for upgrading the durability
and their wash fastness and curing temperature have been reported [
100% cotton one woven and one knit fabrics (scoured and bleached) are used for this experiment to apply different types of finishes by pad-dry-cure method. The woven fabric is collected from local shops and knit fabric is supplied by Essential Clothing Ltd., Gazipur, Bangladesh. Woven fabric has plain weave structure with 110 GSM and knit fabric is single jersey with 160 GSM. Siligen softener SIH (nonionic antistatic finishing agent based modified polysiloxane, BASF), Kieralon wash JET-B Conc (nonionic surfactant with wetting and emulsifying property, BASF), Perapret additive PU New (nonionic polyurethane based finishing agent, BASF), Siligen Softener SIS (one softener is silicon micro emulsion and another softener is silicon nano emulsion, nonionic, BASF), Perapret Additive PEP (nonionic polyethylene wax based finishing agent, BASF), Nuva TTC (fluorocarbon based water repellent finishing agent, weakly cationic, dispersion of fluorine compound, Clariant), Fixapret F-ECO (modified dimethylol dihydroxy ethylene urea, cationic, BASF), Fixapret Catalyst F-M (a synergistic mixture of metal salts used for as a catalyst to initiate crosslinking reaction with cross linker, BASF), Perapret F-PEB (a secondary polyethylene dispersion, BASF), Siligen Softener SIO (softener, BASF), Perapret Stiffener VA New (weakly cationic poly vinylacetate-based polymer dispersion, BASF), Siligen Softener SIE (nonionic, amino functional polysiloxane, BASF) are of commercial grade.
Supplied fabrics are then processed with different types of finishing chemicals to investigate the effect of finishes on other physical properties of the fabrics.
Supplied fabrics are then processed with different types of finishing chemicals to investigate the effPortions of woven and knit fabrics (scoured and bleached) are padded using Siligen softener SIH (30 g//L) and Kieralon wash JET-B Conc. (2 g/L) to a wet pick up of 80% followed by drying 120˚C for 2 min.
Portions of woven and knit fabrics (scoured and bleached) are padded using Perapret additive PU New (30 g/L) along with Kieralon wash JET-B Conc. (2 g/L) to a wet pick up of 80% followed by drying 120˚C for 2 min and curing at 150˚C for 5 min.
Siligen Softener SIS (one is in micro level (particle size 80 nm) and another is in macro level (particle size 120 nm)) is used on cotton fabric in this experiment. Fabrics are finished with Siligen Softener SIS (30 g/L) and Kieralon JET-B Conc. (2 g/L) by padding at 80% pick up and followed by drying at 120˚C for 2 min.
Fabrics are treated with Perapret Additive PEP (30 g/L) and Kieralon JET-B Conc. (2 g/L) by using pad (80% pick up) and dry (120˚C for 2 min) process on both cotton woven and knit fabrics in this experiment.
Fabrics are treated with Nuva TTC (30 g/L) and Acetic acid (2 ml/L) by using pad (80% pick up), dry (120˚C for 2 min) and cure process (150˚C for 5 min) on both cotton woven and knit fabrics in this experiment.
Fixapret F-ECO (20 g/L), Fixapret Catalyst F-M (6 g/L), Perapret F-PEB (3 g/L) and Siligen Softener SIO ((3 g/L) are used on cotton fabric in this experiment. Fabrics are finished with above chemicals by padding at 80% pick up, followed by drying at 120˚C for 2 min and curing at 150˚C for 5 min.
Perapret Stiffener VA New (20 g/L), Siligen Softener SIE (10 g/L) and Kieralon wash JET-B Conc. (2 g/L) are used on cotton fabrics in this experiment. Fabrics are finished with above chemicals by padding at 80% pick up, followed by drying at 120˚C for 2 min and curing at 150˚C for 5 min.
Portions of fabrics are treated by Perapret F-PEB (20 g/L), Siligen Softener SIE (10 g/L) and Kieralon wash JET-B Conc. (2 g/L) in this experiment. Fabrics are finished with above chemicals by padding at 80% pick up, followed by drying at 120˚C for 2 min and curing at 150˚C for 5 min.
Both woven and knit fabrics are treated with a general bath condition. The process parameters are adopted as recommended by the supplier. Pad-Mangle machine is used for padding with 2.5 m/min fabric speed and 2.8 kg/cm2 padding pressure. Fine oven machine is used for drying. SDL Mini-Dryer Steamer is used for curing.
Each sample is tested in the standard atmosphere, 25 ± 2˚C temperature and 65% RH after conditioning 24 hrs.
It is done by GSM cutter from James H. Heal & Co. Ltd. Halifax, England according to ASTM (D 3776-79) method.
It is determined according to AATCC (79-1992) method.
It is done for woven fabric according to ASTM (D 5045) method by Good brand fabric strength tester.
It is done by Trust burst tester according to ASTM (D 3786-87) method.
It is done according to AATCC 96-1997 method.
It is done by Shirley crease recovery tester according to AATCC 66-2003 method and is taken the average values of warp and weft results.
Spray rating tests are done by Spray Rating Tester by James H. Heal & Co. Ltd. Halifax, England. AATCC 22-2001 test method is used to evaluate the water repellency of the fabric. Where 100 grade of surface resistance rating expresses that there will be no sticking or wetting of the upper fabric surface, 90 grade rating expresses that there will be only slight random wetting on the upper fabric surface, 80 grade means there will be wetting at the spray points on the upper surface of fabric while a fabric with complete wetting was assigned a 0 rating.
Since the main task of the present study is to observe the effect of different finishing on cotton both woven and knit fabrics, a wide range of finishing formulations have been used and evaluated on the basis of the performance of treated cotton fabric. Nine different finishes are chosen in this work and are applied on plain weave woven and single jersey knit fabrics. Anti-Static finish is expressed as A static, Polyurethane finish is expressed as PU, Silicon (Micro) finish is expressed as Sil (Mic), Silicon (Macro) finish is expressed as Sil (Mac), Polyethylene finish is expressed as PE, Water repellent is expressed as W R, Wrinkle Free is expressed as W F, Paper touch is expressed P touch, Silky soft finish is expressed as Silky throughout the results. All finishes are done by using 32 g/L solutions to avoid the effects of add on variation. Results obtained along with their appropriate discussions are as follows.
Tensile strength plays a vital role after different finishes. It was done according to ASTM (D 5045) method to evaluate the treated woven fabric’s tensile strength. In the chart (
| Name of the Finish | Tensile Strength in lbs/in2 (woven) | |||
|---|---|---|---|---|
| Warp | Weft | |||
| Before Finish | After Finish | Before Finish | After Finish | |
| Anti-Static | 30 | 34 | 25 | 27 |
| Polyurethane | 30 | 28 | 25 | 24 |
| Silicon (Micro) | 30 | 32 | 25 | 26 |
| Silicon (Macro) | 30 | 34 | 25 | 27 |
| Polyethylene | 30 | 28 | 25 | 26 |
| Water Repellent | 30 | 27 | 25 | 23 |
| Wrinkle Free | 30 | 22 | 25 | 20 |
| Paper Touch | 29 | 28 | 24 | 22 |
| Silky Soft | 31 | 34 | 26 | 27 |
warp and weft except soft finishes. Soft finishes make fabric flexible and for this reason tensile strength is increased. In wrinkle free finish, tensile strength decreases and it is obviously taken into account as resin crosslinks in amorphous region of cellulose leading lower flexibility and harsh handfeel, though it is reasonable for the fabric to go for the next proceedings.
In all water repellent finishes, tensile strength reduces as resin crosslinks in acetic condition within the amorphous region of cellulose leading lower flexibility and harsh handfeel. For soft, silky soft and antistatic finishes, tensile strength increases due to a direct consequence of deposition and formation of a waxy thin film onto or within the fibre. Paper touch finish make fabric stiff and probably because of that reason tensile strength decrease.
But in the chart (
The bursting strength of knit fabric is done according to ASTM (D 3786-87) method and found bursting strength is reduced for water repellent and wrinkle free finishes, because of effect of the cellulosic fiber during cross linking process. When the water repellent and wrinkle free ‘chemicals form cross link with the cotton free O-H group in the amorphous region, it makes stiff of the fabric and moreover, cross linking reaction is done mainly in acidic condition which are also responsible for the loss of the fabric’s bursting strength. Paper touch finish make fabric stiff and for that consequence, reduce bursting strength. For soft (Sil (Mac), Sil (Mic)), silky soft and antistatic finishes, tensile strength increases due to a direct consequence of deposition and formation of a waxy thin film onto or within the fibre.
The GSM tests are done according to ASTM D 3776-79 method for all finished fabrics. The variation of GSM of woven fabric after finishing has given in below
Three types of soft finish are used in this work. One is silky soft finish and other two are silicon soft finish in micro and macro level. The variation of untreated and treated fabric’s GSM after soft finishing, are depends on the chemicals add on, formation of interfibre and interyarn bonds and the effects of the softeners deposits in and/or onto the structure on the fabric. The variation of GSM of knit fabric after finishing has given in below
| Name of the Finish | Bursting Strength (kpa) | |
|---|---|---|
| Before Finish | After Finish | |
| Anti-Static | 310 | 316 |
| Polyurethane | 310 | 298 |
| Silicon (Micro) | 310 | 324 |
| Silicon (Macro) | 310 | 327 |
| Polyethylene | 310 | 296 |
| Water Repellent | 310 | 291 |
| Wrinkle Free | 310 | 283 |
| Paper Touch | 310 | 302 |
| Silky Soft | 310 | 324 |
| Name of the Finish | GSM (Woven) | |
|---|---|---|
| Before Finish | After Finish | |
| Anti-Static | 110 | 116 |
| Polyurethane | 110 | 118 |
| Silicon (Micro) | 110 | 114 |
| Silicon (Macro) | 110 | 117 |
| Polyethylene | 110 | 116 |
| Water Repellent | 110 | 121 |
| Wrinkle Free | 110 | 123 |
| Paper Touch | 110 | 118 |
| Silky Soft | 110 | 114 |
| Name of the Finish | GSM (S/J) | ||
|---|---|---|---|
| Before Finish | After Finish | ||
| Anti-Static | 160 | 165 | |
| Polyurethane | 160 | 167 | |
| Silicon (Micro) | 160 | 164 | |
| Silicon (Macro) | 160 | 167 | |
| Polyethylene | 160 | 168 | |
| Water Repellent | 160 | 171 | |
| Wrinkle Free | 160 | 173 | |
| Paper Touch | 160 | 164 | |
| Silky Soft | 160 | 166 | |
The dimensional stability or shrinkage tests are done according to AATCC 96-1997 method for all finished fabrics. The variation of shrinkage% after all finishing process have given in below
After soft finishing dimensional stability are rises due to the mechanical reinforcement by formation of bonds within interfibre and interyarn. Soft finishes reduce the surface roughness by reducing interfibre and interyarn friction. For water repellent finishing, the change in the physico-mechanical and comfort properties of the treated cotton is an improvement of dimensional stability. The improvement of dimensional stability of both knit and woven fabrics are because of the formation of a repellent film on the fibre surface along with a hydrophobic layer around the fibres. After paper touch finish, fabric’s stiffness is improved which reduces shrinkage percentage. Moreover, after wrinkle free finish, dimensional stability for both woven and knit fabric is improved due to the crosslinking reaction of the resin.
| Name of the Finish | Shrinkage% (woven) | |||
|---|---|---|---|---|
| Warp | Weft | |||
| Before Finish | After Finish | Before Finish | After Finish | |
| Anti-Static | 3 | 2.5 | 2.5 | 2 |
| Polyurethane | 3 | 2 | 2.5 | 2 |
| Silicon (Micro) | 3 | 2.5 | 2.5 | 2 |
| Silicon (Macro) | 3 | 2.5 | 2.5 | 2 |
| Polyethylene | 3 | 2 | 2.5 | 1.5 |
| Water Repellent | 3 | 2 | 2.5 | 1.5 |
| Wrinkle Free | 3 | 2 | 2.5 | 1.5 |
| Paper Touch | 3 | 2.5 | 2.5 | 2 |
| Silky Soft | 3 | 2.5 | 2.5 | 2 |
| Name of the Finish | Shrinkage% (knit) | |||
|---|---|---|---|---|
| Wales | Coarse | |||
| Before Finish | After Finish | Before Finish | After Finish | |
| Anti-Static | 5 | 4 | 4.5 | 4 |
| Polyurethane | 5 | 4 | 4.5 | 3 |
| Silicon (Micro) | 5 | 3.5 | 4.5 | 3.5 |
| Silicon (Macro) | 5 | 3.5 | 4.5 | 3.5 |
| Polyethylene | 5 | 3 | 4.5 | 3 |
| Water Repellent | 5 | 3.5 | 4.5 | 3 |
| Wrinkle Free | 5 | 3 | 4.5 | 3 |
| Paper Touch | 5 | 3.5 | 4.5 | 3.5 |
| Silky Soft | 5 | 3.5 | 4.5 | 3.5 |
Shrinkage percentage decreases after applying the finishes, which means the quality of fabric have improved.
In a pipette a solution of 1% direct red (Congo red) is taken and droplet of solution put on the different places of the fabric. The time of the absorption of that water droplet on the fabric is observed. From below
The water absorbing time of original cotton was instant because of its hydrophilic property. The cellulose hydroxyl groups of cottons of cotton fabric make the water droplets spread instantly when it is placed in the surface of the fabric. After different finishing process the absorbing time is increased and it is reasonable as after soft finishing with both Sil (Mac) and Sil (Mic) softener and silky soft finishes, a waxy thin layer of silicon was made onto the fabric which prolong
| Name of the Finish | Time in Second | |
|---|---|---|
| Before Finish | After Finish | |
| Anti-Static | 15 | 20 |
| Polyurethane | 15 | 77 |
| Silicon (Micro) | 15 | 18 |
| Silicon (Macro) | 15 | 17 |
| Polyethylene | 15 | 75 |
| Water Repellent | 15 | - |
| Wrinkle Free | 15 | 13 |
| Paper Touch | 15 | 19 |
| Silky Soft | 15 | 80 |
| Name of the Finish | Time in Second | |
|---|---|---|
| Before Finish | After Finish | |
| Anti-Static | 12 | 17 |
| Polyurethane | 12 | 63 |
| Silicon (Micro) | 12 | 17 |
| Silicon (Macro) | 12 | 15 |
| Polyethylene | 12 | 75 |
| Water Repellent | 12 | - |
| Wrinkle Free | 12 | 10 |
| Paper Touch | 12 | 18 |
| Silky Soft | 12 | 60 |
absorbing time. Whereas after antistatic finish, water absorbing time is not increased significantly as siligen Softener SIH has hydrophilic nature. After wrinkle free finish, absorbing time is reduced as it make fabric stiff so more friction is occurred between water droplet and fabric. It is obvious that after water repellent finishes, absorbing time will increases because of the hydrophobic nature of fluorocarbon. After PE finishing, it imparts a fuller, smoother handle to both woven and knit fabrics as it acts as a polyethylene dispersion. After PU finish, polyurethane dispersion make a film forming result in a fuller handle thus reduce absorbing time.
It is done according to AATCC 66-2003 method and is taken the average values of warp and weft results.
| Name of the Finish | Crease Recovery in Degrees | |
|---|---|---|
| Before Finish | After Finish | |
| Anti-Static | 55 | 63 |
| Polyurethane | 55 | 69 |
| Silicon (Micro) | 55 | 70 |
| Silicon (Macro) | 55 | 71 |
| Polyethylene | 55 | 72 |
| Water Repellent | 55 | 67 |
| Wrinkle Free | 55 | 93 |
| Paper Touch | 55 | 75 |
| Silky Soft | 55 | 68 |
| Name of the Finish | Crease Recovery Angle (S/J) | |
|---|---|---|
| Before Finish | After Finish | |
| Anti-Static | 60 | 69 |
| Polyurethane | 60 | 72 |
| Silicon (Micro) | 60 | 70 |
| Silicon (Macro) | 60 | 75 |
| Polyethylene | 60 | 78 |
| Water Repellent | 60 | 77 |
| Wrinkle Free | 60 | 97 |
| Paper Touch | 60 | 75 |
| Silky Soft | 60 | 70 |
| Spray rating (before wash) | |||
|---|---|---|---|
| Concentration (g/L) | Water repellent chemicals | Fabric | Rating |
| 30 g/L | Fluorocarbon | Unfinished woven | 0 |
| Finished woven | 90 | ||
| Unfinished knit (S/J) | 0 | ||
| Finished knit (S/J) | 90 | ||
Water repellent finish (W R) is done by fluorocarbon based water repellent chemical in 30 g/L concentration and is applied on woven and S/J knit dyed fabrics. There treated fabrics were evaluated by using AATCC 22-2001 method. Water repellency of both woven and knit (S/J) fabrics treated with fluorocarbon resin is shown in
The effects of special finishes were observed on both woven and knit 100% cotton fabrics. To do so, 54 treated fabrics samples were tested and obtained results were evaluated. Different physical test results showed that different special finishes significantly are influenced on both woven and knit fabrics. This study mainly focused on the impact of chemical finishes, i.e., soft finish, silky soft finish, anti-static finish, water repellent finish, wrinkle free finish, paper touch finish, polyethylene finish and polyurethane, on the functional properties of cotton woven and knit fabrics. There was no remarkable deviation which is observed in GSM on the basis of different finishes. The obtained results show that the dimensional stability GSM is improved via chemical finishing; the wettability is decreased more via water repellent finish. Different chemical finishes did not cause significant change to bursting strength of knit fabrics and tensile strength for woven fabrics except soft finishes, which is another important conclusion of this work.
I would also like to express my deep gratitude to MICRO FIBRE for providing the lab facilities during the work. I would also like to thank Essential Clothing Ltd for providing knit fabrics. Again special gratitude also goes to the Wet Processing Lab & the TTQC Lab of Bangladesh University of Textiles (Butex) for most of the physical tests.
Chowdhury, K.P. (2018) Effect of Special Finishes on the Functional Properties of Cotton Fabrics. Journal of Textile Science and Technology, 4, 49-66. https://doi.org/10.4236/jtst.2018.42003