As the inorganic binder, liquid glass is perspective material in the production of ceramics, composites and coverings silicate [1]. Simultaneously, during the long-term storage, polymerization reactions may occur spontaneously in the liquid glass, which lead to the “aging” and reducing strength and heat resistance of products and limiting the periods of storage and operating. These problems can be solved by substituting the traditional liquid glass with the modified liquid glass. Materials obtained on the basis of the modified liquid glass have high strength, durability, heat resistance, water resistance and other performance characteristics [2].

In the previous studies modified liquid glasses were obtained mostly by traditional method of modification with sodium, potassium or lithium liquid glass and their mixtures with the silicate modulus in the range 2 - 5. The process for obtaining the modified liquid glass carried out by physical and chemical methods of modification using organic and inorganic modifiers. Chemical modification has proven to be an effective way [3].

To reduce manufacturing costs for the production of the modified liquid glass, we offer a way to simultaneously produce sodium modified liquid glass from low-quality aluminum-containing raw material-kaolinite clay at their complex processing. Complex processing of kaolinite clays allows obtaining an enriched concentrate of kaolin and aluminum oxide for the production of alumina. Excess silica of kaolinite clays can be used as raw materials for the production of silicate products, including liquid and liquid-modified glass. The liquid glass obtained from excess quartz fraction can be used to modification processes, by leaching with sodium hydroxide under optimal conditions [4]-[6].

Chemical composition of kaolinite clay was found to be 69.6% SiO₂; 19.3% Al₂O₃; 0.97% Fe₂O₃; 0.15% Na₂O; 0.01% S₂O₃; 0.6% K₂O; 6.3% LOI and silicic module-0.28 for obtaining the solution of sodium liquid glass [7].

The excess quartz fraction of kaolinite clay was separated by elutriation. There have been received 46% quartz fraction and 54% of clay fraction after the process of washing. The clay fraction will be directed for obtaining of purified kaolin and aluminum oxide concentrate. The quartz fraction was used to produce a liquid glass by leaching with sodium hydroxide solution at the optimal conditions [8].

As a result there have been developed sodium liquid glass, complies with the Russian Interstate standard 13078-81 for sodium liquid glass, with chemical composition (g/dm³): SiO₂-350; Na₂O-155; Al₂O₃-2,1; Fe₂O₃-0,3, silicate module-2.33 and density- 1.49 g/cm³. The percentage of components (%): SiO₂-27.74; Na₂O-12.3; Al₂O₃-0.15; Fe₂O₃-0.02. Content of impurities oxides (%): Al₂O₃ + Fe₂O₃-0.17 (the content of impurities does not exceed 0.25% - 0.4%) [9].

The following modifiers are using to the processes of modification: starch (C₆H₁₀O₅) n, sodium hexametaphosphate (NaPO₃)₆, PEG-polyethylene glycol (C₂H₄O) nH₂O), dextrin (C₆H₁₀O₅)n, KBr (potassium bromide), KNO₃ (potassium nitrate), NaBr (Sodium bromide), NaNO₃ (sodium nitrate), Na₂B₄O₇∙10H₂O (borax) and sorbitol (C₆H₁₄O₆).

The obtained sodium silicate solution was used to produce modified liquid glass. In this case, modifiers in an amount of 6 grams (4% by weight of liquid glass solution) were introduced into the original liquid glass of 100 ml. Contacting and mixing of modifiers with liquid glass carried out at 80˚C for 30 minutes. The obtained modified liquid glass was placed under the room temperature for two days until complete homogenization.

It is known, that the materials derived from modified liquid glasses possess improved performance characteristics in comparison with material of obtained from traditional liquid glass. Strength is one of the main characteristics of the materials, which was obtained by using liquid glass.

The strength of hard materials obtained by using modified liquid glass, initial liquid glass and quartz from kaolinite clay was tested.

To study the strength of the materials obtained on the basis of the modified liquid glass and initial liquid glass, taken a similar amount (45 g) of the sand (quartz) fraction separated from kaolinite clay, which is mixed with 1.5 ml of the obtained various kinds of plasticizer (the initial and the modified liquid glass). Then, blanks in the form of tablets with diameter of 36 ± 0.1 mm and a height of 20 ± 0.1 mm was formed in a hydraulic press-Metallkraft WPP50M by pressing, which were dried in an oven at 105˚C for 5 hours in the beginning.

After cooling within 24 hours, the obtained samples were carried out calcinations at 200˚C for 3 hours; the samples were weighed before and after calcining.

Sample of kaolinite clay from Alekseev deposits of Kazakhstan were used for experiments on the obtaining of modified liquid glass. The phase composition of the sample of kaolinite clay from Alekseev deposits was identified according to X-ray diffrac- tion analysis: 67.5% quartz, 31.4% kaolinite-Al₂(Si₂O₅)(OH)₄ and 1.1% muscovite- KAl₂(AlSi₃)O₁₀(OH₁F)₂ (Figure 1).

Alekseev kaolinite clay deposit contains a significant amount of silicon oxide-quartz fraction, there was shown results of X-ray and chemical analysis. Quartz fraction consists of quartz phase (Figure 2), the clay fraction of the following composition: (%), Al₂O₃-31.2; SiO2-51.6; Fe₂O₃-0.53; Na₂O-0.095; K₂O-1.5; LOI 6.3. Silicic module-0.61.

As a result, the sodium liquid glass processed by kaolinite clay, with chemical composition (g/dm³): SiO₂-350; Na₂O-155; Al₂O₃-2.1; Fe₂O₃-0,3, silicate module-2.33 and density-1.49 g/cm³ (complies with the Russian Interstate standard 13078-81 for sodium liquid glass) has been used for production of the modified liquid glass.

Composition of clay fraction reflected by X-ray analysis: 63.2% kaolinite, 21.6 % quartz and 15.3 % muscovite) (Figure 3).

The clay fraction-enriched kaolinite clay as a commodity product can head to the processing of industry and a process for producing aluminum oxide concentrate. The quartz fraction was used for obtain liquid glass by leaching with sodium hydroxide under optimal conditions, then obtained liquid glass subjected modification process to investigate the effect of modifiers.

As a result, we obtained 10 kinds of modified liquid glass.

Materials derived from various liquid glasses, characterized by different physical- chemical properties. One of the main characteristics of the liquid glass is the strength.

There have been carried out the process of identification the strength of the samples obtained modified liquid glass and original liquid glass. The number and kind of modifiers for the samples are shown in Table 1.

Studied the strength materials derived from the quartz fractions by using modified liquid glass (number of 2 - 11) and initial liquid glass (number 1) (Table 1), produced 11 molded specimens (diameter-3.6 cm, height-2.0 cm), which in the beginning were dried in an oven at 105 ᵒC for 5 hours. After cooling the obtained samples were carried out calcinations; the samples were weighed before and after calcinations. There was a slight decrease in the weight of the samples-about 0.25% (Figure 4).

Results for the test on the strength of samples obtained by using modified liquid glass and initial liquid glass are given in Figure 5.

The data in Figure 5 shows that the obtained modified liquid glass from kaolinite clay can improve the strength of the quartz material for 1.6 - 3.12 times higher than the initial liquid glass.

As a result, the sodium liquid glass processed by kaolinite clay, with chemical composition (g/dm³): SiO₂-350; Na₂O-155; Al₂O₃-2.1; Fe₂O₃-0.3, silicate module-33 and density- 1.49 g/cm³ (complies with the Russian Interstate standard 13078-81 for sodium liquid glass) has been used for production of the modified liquid glass.

Have been synthesized 10 samples modified liquid glass from the sodium liquid glass by introducing different modifiers in an amount of 4% by weight of the solution.

It has been established that the obtained modified liquid glass from kaolinite clay can improve the strength of the quartz material for 1.6 - 3.12 times higher than the initial liquid glass. Using liquid glass modifier to the inorganic sodium nitrate (NaNO₃) increases the strength 3.12 times. Modifiers are also effective-sodium polyphosphate, sorbitol (increase the strength of 2.04 times) and sodium bromide (increase the strength 1.93 times).

Sarsenbay, G., Kov- zalenko, V.A., Sadykov, N.M.-K. and Kaldy- baeva, A.O. (2016) Production of the Mo- dified Liquid Glass in the Processing of Kao- linitic Clay. World Journal of Engineering and Technology, 4, 151-157. http://dx.doi.org/10.4236/wjet.2016.43D018