(Bi₂O₃Fe₂O₃)_0.4(Nb₂O₅)_0.6 was manufactured by employing solid state ceramic routing. For the preparation of the samples, 99.9% pure (Aldrich, India) Bi₂O₃, 99.9% pure (LobaCheme, India) Fe₂O₃, 99.9% pure (Merck, Germany) Nb₂O₅ were used as raw materials. Required amount of high purity Bi₂O₃ and Fe₂O₃ were weighed cautiously and mixed completely in an agate mortar for 1 hour. Mixed oxide was again thoroughly mixed using stabilized ZrO₂ balls in ethanol. After 24 hour milling in ethanol medium the solution was dried at 100˚C for 24 hour. Dried samples were again pasted with binder (Polyvinyl Alcohol, 4%). These powders were then compacted into discs with 10 mm diameter and 4 mm thickness. Powders were pressed under 254 MPa pressure by using a Hot Press (P/O/WEBER, PO 40 H, Germany). The final sintering was done at 850˚C, 925˚C, 1000˚C and 1150˚C for 2 hour with 1 hour holding time at 600˚C for the elimination of binder. For sintering, heating rate was 5˚C/min and cooling rate was 3˚C/min.

Dielectric properties of the samples were measured by an Impedance analyzer (Wayne Kerr 6500B, UK), for the measurement of dielectric property, both side of the polished pellet was painted by Ag paste. DC resistivity of samples was studied by an Electrometer (6517B Electrometer/High Resistance Meter, Keithley, Germany). Structural properties were investigated by X-ray Diffraction (D8 Advance, BRUKER, Germany) with CuK α (λ = 1.54) radiation and 2 θ ranges from 10˚ to 70˚. Scanning Electron Microscopy (EVO 18 Research: ZEISS, Germany) image of the samples were taken for the analysis of surface morphology.

Figure 1 shows the XRD pattern of (Bi₂O₃Fe₂O₃)_0.4(Nb₂O₅)_0.6 sintered at different temperature. Two phases were found for samples sintered at lower temperature (850˚C and 925˚C) and the phases are bismuth niobium oxide, BiNbO₄ and iron niobium oxide, Fe (NbO₄). Both of the phases has Orthorohombic lattice matched with JCPDS card no: 00-016-0295 and 01-084-1981 respectively. When sintering temperature increased, then single phase Bismuth Iron Niobium Oxide was found. When sample were sintered at 1000˚C then Bi_1.34Fe_0.66Nb_1.34O_6.35 is found. On the other hand Bi_1.721δ_0.089Fe_1.056Nb_1.134O₇ is found for sample which sintered at 1150˚C. Both Bi_1.34

Fe_0.66Nb_1.34O_6.35 and Bi_1.721δ_0.089Fe_1.056Nb_1.134O₇ are very similar. One has consecutive peak at 57.451˚ and 58.192˚ but the other has only one peak at 58.256˚. For Bi_1.721δ_0.089Fe_1.056Nb_1.134O₇ JCPDS card no is 00-060- 0267 and for Bi_1.34Fe_0.66Nb_1.34O_6.35 JCPDS card no is 00-052-1774.

SEM image in Figure 2(ii) reveals that grain sizes of the samples are almost identical at comparatively low sintering temperature (850˚C and 925˚C). When temperature increases to 1000˚C then grain size slightly increases and average grain size becomes 1.173 μm. It is clear from the microscopic view that at 1150˚C sintering temperature grain size is the largest among the four samples and the average grain size of Figure 2(ii)(d) is approximately 3.47 μm.

Figure 3 and Figure 4 represent the variation of dielectric constant and dielectric loss on frequency respectively. It is observed from the Figure 3, that the dielectric constant decreases with the increase of frequency. At low frequency higher value of dielectric constant is obtained on the other hand at higher frequency dielectric constant is more or less constant for all samples. This decrease of dielectric constant with the increase of frequency can be happened due to dipole relaxation phenomenon, where the dipoles can follow the frequency of the applied field at low frequencies [6] .

From Figure 4 it is found that dielectric loss decreases with the increase of frequency for the sample sintered at 850˚C, 925˚C and 1000˚C. But for the sample which sintered at 1150˚C shows a Debye like peak at higher frequency. According to Wang et al. [7] this higher frequency relaxation is attributed to the ionic relaxation and this type of behavior is supported by Feridoon et al. [8] .

Figure 5 and Figure 6 represent the effect of temperature on dielectric constant and loss tangent. The dielectric constant and loss tangent remain more or less constant up to 700˚C and only dielectric constant increases

slightly after 700˚C for the samples sintered at 850˚C and 925˚C, but loss remain constant for the whole range i.e.; up to 800˚C. For samples sintered at 1000˚C dielectric constant remain constant up to 800˚C but dielectric loss increases nearly at 800˚C.

But for samples having high sintering temperature (1150˚C) displays a sharp rise of dielectric constant when

measuring temperature is 800˚C. This rise of dielectric constant reveals that an anti-ferromagnetism to paramagnetism transition [9] has occurred. So, it can be said that for this sample Neel temperature (T_N) will be nearly at 800˚C. For other samples this temperature might be found when measuring temperature will be greater than 800˚C because before 800˚C no transition phase occurred for those samples.

Figures 7-10 are showing the effect of temperature on resistivity for (Bi₂O₃Fe₂O₃)_0.4(Nb₂O₅)_0.6 at different

voltage. Figure 7 reveals that for the samples sintered at 850˚C, resistivity of the samples decreases up to 150˚C measuring temperature. When measuring temperature is greater than 150˚C, then resistivity remains more or less constant. Resistivity decreases with the increase of temperature due to semiconducting nature [10] . Therefore it can be said that up to 150˚C, samples sintered at 850˚C showed semiconducting behavior. Samples sintered at 925˚C (Figure 8) evolve that resistivity (R) decreases sharply for all voltages up to 200˚C and above 200˚C, it

remains constant. It is also revealed that dR/dT is higher at lower voltage.

As a result, it can be said that specimens sintered at 925˚C show semiconducting nature up to 200˚C. Sample sintered at 1000˚C shows identical response with the samples sintered at 925˚C. Only difference between them is that resistivity falls after 150˚C when comparatively (80 V and 100 V) higher voltage applied.

On the other hand, sample sintered at 1150˚C evolves that resistivity decreases slowly up to 300˚C for all voltages. It is also found that dR/dT of the sample is lower in comparison with other samples.