The utilisation of lesser utilised timber species as replacement for the primary commercial wood species has been a matter of discussion for some time now. This is in the light of many efforts by research institutions such as the Forestry Research Institute of Ghana and Building and Road Research Institute of Ghana, in a bid to stop or minimise the extinction of some of the durable timber species due to overexploitation. The efficient utilisation of these lesser utilised species (LUS) depends on the knowledge of their anatomical properties among others [1] .

The natural forest resources in several tropical timber producing countries including Ghana are getting exhausted, resulting in reduced availability and quality of the preferred traditional timber species. The author states that although about 70 species are harvested and used commercially out of about 420 which grow to timber size in Ghana’s forests, the trade is dominated by about only eight species [2] . According to another author, of the 60 - 64 Ghanaian timber species, it is noted that Afzelia spp., Aningeria spp., Ceiba pentandra, Terminalia ivorensis, Pterygota macrocarpa, Khaya grandifoliola, Tarrietia utilis, Milicia excelsa, Terminalia superba, and Triplochiton scleroxylon are dominated in terms of volume exported [3] . About 160,594 m³ of these species were exported in 2004 [4] . By 2007, the total volume of these species exported had decreased to 97657.6 m³ [5] . Ghana forestry reports in recent years indicate that the species for which Ghana is known in international markets is becoming very scarce. Current thinking is that to reduce the pressures on the popular species, industry must take a close look at the lesser-species (LUS).

The utilisation of lesser utilised timber for bridges has been adopted in other African countries like Cameroon with considerable gain to the economy [6] . Zziwa et al. [7] studied non-traditional timber species used for furniture by Ugandan carpenters. Based on his findings, he urged that fast growing species such Pinus caribea should be planted to cater for the increasing demand for furniture products. In the work of another author, he discussed the possibility of using less known tropical hardwood species to meet the increasing demand on timber [8] . The use of Piptadeniastrum africanum as a promising alternative to Milicia excelsa was also suggested [9] . Furthermore, an author also suggested that the use of lesser utilised wood species would reduce negative ecological imparts such as reduction in biodiversity and desertification [10] .

There are several methods of studying the anatomy of wood. These include the use of hand lens, light microscope, and scanning electron microscope. More common techniques employ the use of the light microscope. With the light microscope, one can survey enormous quantities of material in a short time, exploring variability and distribution of features within the wood [11] .

In this work, we studied the anatomical properties of three lesser utilised wood species namely Albizia ferruginea (Guill. & Perr.) Benth, Blighia sapida K. D. Koenig, and Sterculia rhinopetala K. Schum. Some of the findings were that Albizia ferruginea had 63.3% fibers second to Blighia sapida with 64.3% of fibers. Sterculia rhinopetala had the lowest percentage of fibers with 43%. In vessel proportion, Blighia sapida had the proportion of 11.5% and a vessel density of 12 vessel/mm², followed by Sterculia rhinopetala with 7.3% and vessel density of 7 vessels/mm² and Albizia ferruginea with lowest proportion of vessels at 5.8% and vessel density of 6 vessels/mm².

This work will be organised as follows: Section, one introduction; section two, methodology; section three, results and discussion, and finally section four, conclusions and acknowledgements.

Three lesser utilised species Albizia ferruginea (Guill. & Perr.) Benth, Blighia sapida K. D. Koenig and Sterculia rhinopetala K. Schum were selected for anatomical study. The anatomical study was carried out in the wood anatomy laboratory of the University of Applied Science in Biel, Switzerland. Discs 10 cm thick were cut from a height of 1.30 m from the butt of the tree (Figure 1).

From each disc samples of 1 cm × 3 cm were taken from the heartwood portion. They were weighed and their densities determined by the oven dry method. The samples were then softened by first saturating with water and later soaking them in ethanol and glycerol (1:1) in labelled containers for an average period of about 20 - 30 days. Thin sections, 20 - 30 µm thick produced on a Leica sliding microtome were first washed in water and then in 1% safranin in 50% ethanol solution for about 10 - 20 minutes. After staining they were washed in water and dehydrated in increasing concentrations of ethanol: 30%, 50%, 70%, 85%, 90% and 100%.

After dehydration, they were permanently mounted in Canada balsam. Slides were examined using a Leica DMLM light microscope, and photographs taken using a Leica DFC 320 digital camera. Photomicrographs were then analysed with software Leica 1M 1000 Version 4.0 Release 132. For the Scanning electron microscope (SEM), small wood samples were thoroughly impregnated with an alkyd or acrylic resin and then allowed to cure [12] [13] . The resin was known to be resistant to acids such as 72% sulphuric acid which was used to remove the cellulose and hemicelluloses from the sample, and to a 50:50 mixture of 10% chromic and 10% nitric acids which dissolve the lignin. After careful washing with distilled water, the residue was a negative or cast of the openings in the wood which has been penetrated by the resin. After careful separation of the very small casts, they were dehydrated, mounted on a specimen stub, with a fixative solution of formalin. It was then coated with

a thin layer of gold in a sputter coater. The prepared sample was then placed in the sample chamber of a scanning electron microscope with a spatial resolution of 8.0 nm at 5 kV. SEM photomicrographs were produced and analysed. Vessel diameter was obtained by measuring 30 randomly selected pore, then taking the average. The frequency of vessels per mm² was calculated by counting the number of vessels in thirty 1-mm² fields, then taking an average. The micrographs were analysed using the stereological technique (Figure 2) for the proportion of the tissues [14] [15] . Thirty randomly selected micrographs for each tissue studied were used for study and then the averages taken. Dots grid were used to determine area fractions (P_p) of anatomical elements and oriented segments of predetermined length were used to determine the number of elements per unit length of the test line in the radial and tangential directions (NL_R・NL_T) (Figure 2). Standard areas were used to determine the number of elements per unit area (N_A). These basic counts were then used to derive other parameters such as proportion of elements in percentages. Splinters were also taken from the discs and macerated in a solution of equal parts of Acetic acid and hydrogen peroxide and heated in an oven at about 65˚C for 72 hours.

We performed stereo analysis of the microtome sections. The quantitative anatomical measurements are presented in Table 1. Albizia ferruginea had 63.3% fibers second to Blighia sapida with 64.3% of fibers. Sterculia rhinopetala had the lowest percentage of fibers with 43%. In vessel proportion, Blighia sapida had the proportion of 11.5% and a vessel density of 12 vessel/mm², followed by Sterculia rhinopetala with 7.3% and vessel density of 7 vessels/mm² and Albizia ferruginea with lowest proportion of vessels at 5.8% and vessel density of 6 vessels/mm². Of the three species, Albizia ferruginea had an average vessel lumen diameter of 215 µm (maximum 310 µm, minimum 121 µm). Blighia sapida had an average vessel lumen diameter of 178 µm (maximum 281 µm, minimum 91 µm) whilst Sterculia rhinopetala had an average vessel lumen diameter of 164 µm (maximum 257 µm, minimum 85 µm). Sterculia rhinopetala had the highest proportion of axial parenchyma of 34.3% followed by 23% of axial parenchyma in Albizia ferruginea. Axial parenchyma was however not distinct in Blighia sapida. Proportion of rays was in the order of 24.3%, 15.5%, and 8% for Blighia sapida, Sterculia rhinopetala and Albizia ferruginea respectively. Sterculia rhinopetala had twice as thick walled fibers as Blighia sapida, with average double fiber wall thickness of 806 µm and 432 µm respectively. Albizia ferruginea had an avearge double fiber wall thickness of 374 µm. With a mean fiber length of between 1474 - 1899 µm (Table 2), Sterculia rhinopetala had the longest fibers of the three selected species but the mean vessel lumen diameter was the smallest of the three species with a value of 164 µm. Albizia ferruginea had mean vessel lumen diameter value of 215 µm which was the largest of the three species while having relatively short fibers which ranged from 1196 - 1274 µm. Blighia sapida had a mean vessel lumen diameter of 178 µm and a mean fiber length of between 1127 - 1303 µm. This brings to the fore the fact that Sterculia rhinopetala has thick long fibers

Legend: DFWT―Double fiber wall thickness.

with small vessel lumen diameter whilst Albizia ferruginea had relatively short fibers with wide vessel lumens.

Qualitative analyses of the anatomical investigations are shown in micrographs in Figures 3(a)-(k). Figure 3(a) shows the transverse section of Albizia ferruginea showing solitary vessels with radial multiples of 2 - 4 vessels. Some of the vessels were occluded with tyloses. The axial parenchymas were arranged paratracheal, vasicentric, aliform and confluent. In the tangential section, Figure 3(b), the rays were storied and filled with inclusions.

The photomicrographs (Figures 4(a)-(e)) explain further observations made with the light microscope. Figure 3(a) Showed Albizia ferruginea with tyloses in vessel and Figure 4(a) enhances this feature; the tyloses. In

the same way, Figure 3(g). depicted rays in Sterculia rhinopetala filled with inclusions. Figure 4(b) threw more light on this feature. The sculptured wall of vessels and occluded pits in Blighia depicted in Figure 3(c) and Figure 3(d) was also better understood and seen properly in Figures 4(c)-(e) enhances the crystals in the rays seen in Figure 3(f).

The anatomical features identified macroscopically by Oteng-Amoako et al. [16] for Albizia ferruginea are that the vessels were medium and solitary with inclusions present this has been made clearer by the microscopic study as seen in Figure 3(a). More so, the macroscopic identification indicated that the axial parenchyma was as seen in Figure 3(a). The axial parenchyma is present and appears as aliform and confluent paratracheal and in the tangential section the rays are storied and also filled with inclusions (Figure 3(b)) whilst the macroscopic

identification did not indicate the inclusions in the rays for the same species. According to an author, vessel diameter and vessel distribution have effect on water conduction efficiency [17] . Therefore with vessel distribution of 6 vessels/mm², and a maximum vessel lumen diameter of 310 µm it could be expected of Albizia ferruginea to have high water uptake. Formation of tyloses in this species may be another reason for its high durability, since tyloses apparently assist in restricting pathogen movement [18] . He indicated that, in elm trees, tyloses formation was correlated with increased resistance to Dutch elm disease.

For Blighia sapida, features identified macroscopically which was also confirmed microscopically were vessels distribution with inclusions, axial parenchyma not distinct and ray parenchyma not distinct however the microscopic tangential section gives a very distinct heterocellular ray parenchyma which are multiseriate and uniseriate (Figure 3(d)). Furthermore, the SEM micrographs Figure 4(c)-(e) throws more light on how sculptured the vessels are, that there are not just inclusions in the vessels but some of the vessels are occluded as well as have prismatic substances in some of the vessel lumens (Figures 3(f) and Figure 4(e)) which will help to better understand the wood when in use. Vessel wall sculpturing as seen in Figure 4(c) agreed with the findings [19] . Prismatic crystals occurring in the ray cells as depicted in Figure 3(f) and highlighted by SEM micrographs in Figure 4(c) was also confirmed [19] . The presence of these substances could blunt tools when this species is being sawed and also occupy sites where water could have occupied thereby contributing to lower water/moisture uptake.

Sterculia rhinopetala had fewer fibers than the other two species. Most of its fibers had thicker walls and that could account for its high bending strength and density. Since according to the authors, fiber wall thickness is closely linked with density, i.e. the thicker the wall, the higher the density [20] . From Figure 4(b), it was seen that Sterculia rhinopetala had almost all its axial parenchyma occluded with substance which probably maybe the polyphenols and this could be responsible for its durability. The actual composition of the substances was yet to be identified. These substances could also act as bulking agents preventing moisture intake and for that matter water. The low water uptake of Sterculia rhinopetala can be explained by the fact that thick-walled fibers go hand in hand with thick-walled vessels and therefore low water uptake.

Another advantage of having thick-walled vessels was narrow vessel lumens which leads to resistance to embolism; that is the situation where gases fill the conduit and leads to cavitation. This was because it has been stated that the spread of embolisms within a conducting element, and from vessel element to element through the perforation plates, causes the entire vessel to become dysfunctional [18] . Ewers [21] prepared a diagram of a trade-off triangle of wood functions and associated anatomical features, the points of the triangle being 1) resistance to embolism (narrow vessels), 2) conductive efficiency (wide vessels), and 3) mechanical strength (thick-walled fibers). It was proposed that there is a negative relationship between mechanical strength and conductive efficiency and a positive relationship between mechanical strength and safety. Wheeler et al. [22] in discussing the variation in global dicotyledon wood anatomy, asserts that woods with thick-walled fibers have thick-wall vessels which result in low conductive efficiency. Therefore it is understandable that Sterculia rhinopetala with thick-walled fibers has low water uptake due to narrow vessel lumen. In the same way, another author stated that the characteristics of these fibrous cells and their arrangement affect strength properties, appearance, and resistance to penetration by water and chemical solutions, resistance to decay and many other properties [23] .

We studied Albizia ferruginea, Blighia sapida, and Sterculia rhinopetala all belonging to the lesser utilised wood species. We found out that Albizia ferruginea had on the average two out of six of its vessels occluded with tyloses. These tyloses and inclusions occluded some of the vessels of this species thereby lowering the uptake of substances such as water and also prevent pathogen movement. These inclusions which are organic may be hydrophilic, accounting for the high water uptake even though it is highly durable. Such observation has also been found as reported and cited in International Agency for Research on Cancer (IARC) [24] monograph, indicating that some extractives such as tannins are polar and are generally able to dissolve in water making them hydrophilic [25] .

We also identify cell wall sculpturing and the presence of prismatic substances in the cell lumen of Blighia sapida which may affect transfer of substance between cells. The crystals may also affect machining of the wood by blunting the tools. The occluded pits of Blighia sapida could also hinder transportation of water and minerals between the cells.

Lastly but not the least, we noticed that narrow vessel lumens in Sterculia rhinopetala also affected water uptake and therefore made the wood species less permeable and the thick cell walls also made this wood very strong and stiff.

Anatomical features and structures studied helped explain the results of the properties of the wood species. It was possible to make certain predictions about wood properties from careful anatomical examinations. Accordingly woods with many thick-walled cells would be stronger, heavier and stiffer than wood with thin-walled elements. Some anatomical features like fibre wall thickness have an effect on the bending strength of the species. Some inclusions which may include extractives found in Albizia ferruginea and Sterculia rhinopetala could be responsible for their natural durability. The use of scanning electron microscopy (SEM) to examine the anatomical and ultrastructural aspects of wood has been found to be a useful approach to a clearer understanding of the features and structures found in wood.

It has enabled us to identify some of the features that are not visible macroscopically, for example, the presence of crystals in Blighia sapida and the thick-walled fibers of Sterculia rhinopetala and the absence of axial parenchyma in Blighia sapida.

I am grateful to Professor Maurice Brunner, Prof. Dr Ernst Zurcher and Dr. Thomas Volkmer all of the University of Applied Science, Biel in Switzerland for their guidance and support during my stay with them. I also want to thank the Swiss National Science Foundation and Get Fund for financial support. Final thanks goes to my supervisor, Prof. Frimpong Mensah of Kwame Nkrumah University of Science and technology.

Gladys A.Quartey, (2015) Anatomical Properties of Three Lesser Utilised Ghanaian Hardwood Species. Materials Sciences and Applications,06,1111-1120. doi: 10.4236/msa.2015.612110