In 1988, a new class of superior soft magnetic iron based alloys was introduced by Yoshizawa, Oguma and Yamauchi [1] . Those alloys have low losses, high permeability and near zero magnetostriction which indicate the soft magnetic materials. Later soft magnetic properties have been successfully addressed by Herzer [2] with the help of random anisotropy model. Because of the ultrafine microstructure of bcc Fe-Si with grain sizes of 10 - 15 nm, the Fe_73.5Cu₁Nb₃Si_13.5B₉ alloys are known as nanocrystalline. The soft magnetic properties of Fe_73.5Cu₁ Nb₃Si_13.5B₉ and related alloys were reported by many publications [3] - [8] .

Based on random anisotropy model, by taking into account the nanocrystalline materials as a single phase magnetic system, Herzer explained the grain size dependence of the coercivity. By considering two phase materials, Hernando et al. [9] extended this model and were able to explain the thermal dependence of the coercivity [10] - [12] . Also based on the random anisotropy model, Herzer established the early explanation of the soft magnetic properties of these nanocrystalline alloys which were related to the ratio of the domain wall thickness to the mean crystallite size [5] . This model explained the main feature of the dependence of coercivity on the grain size [13] [14] . Some previous researches showed that at the very beginning of nanocrystallization, magnetic hardening took place [15] - [18] . Stoner and Wohlfarth [19] theoretically proposed single domain permanent magnets. From the single domain permanent magnets, high coercivity is obtained by mechanically locking the magnetized single domain particles. However, we can produce soft magnetic materials by reducing the size of the magnetic particle much below the critical size, which is normally of nanometer order.

If Fe-Si-B based amorphous ferromagnetic materials heated below their crystallization temperature, then good soft magnetic properties were observed. After partial crystallization of Fe_73.5Cu₁Nb₃Si_13.5B₉, subjected to heat treatment just above the crystallization temperature for a specific time, an extraordinary high permeability i.e. two order of magnitude was developed which was higher than their conventional Fe-Si-B based alloys. The annealed nanometric grain size of 4 - 30 nm is developed for the heat treatment of the alloy. If the grain size is 10 - 12 nm then good magnetic properties are obtained. If, where Lex is the ferromagnetic exchange length [6] [8] and D is the average grain size, then best magnetic properties are obtained. According to calculation, for Fe(Si) alloy, Lex 35 nm [20] .

The aim of the present research work is to synthesize Fe-based alloys of Fe_73.5Cu₁Nb₃Si_13.5B₉ composition in the amorphous state by using rapid solidification technique and study their magnetic properties with the evolution of different phases by varying annealing condition. Annealing of Fe-based soft nanocomposite magnetic materials has been performed in air. Then, the Curie temperature, initial permeability, hysteresisgraph (BH- loop), temperature dependence relative quality factor and loss factor of the composition Fe_73.5Cu₁Nb₃Si_13.5B₉ are determined. X-ray diffraction technique has been used for the characterization of nanostructured phases. The purpose is to correlate the evolution of nanograins, their volume fraction and size with the magnetic properties of the composition.

The ribbons with composition Fe_73.5Cu₁Nb₃Si_13.5B₉ has been prepared by rapid solidification technique. The amorphous ribbons are prepared at a temperature 1500˚C in an argon atmosphere (0.2 to 0.3 atoms). The dimension of the ribbon was 10 mm width and 25 mm thickness. The purity of the material is Fe (99.98%), Cu (99%), Nb (99.8%), Si (99.9%) and B (99.5%) as obtained from Johnson Mathey (Alfa Aesar Inc.).

A PHILIPS PW3040 X' Pert PRO X-ray diffractometer was used to study the crystalline phases of the prepared samples in the Materials Science division, Atomic Energy Centre, Dhaka. The powder specimens were exposed to CuK_a radiation with a primary beam of 40 kV and 30 mA with a sampling pitch of 0.02˚ and time for each step data collection was 1.0 sec. A 2q scan was taken from 10˚ to 90˚ to set possible fundamental peaks where Ni filter was used to reduce CuK_a radiation. All the data of the samples were analyzed using computer software “X’PERT HIGHSCORE”. X-ray diffraction patterns were carried out to confirm the crystal structure. Instrumental broadening of the system was determined from q - 2q scan of standard Si. The average grain size of the crystallites α-Fe(Si) were determined by Scherrer’s method [21] after correction for instrumental boarding.

As a function of frequency, dynamic magnetic properties of the nanocrystalline magnetic ribbon with composition Fe_73.5Cu₁Nb₃Si_13.5B₉ have been measured. By using a laboratory built furnace and Wayne Kerr 3255B impedance analyzer, temperature dependence of initial permeability of the as cast and annealed ribbons was measured. The Wayne Kerr 3255B impedance analyzer was operated with very low applied ac field of ~10⁻³ Oe from room temperature to above 600˚C with continuous heating rate of ~5˚C/min. With the equation of µ' = L/L₀, the permeability µ' was calculated, where L is the measured sample inductance and L₀ is the inductance of the coil of same geometric shape of vacuum. With the equation of μ" = µ' D, the imaginary permeability μ" was determined, where D = tanδ, the loss tangent of the sample. On piece of each ribbon has been measured at room temperature after subsequent annealing treatments in order to avoid the experimental error due to fluctuation in ribbon thickness and thermal treatments. From the temperature dependence of permeability measurements, the Curie temperature was determined. The permeability shows an abrupt drop to a very low value at Curie temperature. B-H loops were measured by using a B-H loop tracer.

Figure 1 represents the X-ray diffraction spectra of quenched alloy and the alloy annealed at different temperatures for 30 min. In the figures, the parenthesis represents the indices of the reflecting planes of the phases. bcc a-Fe(Si) phases are found, identified by using standard software. From the X-ray fundamental line (110), the mean grain size of the nanograins was determined by using the Scherrer’s formula.

In order to determine the Curie temperature of amorphous sample, the real part of the complex initial permeability µ' vs. temperature T curves has been presented in Figure 2 for as-cast sample. The Curie temperature has been estimated to be 355˚C for this alloy composition in the as-cast condition. It has been found from Figure 2 that µ' decreases gradually and then there is a sharp increase of µ' near the Curie temperature which is a characteristic feature of the Hopkinson effect.

In Figure 4, for as-cast and annealed samples, the real part of the complex initial permeability µ' up to f = 10,000 kHz has been measured and presented. The results refer to isothermal annealing time of 30 min. It can be noted that µ' increase with the increase of annealing temperature and it drops at critical frequencies rapidly.

In Figure 6, the annealing temperature dependence of relative quality factor µ'/D of the samples at different frequency and a fixed 30 minute annealing time are presented. The relative quality factor increases with increasing annealing temperature up to 560˚C when the applied frequency is 1 kHz, 2 kHz and 3 kHz. Then, a rapid decrease of relative quality factor with increasing annealing temperature is above 560˚C. In the similar manner, the relative quality factor increases with increasing annealing temperature up to 545˚C when the applied frequency was 5 kHz and 10 kHz. A rapid decrease of µ'/D with increasing annealing temperature above 545˚C was noticed when the applied frequency was 5 kHz and 10 kHz. For the sample annealed at 545˚C for 30 minute give the maximum quality factor if the applied frequency is lowers i.e. 10 kHz. This gives a choice of optimal annealing temperature for attaining best magnetic properties.

In Figure 7, the annealing temperature dependence of loss factor of the samples measured at different frequency have been presented. Loss factor rapidly decreases with increasing annealing temperature for all applied frequencies i.e. 2 kHz, 3 kHz, 4 kHz, 5 kHz and 50 kHz. Loss factor has high value at 50 KHz and decreases with the decrease of frequency. In Figure 8, the B-H loops at room temperature and at a constant frequency 1 kHz of the alloy were presented. Figures 9(a)-(d) represent the annealing time (ta) dependence of magnetic flux density (Bv), remanence (Br), coercivity (Hc) and loss (W/kG) of the sample annealed at temperature Ta = 545˚C respectively.

Crystalline phases that developed through heat treatment have been studied by X-ray diffraction and presented in Figure 1. In the as cast condition, the sample is in the amorphous state having no sharp peaks of crystalline phase since no crystalline phase has formed due to rapid quenching. When the sample is annealed above the crystallization temperature, nanocrystalline grain of α-Fe(Si) was formed in the amorphous precursor. X-ray diffraction results indicate that no α-Fe phases are present in the alloys annealed below 510˚C. The appearance of broader diffused pattern is also the characteristic of amorphous material was observed bellow the annealing temperature 510˚C. Crystalline phase was developed on the amorphous ribbon, when the alloys were annealed at or above 525˚C. The grain size increases gradually and attains a limiting value of 7 to 14 nm until 560˚C, which is very suitable for the exchange coupling through residual amorphous matrix [23] . A sudden increase of grain size above 650˚C was observed, achieving a value of 18 and 23 nm at 600˚C and 680˚C, respectively [22] . Because annealing at higher temperature above 680˚C leads to the precipitation of Fe-borides [24] . The nanocrystalline material obtained in this way displays improved mechanical and magnetic properties in comparison to the

ones achieved by conventional annealing [2] [5] [25] .

The temperature at which the ferromagnetic material becomes paramagnetic is known as Curie temperature. From the initial permeability µ' versus annealing temperature T curves, the Curie temperature (Tc) of the Nanocrystalline ribbons of the sample Fe_73.5Cu₁Nb₃Si_13.5B₉ has been determined. At fixed frequency (1 kHz), from the as-cast condition of Fe_73.5Cu₁Nb₃Si_13.5B₉ alloy, the temperature dependence of real part of the initial permeability has been presented in Figure 2 in order to determine the Curie temperature of the sample. The ferromagnetic to paramagnetic transition of the amorphous phase can be characterized by Hopkinson effect and can be determined from the as-cast sample if the initial permeability passes through a maximum just before a sharp fall. Due to irreversible components of the structural relaxation like chemical short-range order, topological and long-range internal stress of the materials, it is very much difficult to determine the accurate Curie temperature, Tc of the amorphous materials. Curie temperature Tc may influence with this structural relaxation without destroying the amorphous state. So, the heating rate should be adjusted in such a way during the measurement of Tc that, no substantial relaxation takes place. Figure 2 shows that, with increasing the annealing temperature the initial permeability of the nanocrystalline sample also increase. The maximum initial permeability µ׳ found at 350˚C and above the 350˚C annealing temperature, the permeability decrease rapidly. Thus Curie temperature has been estimated as 355˚C from the sharp fall of the initial permeability after 355˚C [26] . In the similar way, the various curie temperature of residual amorphous matrix are determined like 350˚C, 367˚C, 350˚C and 310˚C from the variation of µ׳ with temperature for the toroidal samples annealed at 400˚C, 450˚C, 490˚C and 525˚C respectively have been presented in Figure 3.

For as cast and annealed samples, real part of the complex initial permeability µ' has been presented in Figure 4 up to f = 10,000 kHz. Magnetic initial permeability are measured in very low field of the toroidal shaped samples annealed at different temperatures, in order to correlate the soft magnetic properties of the alloys with microstructural features. From the domain wall mobility especially in the range of reversible magnetization, the magnetic properties of the soft magnetic materials are determined. Figure 4 shows that the real part of initial permeability µ' decreases when the frequency increases and µ' becomes almost zero at very high frequency. This is because the very high frequency indicates the AC field and magnetization is opposed by AC field. As a result, at higher frequencies damping of the domain walls occurs and for this permeability drops to a very low value. This phenomenon defines the best frequency range at which a particular magnetic material can be used for practical application.

From the annealing temperature dependence of initial permeability and relative loss factor curve (Figure 5), the role of amorphous phase in intergrain coupling can be easily realize. The curve express itself strong depen-

dence of initial permeability on annealing temperature. Due to irreversible structural relaxation of the amorphous matrix, an increase of initial permeability with annealing temperature was observed when the sample annealed at temperature below the crystallization, i.e. up to 470˚C. Permeability decrease with the increase of annealing temperature up to 490˚C and beyond 490˚C annealing temperature i.e. from 510˚C to 545˚C a sharp increase of permeability was observed due to crystallization of α-Fe(Si) phase. For the annealing temperature of 545˚C, an enhancement of initial permeability by two orders of magnitude was observed (μ' = 23,065). From the other part of Figure 5 it was observed that, the relative loss factor drops sharply as the annealing temperature increased and at annealing temperature 545˚C a minimum value relative loss factor (=4.002 × 10⁻⁵) was found. Beyond this temperature μ' drops to lower value drastically and again increases very rapidly, as a result of magnetic hardening takes place [16] .

At different frequency, the annealing temperature dependence of relative quality factor μ'/D and loss factor D of the samples are presented in Figure 6 and Figure 7 respectively. From the application point of view, for the soft magnetic materials both loss factor tand or D and relative quality factors are the important parameters. Soft magnetic materials must have minimum loss factor and maximum relative quality factors. It is well-established that, minimum loss and very high relative quality factor with the order of magnitude 10⁵ - 10⁶ observed upon optimal annealing nanocrystalline alloys. By the successive annealing of the alloys from 350˚C to 600˚C, the optimal annealing temperature is determined. At high frequency the flux penetration becomes low, as a result the loss is mainly controlled by interaction between the grains of the alloy but at very low frequency the loss is controlled by hysteresis losses.

Measurement of a hysteresis loop is a very simple and fast method to characterize magnetic materials. The hysteresis curves and their properties such as the remanence (Br), coercivity (Hc), and hysteresis loss (W/kG) are very useful information from the application point of view. The B-H loops at room temperature of the investigated alloy Fe_73.5Cu₁Nb₃Si_13.5B₉ were measured at a constant frequency (f = 1 kHz), and the results are presented in Figure 8. From these loops, Br, W/kG, and Hc were determined. In Figures 9(a)-(d), it can be observed that the magnetic flux density (Bv), remanence, coercivity and also hysteresis loss decrease with increase in annealing time, which implies good soft magnetic property of the alloy of Fe_73.5Cu₁Nb₃Si_13.5B₉ (Table 1).

Annealing at temperatures 545˚C for 30 min best soft magnetic properties has been achieved which corresponds

to a maximum value of initial permeability (μ') which is 23,065 while the corresponding value of relative loss factor is 4.002 × 10⁻⁵ at a low frequency f = 1 kHz. At 545˚C, from magnetic hysterisisgraph we observe low core loss (26.234 - 17.752) W/kG, low remanence (3.224 - 2.183) kG and low coercivity (0.616 - 0.406).

The authors are thankful to Materials Science Division, Atomic Energy Centre, Dhaka-1000, Bangladesh for providing the amorphous Fe_73.5Cu₁Nb₃Si_13.5B₉ ribbon materials and for extending experimental facilities. We also thank Dr. Sheikh Manjura Hoque, Materials Science Division, Atomic Energy Centre, Dhaka-1000, for her valuable suggestions for the research work.

Md. KhalidHossain,JannatulFerdous,Md. ManjurulHaque,A. K. M. AbdulHakim, (2015) Study and Characterization of Soft Magnetic Properties of Fe_73.5Cu₁Nb3Si_13.5B₉ Magnetic Ribbon Prepared by Rapid Quenching Method. Materials Sciences and Applications,06,1089-1099. doi: 10.4236/msa.2015.612108