OJPChemOpen Journal of Polymer Chemistry2165-6681Scientific Research Publishing10.4236/ojpchem.2012.22009OJPChem-19536ArticlesChemistry&Materials Science Surface Modification of Waste Tire by Grafting with Styrene and Maleic Anhydride assinA. Aggour1*AyedS. Al-Shihri1MohamedR. Bazzt1Chemistry Department, College of Science, King Khalid University, Abha Kingdom of Saudi Arabia* E-mail:Yassina9@yahoo.com(AAA);3005201202027076March 21, 2012May 7, 2012 May 15, 2012© Copyright 2014 by authors and Scientific Research Publishing Inc. 2014This work is licensed under the Creative Commons Attribution International License (CC BY). http://creativecommons.org/licenses/by/4.0/

Waste tire powder, as waste rubber WR was subjected to grafting with styrene (St) and maleic anhydride (MA). Hydrogen peroxide H2O2 was used to initiate the free radical copolymerization of St onto WR. A thermal initiation was used in case of grafting of MA onto WR. Effect of initiator and monomer concentrations together with the influence of reaction temperature and reaction time were investigated. The grafting was estimated by weight, and the grafted copolymers were characterized by FT/IR, DSC and SEM to prove the grafting. It has found that the grafting increases with increase monomer and initiator concentrations. The increase in the reaction temperature and time also causes increasing levels of the grafted St and MA.

Waste Rubber; Grafted Copolymerization; Styrene; Maleic Anhydride1. Introduction

Vulcanized waste rubber especially the scrap tires, cause several environmental problems. Recycling of waste rubber by grafting or blending with polymeric material has become an important in last decades. Surface modification of ground waste tire powder by chlorination and amination reactions, and by photo grafting using UV energy, have been studied [1-3]. Recently authors are modified the surface of rubber crumb with ozone [4], the enhancement of mechanical properties by blending of polypropylene with ground waste rubber powder were done [5]. Also the scrap tires are used as adsorbents for adsorption of organic and inorganic solutes [6]. Grafting copolymerization methods are increasing employed, because of permanent modification effects [7,8]. Styrene is widely used monomer for grafting reaction, due to high reactivity of benzene ring. Therefore, many efforts have been devoted to investigate the grafting of styrene onto various substrates [9,10]. Surface graft polymerization is important because it can provide materials with tailored properties for practical application. The ground tire rubber particles can be modified by grafting with styrene and acrylate [11]. Zhang et al., show that the grafted styrene onto waste rubber powder form core-shell structure [12]. The main advantages of polystyrene are its transparency, high stiffness, excellent process ability and good dielectric properties. Pukkata et al. [13], found that graft polymerization depend not only on the number of active site generated on rubber particles but also on feed of styrene.

Modification of different kinds of rubber using maleic anhydride (MA) is useful to enhance compatibility of immiscible blends as well as improving interfacial adhesion in polymeric composites [14]. Maleic anhydride was successfully photo grafted onto low density polyethylene film, and the surface hydrophilic properties of the grafted films were improved [15,16]. The grafting of maleic anhydride onto natural rubber, was generally carried out in the molten state [17-19]. The initiation system used in the grafting was peroxide initiator [20], or the shearing action [16-18] of the materials in an internal mixer at high temperature. Very limited data on preparation of MA grafted natural rubber in the solution state [21]. Different techniques have been reported to know the MA content grafted onto rubber, such as titration of acid group, gravimetry, infrared spectroscopy and so on [22].

In this work, powdered waste tires (as waste rubber), were used as a polymer backbone for the grafting reaction with styrene and maleic anhydride.

The effect of monomers (St or MA), initiator concentration (H2O2) (in case of St) as well as the reaction time and reaction temperature was studied. The surface chemistry of untreated and treated waste rubber (WR) was characterized by FT/IR spectroscopy, DSC thermal analysis and by scanning electron microscope (SEM).

2. Experimental2.1. Materials

The ground scrap tires with an average particle size 0.2 - 0.4 mm was prepared from waste tires SBR (styrenebutadiene rubber), USA, which contain about 60% SBR and 40% various additives. Styrene and maleic anhydride (Aldrich) are used without further purification. H2O2, fuming H2SO4 (Fluke). The other chemical solvents and reagents used are of analytical pure grade.

2.2. Surface Grafting Process

The appropriate quantities of WR and St were added in a special designed steel reactor. The requisite amount of H2O2 (initiator) were added and the reactor closed tightly at the required temperature for certain demand time. After the reaction completed, reactor is cooled and opened carefully, then the polymerization mixture was poured into acetone and leaved for 24 h. Washing of grafted polymer carried using chlorobenzene, followed by drying at 40˚C for two days to constant weight.

The above procedure was used for grafting of MA onto WR without using chemical initiator, only by thermal initiation. Sulfonation of WR and WR-g-St was carried using fuming conc. H2SO4 at 80˚C for 8 h. All treated waste rubber material was dried in an oven at 40˚C for 24 h prior to further use.

2.3. Determination of Grafting Yields

Grafting yields were characterized by the following parameters:

Grafting percentage: Gp% = (A – B/B) × 100 Weight conversion: Wc% = (A ÷ B) × 100 where A and B are the weights of the grafted product and WR respectively.

2.4. Characterization Methods

FT/IR spectra were recorded using JASCO FT/IR 460 plus spectrophotometer. Scanning electron microscope (SEM) 6360 (LA) were used to investigate the microstructure of the polymers. Thermal date was obtained by using Shimadzu DSC-50 instrument.

3. Results and Discussion

The grafting of St or MA onto WR was performed at various conditions to get the most suitable conditions for grafting. The variables studied were temperature, time, and the amounts of monomers and initiator.

3.1. Effect of the Reaction Temperature

The graft copolymerization of St onto WR was carried out at four different temperatures ranging from 75˚C to 150˚C. The initiator and WR concentration were 0.5 and 0.25 g/ml respectively, for three days. In Table 1, we see that at higher temperature up to 125˚C, higher level of grafted St and Gp% and Wc% increases. These are attributed to high temperature lead to dissociation of H2O2, and the free radicals increased on the WR chains leading to improve the grafting. Also at such temperature the mobility of WR chains will improved, which enhance the reaction process. Higher temperature than 125˚C cause the grafting decreased, which could be due to degradation of the grafted polymer [23,24].

Table 2 shows the effect of temperature on the grafting of MA onto WR, at temperature ranged from 130 to 250˚C without initiator, at time 5 h and concentrations of MA and WR were 0.3 and 0.25 g. Again as temperature increase the mobility of WR chains increase, leading to reach of MA onto active sites of WR and grafting increase. However, at elevated temperature cause decompose of grafted polymer, resulting Gp% and Wc% declined.

ReferencesY. A. Aggour, A. S. Al-Shihri and M. R. Bazzt, “Recycling of Vulcanized Waste Rubber through Halogenations and Amination Chemical Reactions,” WIT Transaction on Ecology & Environment WIT Press, Vol. 120, 2009, pp. 875-883.K. I. Lee and S. H. Ryu, “Ultraviolet Photo Grafting Reaction of Acrylamide onto Styrene-Butadiene Rubber,” Elastomers, Vol. 33, No. 4, 1998, p. 363. J. J. Yu and S. H. Ryu, “Ultraviolet-Initiated Photo Grafting of Glycidyl Methacrylate onto Styrene-Butadiene Rub- ber,” Journal of Applied Polymer Science, Vol. 73, No. 9, 1994, pp. 1733-1739. doi:10.1002/(SICI)1097-4628(19990829)73:9<1733::AID-APP14>3.0.CO;2-JF. Cataldo, O. Ursini and G. Angelini, “Surface Oxidation of Rubber Crumb with Ozone,” Polymer Degradation and Stability, Vol. 95, No. 5, 2010, pp. 803-810. doi:10.1016/j.polymdegradstab.2010.02.003S. L. Zheng, Z. X. Zheng, K. Pal, Z. X. Xin, J. Suh and J. K. Kim, “Prediction of Mechanical Properties of Waste Polypropylene/Waste Ground Tire Powder Blends Using Artificial Neutral Networks,” Material & Design, Vol. 31 No. 8, 2010, pp. 3624-3629. doi:10.1016/j.matdes.2010.02.039C. T. Torrado, M. A. Franco, C. F. Gonzalez, M. A. Domingues and V. G. Serrano, “Development of Adsor- bents from Used Tires Rubber, Their Uses in the Adsorption of Organic and Inorganic Solutes in Aqueous Solution,” Fuel Processing Technology, Vol. 92, No. 2, 2011, pp. 206-212.C. Geismann and M. Ulbricht, “Photoreactive Functionalization of Poly(Ethylene Terphthalate) Trak-Etched Pore Surfaces with Smart Polymer Systems,” Macromolecular Chemistry and Physics, Vol. 206, No. 2, 2005, pp. 268- 281. doi:10.1002/macp.200400374Y. A. Aggour, A. S. Al-Shihri and M. R. Bazzt, “Chemical Modification of Scraped Tires through Grafting with AMPS,” 2012, in press. J. Cha and J. L. White, “Styrene Grafting onto a Polyolefin in an Internal Mixer and Twin-Screw Extruder,” Polymer Engineering Science, Vol. 41, No. 7, 2001, pp. 1238-1250. doi:10.1002/pen.10825T. Rager, “Pre-Irradiation Grafting of Styrene/divinyl- benze onto PTFE Co-Hexafluropropylene from Non- Solvents” Helvetica Chemica Acta, Vol. 86, No. 6, 2003, pp. 1966-1981.S. Coiai, E. Passaglia and F. Ciardell, “Gradient Density Grafted Polymers on Ground Tire Rubber Particles by Atom Transfer Radical Polymerization,” Macromolecular Chemistry and Physics, Vol. 207, No. 4, 2005, pp. 2289- 2298. doi:10.1002/macp.200600376J. L. Zhang, X. H. Chen, C. M. Ke, Y. Zhou, H. Z. Lu and D. L. Wang, “Graft Polymerization of Styrene onto Waste Rubber Powder and Surface Characterization of Graft Copolymer,” Polymer Bulletin, Vol. 68, No. 3, 2012, pp. 789-801. doi:10.1007/s00289-011-0586-9N. Pukkate, Y. Yamamoto and S. Kawahara, “Mechanism of Graft Copolymerization of Styrene onto Deproteinized Natural Rubber,” Colloid Polymer Science, Vol. 286, No. 4, 2008, pp. 441-416. doi:10.1007/s00396-007-1787-5S. Newman, “Rubber Modification of Plastics,” In: D. R. Paul and S. Newman, Eds., Polymer Blend, Academic Press, New York, Vol. 2, 1978, p. 63J. P. Deng, W. T. Yang and B. Ranby, “Melt-Photo- grafting Polymerization of Maleic Anhydride onto LDPE Film,” European Polymer Journal, Vol. 38, No. 7, 2002, pp. 1449-1455. doi:10.1016/S0014-3057(02)00004-6J. P. Deng and W. T. Yang, “Surface Photo-Grafting Polymerization of Vinyl Acetate Malic Anhydride and Their Charge-Transfer Complex IV. MA,” Journal of Applied Polymer Science, Vol. 87, No. 14, 2003, pp. 2318-2325. doi:10.1002/app.11734E. Carone, U. Kipcak Jr, M. C. Goncalves and S. P. Nunes, “In Situ Compatibilization of Polyamide 6/Natural Rubber Blends with Maleic Anhydride,” Polymer, Vol. 41, No. 15, 2000, pp. 5929-5935. doi:10.1016/S0032-3861(99)00800-9C. Nakason, A. Kaesaman, Z. Samoh, S. Homsin and S. Kitkamjonwong, “Rheological Properties of Maleated Natural Rubber and Its Blends,” Polymer Testing, Vol. 21, No. 4, 2002, pp. 449-455. doi:10.1016/S0142-9418(01)00109-XC. Nakason, A. Kaesaman, S. Homsin and S. Kiatkamjonwong, “Rheological and Curing Behavior of Reactive Blending, Maleated Natural Rubber Cassava Starch,” Journal of Applied Polymer Science, Vol. 81, No. 11, 2001, pp. 2803-2813. doi:10.1002/app.1728M. Saedan, T. Navarat and A. Sobmbat, “Grafting of Maleic Anhydride on Natural Rubber Molecules in a Molten State,” The National Research Council of Thailand, Bangkok, 1997.C. Nakason, A. Kaesaman and P. Supasanthitikul, “The Grafting of Maleic Anhydride onto Natural Rubber,” Polymer Testing, Vol. 23, No. 1, 2004, pp. 35-41. doi:10.1016/S0142-9418(03)00059-XF. M. B. Coutinho and M. I. P. Ferreira, “Characterization of EPDM Rubber Modified with Maleic Anhydride by Diffuse Reflective FTIR,” Polymer Testing, Vo. 13, No. 1, 1994, pp. 25-34. doi:10.1016/0142-9418(94)90037-XY. A. Aggour, G. Bekhat and A. M. Atia, “Copolymerization and Thermal Investigation of AMPS with Acrylonitrile,” Journal of Polymer Materials, Vol. 17, No. , 2000, p. 193.J. Deng and W. Yong, “Grafting Copolymerization of Styrene and Maleic Anhydride Binary Monomer System Induced by UV Irradiation,” European Polymer Journal, Vol. 41, No. 11, 2005, pp. 2658-2692. doi:10.1016/j.eurpolymj.2005.05.022Y. A. Aggour, “Modification of Polystyrene Properties through N-vinylcarboxamido-2-methylpropane Sulfonic Acid Monomer,” Polymer International, Vol. 53, No. 12, 2004, pp. 1930-1935. doi:10.1002/pi.999Z. G. Shen, H.-M. Li, H.-B. Chen and S. G. Lin, “Preparation and Characterization of MA functionalized Syndiotactic Polystyrene,” Polymer, Vol. 43, No. 20, 2002, pp. 5455-5461. L. J. Bellamy, “The Infrared Spectra of Complex Molecules,” Wiley, New York, 1964.F. Chen and J. Quian, “Studies of the Thermal Degradation of Waste Rubber,” Waste Management, Vol. 23, No. 6, 2003, pp. 463-467.G. S. Miguel, J. Aguodo, D. P. Serrano and J. M. Escola, “Thermal and Catalytic Conversion of Used Tyre Rubber and Its Polymeric Constituents Using Py-GC/MS,” Applied Catalysis B: Environmental, Vol. 64, No. 3-4, 2006, pp. 209-219.