Loosely crosslinked hydrophilic polymers (hydrogels) being able to absorb and retain hundreds of their own weight of water are known as superabsorbents [1]. The swelling properties of these hydrogels have attracted the attention of researchers and technologists, and have found wide-spread applications in drug delivery systems, agriculture, separation processes and many other fields [2-7].

The modification of natural polymers is a promising method for the preparation of new materials. Graft copolymerization of vinyl monomers onto natural polymers is an efficient approach to achieve these materials. Superabsorbing resins were first developed with a view to utilizing agricultural materials, and are typed by the hydrolyzed corn starch-g-poly(acrylonitrile), H-SPAN [8]. Since then, starches from different resources as well as other polysaccharides, for example, cellulose, hydroxyethyl cellulose [8-13], agar, sodium alginate [3] and guar gum were graft copolymerized to achieve water absorbing polymers. Polyacrylonitrile (PAN), polyacryamide, and poly (acrylic acid) have been frequently grafted, mostly onto starch, using different, initiators especially the ceric-saccharide redox system Radical polymerizetion, however, has several disadvantages. The reproducebility of this method is poor, and there is little control over the grafting process, so the molecular weight distribution is polydisperse. In addition, the necessity for inert gases (e.g., argon) to prepare an oxygen-free atmosphere and the need for initiators, toxic and/or expensive monomers, and crosslinkers are other disadvantages of freeradical polymerization reactions. These problems have been reviewed in detail. For the first time, Fanta et al., with a new method, tried to synthesize of HSPAN superabsorbent hydrogel. They indicated by a solubility test that crosslinks were formed during graft copolymerizetion, by coupling of the two growing PAN radicals, and during saponification, by the attack of starch alkoxide ions on the nitrile groups as the initioation reaction of nitrile polymerization in the early stages of saponification. The nitrile groups of PAN were converted to a mixture of hydrophilic carboxamide and carboxylate groups during alkaline hydrolysis followed by in situ crosslinking of the grafted PAN chains. The initially formed oxygen-carbon bonds between the starch hydroxyls and nitrile groups of the PAN chains remained crosslinking sites. Then, Fanta and Doane [14] attempted to extend this idea to the preparation of superabsorbent hydrogels by the saponification of PAN in the presence of polyhydroxy polymers. Finally, Yamaguchi et al. [15] reported the preparation of superabsorbing polymers from mixtures of PAN and various saccharides or alcohols.  

In this investigation, we paid attention to the synthesis and investigation of a superabsorbent based on starch and PAA, PHEMA. The swelling behavior in distilled water in pH solutions was investigated as well.

A one step preparative method was used for synthesis of Starch-g-poly(sodiumacrylate-co-HEMA)hydrogel. Starch (1.33 g) was added to 35 mL of doubly distilled water in a three-neck reactor equipped with a mechanical stirrer (Heidolph RZR 2021, three blade propeller type).The reactor was immersed in a thermostated water bath preset at a desired temperature (70˚C). Then 0.10 g of APS as an initiator was added to starch solution and was allowed to stir for 10 min. After adding APS, variable amounts of AA and HEMA were added simultaneously to the starch solution. MBA solution (0.050 - 0.15 g in 5 ml H₂O) was added to the reaction mixture after the addition of monomers and the mixture was continuously stirred. After 60 min, the reaction product was allowed to cool to ambient temperature and neutralized to pH 8 by addition of 1 N sodium hydroxide solution. The hydrogel was poured to excess non solvent ethanol (200 mL) and remained for 3 h to dewater. Then ethanol was decanted and the product scissored to small pieces (diameter ~5 mm) [15-20]. Again, 100 mL fresh ethanol was added and the hydrogel was remained for 24 h. Finally, the filtered hydrogel is dried in oven at 60˚C for 10 h. After grinding, the powdered superabsorbent was stored away from moisture, heat and light. Infrared spectroscopy (Figure 1) and SEM (Figure 2) were carried out to confirm the chemical structure of the materials obtained. Crosslinking graft copolymerization of vinyl monomers (AA and HEMA) onto starch was shown in Scheme 1.

The superabsorbent hydrogel, starch-g—poly(NaAA-coHEMA), was synthesized through graft copolymerization mixture. The maximum water absorbency superabsorbent in solutions with pH = 8 was 95 g/g. Also the superabsorbent hydrogels exhibited high sensitivity to pH, so that, several swelling changes of the hydrogel or drug releaseing percent were observed in lieu of pH variations in a wide range (1-13). Furthermore, the reversible swellingdeswelling behavior in solutions with acidic and basic pH, makes the hydrogels as a suitable candidate for controlled releasing systems.

The authors thank the Research center of Islamic Azad University of Arak.