Among the chemicals used in this research are, 5 g of glycerol; 0.2 g of lead oxide (as catalyst); 3 ml of 5 M methanol; 28 g of phthalic anhydride; and 2 ml of xylene, etc. The apparatus and equipment used were 2000 ml electric heating mantle (220 volts); three-necked round bottom flask (500 ml); thermometer; stirrer (40 cm); glass beakers (500 ml); condenser (300 mm); thimble; Ohaus digital weighing balance (320 g); manual grinder; viscometer, Fourier Transform Infra-Red Spectrometer (FTIR), etc.

The research samples were palm oil, which is an edible vegetable oil derived from the mesocarp (reddish pulp) of palm fruits and mango seed oil, from seed kernels.

1) Isolation of palm oil from palm fruit mesocarp

The palm fruits were carefully detached using a sharp knife from the large fruit bunch. 2 kg of the palm fruits were washed and cooked until softened. This was pounded in a wooden mortar to separate the seed kernel (endocarp) from the mesocarp, which was later washed with cold water. This mixture was further heated to boiling, until, the oil start to separate. The oil phase was carefully decanted and heated further for an hour to remove the water content. The isolated oil was filtered and transferred into a clean container for further analysis.

2) Extraction of Mango seed oil

The mango fruits (Dasheri mango) locally known as German or Sweet mango fruits were picked around Chukwuemeka Odumegwu Ojukwu University environment. The succulent part were removed using sharp knife. The seed kernels were roasted in a drum roaster, the hull removed mechanically and the kernels crushed into small pieces of 0.01 mesh in a hammer mill. 2 kg of the crushed mango seeds were sundried for about 48 hrs to reduce the moisture content, ground into fine powder, dried again for 24 hrs and stored in a desiccators for further studies.

3) Isolation of mango seed oil

The seed oil was later extracted using soxhlet extraction technique at the temperature between 64˚C - 70˚C with n-hexane. The extracted oil was left open to remove excess solvent, before further analysis.

Percentage yield of the Oils

The percentage yield of the extracted mango seed oil and palm-oil was determined according Vogel, (2020) and calculated using the formular below:

$\text{Percentage Yield}\left(\%\right)=\frac{\text{weight of extracted oil}}{\text{weight of dry seed powder}}\times \frac{100}{1}$

Glass cuvette were filled with 20 ml of the two oil samples and placed in com-partment of the Gardner Scale. The oil samples’ colour were observed respectively, according to (0.5 ASTM Color ) standard.

Refractive index of the two vegetable oils were determined at 30˚C using Abbe’s refractometer. The machine was tuned on, the cell was rinsed with water, followed by acetone and allowed to dry by draining it. The oil was added into the cell and the reading taken respectively_.

This was carried out by titrating with phenolphthalein indicator. 7.00 g of the crude oil samples were weighed into two different 250 ml conical flask and 50 ml of 1 M alcohol added to each. Few drops of the indicator was added into 0.1 M sodium hydroxide solution, and agitated vigorously until a permanent pink colour appeared after few minutes.

Percentage free fatty acid was expressed as oleic acid, and was calculated as:

$\text{Acid Value}=\left(V_{eq}-b_{eq}\right)N\frac{56.1\text{g}/\text{mol}}{\text{Oil Weight}\left(\text{g}\right)}$

where: $V_{eq}$ is volume of titrand at equivalent point? $b_{eq}$ is titrant at equivalent point, while; 56.1 g/mol is molecular weight of NaOH.

NB: NaOH is the titrant and Crude oil is the titrand

$N=\frac{1000\times W_{KHP}}{204.23\frac{\text{g}}{\text{mol}}\times V_{eq}}$

where: $W_{KHP}$ is mass (g) of potassium hydrogen phthalate (KHP) in 50 ml of standard solution.

$V_{eq}$ is the volume of titrant (ml) consumed by 50 ml KHP standard solution at the equivalent point, and 204.23 g/mol. is the molecular weight of KHP.

5 g of the each oil sample was weighed into a 250 ml conical flask. 50 ml alcoholic KOH was pipetted into the flask and refluxed for 30 minutes. Allowed to cool and titrated with 0.5 M HCl using phenolphthalein indicator. Blank determination was carried out with same procedure and the value calculated thus:

$\text{Saponification Value}=\frac{28.05\left(B-S\right)}{\text{Weight of Oil}}$

where B = ml 0.5 M HCl required to titrate blank S = ml of 0.5 M HCI required to titrate sample.

Iodine value is used to determine the amount of unsaturated fats in the oil samples. Iodine is slowly absorbed by oil, but is rapidly taken up by Wijs solution, which consists of a solution of iodine monochloride (ICl) in glacial acetic acid and carbon tetrachloride, as in Scheme 1 below. The unsaturated bonds present took up the iodine to saturate the double bonds and the remaining unabsorbed iodine is then titrated by means of sodium thiosulphate (Na₂S₂O₄).

5 g of glycerol was added to 10 g of both mango seed oil (MSO) and palm oil (PO) in the three-necked flask in the presence of 0.2 g of lead oxide (catalyst) to form monoglyceride. The contents were heated simultaneously to 230˚C, and allowed for an hour for completion. Solubility of 1 ml of the heated samples in 3 ml methanol showed completion of alcoholysis reaction to form monoglyceride. The mixtures were allowed to cool to 140˚C, before esterification stage.

2) Esterification Stage

2.8 g of phthalic anhydride, as well as 2 ml of xylene, were added to the already formed monoglyceride sample mixtures. The mixture was heated to 230˚C for 4 hrs to remove water molecules. The acidity values of the two sample mixtures were determined at interval of 30 mins, until a stable pH drop was achieved for the two samples. The polymerization process was terminated by dipping the reaction system in cold water. Afterwards the already formed alkyd resins were allowed to cool. Some properties of alkyd resin were later determined and compared to the commercial grade.

1) Determination of viscosity

Viscosity of the alkyd resins were determined at 30˚C using a viscometer which was rinsed with organic solvent (acetone) and allowed to dry. A small quantity of the resins were added into the viscometer with micro pipette to fill the mark. At the release of each sample, a stop watch was put on and the time taken for the resin to flow from the point of origin to the calibrated mark was noted for the both alkyd resins. These times were recorded and multiplied by a constant factor (0.2483 m²/s).

2) Test on drying process

The alkyd resins from both palm oil and mango seed oil were dissolved in xylene mixed with drying agents (cobalt napththanate), applied on clear glass panels and allowed to dry at room temperature. The drying process was monitored in terms of time to set-to-touch, surface-dry and hard dry.

3) Determination of chemical resistance test (ASTM D 543 standard)

This was done at room temperature, according to [14] . The end of the glass panels of each alkyd resin films were coated with wax in order to prevent migration of film from the open ends. The panels were then dipped into water, 3 % (V/V), dil. HCl and 1 % (W/V) NaOH. The change in appearance at intervals of 30 mins were noted by recording the first noticeable effect or attack on the glass.

4) Impact strength

The impact strength of the dry alkyd resin films from both oils were determined using tubular impact tester according to ASTM D1709/ISO 7765

5) Solubility

The solubility of both modified palm oil and mango seed oil resin were tested in different solvents, by dropping 1 g of each resin into glass beaker containing 5 ml of each of these solvents; xylene, benzene, toluene, acetone, ethanol and methanol.

6) Adhesion Test

Adhesion of the dried films were tested by using cross hatch test according to ASTM 3359 method. A scope tape was adhered onto the film and peeled off quickly at 180˚ angle. The peeled off grid of areas on the tape were observed by a magnifier.

7) Pendulum hardness

This was done using pendulum hardness tester, to determine the viscoelastic behavior of the alkyd resins.

8) Fourier Transform Infra-Red Spectrometer (FTIR) Test

The bond formations and qualitative compositions of the raw oil and modified alkyd resin samples were carried out using FTIR. Standard interpretation according to the peaks of different absorption spectrum were taken to identify the bonds, organic and inorganic compositions of the alkyd resin samples

The results on the percentage yield and other physio-chemical properties of the two vegetable oils are stated in Table 1 . The results showed that the values of 6.37% ± 0.012% and 7.51% ± 0.001% for mango seed oil and palm oil respectively are within acceptable yields for most seed oils, according to [15] [16] . We assumed the low yield could be affected by the method of processing and the samples were also randomly selected from the environment. Saponification values were, 218.383 mg KOH/g, and 203.57 mg KOH, for mango seed oil and palm oil respectively and confirmed that they could undergo alkaline hydrolysis to form salt (soap) and glycerol. [17] , assured that oils with this percentage yield could be used industrially for production of toiletries and cosmetics. Some researches had proved that long chain fatty acids have low saponification values, because, of reduced number of carboxylic functional groups. [18] , emphasized that saponification values of breadfruit seed oil (161.30 mg KOH/g) and soya bean seed oil (191.50 mg KOH/g) also, compared well to our research sample oils. However, they concluded that oil with high saponification value are better for bio-resin production than those with low values.

Mango seed oil (MSO) gave iodine value of 50.91 while palm oil (PO) gave 53.01 as stated in Table 1 . Toshisada, et al. (2021) had suggested that, low iodine values are as a result of high content of saturated fatty acids, while, high iodine values are due to high content of unsaturated fatty acids. Also, some researchers had concluded that oils with iodine values greater than 130 are mostly drying-oil, those between “115 - 130” are semi-drying, while, those with values less than “115” are non-drying oil, [19] . [20] reported that high iodine value of seed oils means high degree of unsaturation and thus more C=C double bond in the molecule. [21] , suggested that double bonds are reactive sites for epoxidation reaction in bio-resin production. However, considering the abundant availability of palm oil, mango seed wastes, comparative low extraction cost, and low iodine values, our sample oils had been suggested to be very suitable for bio-resin production. Iodine value is also a good parameter to determine rancidity of an oil, and confirm the shelf life of the oil, therefore, our mango seed and palm oil have concluded to have a long shelf life.The specific density of mango seed oil and palm oil, were 1.09 g/ml and 0.888 g/ml at 25˚C respectively. They also observed the densities of different species of mango seed oil to be within 0.80 to 1.00 g/ml at, 25˚C, while, [3] confirmed palm oil to be 0.9633 g/ml at 25˚C. They suggested that different chemical compositions could be responsible for the differences in the density, although our oils fall within these range. However, the physio-chemical properties of our sample vegetable oils compared favorably well with those reported by [22] ), who stated the specific densities of palm oil to be, 0.931 g/ml, hemp seed oil (0.893/ml) and soya bean oil (0.908 g/ml). The acid values as stated in Table 1 , is 3.31 mgKOH/g for mango seed oil (MSO) and 2.86 mgKOH/g oil for palm oil (PO). Reports had shown acid values of hemp seed oil as, 2.15 mgKOH/g oil and soya bean oil as 1.05 mgKOH/g according to [22] . The high acid value of mango seed oil indicates, that, it has high free fatty acids and carboxylic acid group compared to palm oil, according to [23] [24] . They concluded that, the lower the acid value, the fewer the free fatty acids, and the low rate of rancidity phenomenon, [25] . We can confirm that the acid values of our research oil samples are low, and therefore, have long shelf life and reduced tendency to spoilage.

NB: % = percentage; g/ml = gram per millilitre; mgKOH/g = milligram potassium hydroxide per gram.

The physio-chemical qualities of our research sample alkyd resins as compared to the commercial grade sample are stated in Table 2 . The viscosity of the resin from mango seed oil showed the value of 448 cP, while, palm oil resin gave 384cP, as against 457cP of the commercial resin. Researches had revealed that, most bio-resins exhibited comparable higher viscosity value than synthetic resins, due to their high molecular weight compositions, [26] [27] . They concluded, that bio-resin with the viscosity within the rage of 100 cP to 1000 cP, is good for surface coatings, gluing, or bonding.

The Gardner scale colour test, showed 14, 17, and 11, for mango seed oil alkyd resin (MSOAR), palm oil alkyd resin (POAR) and commercial alkyd resin (CAR) respectively. The darker colour for POAR could be attributed to the high concentration of fatty acid in the molecule. MSOAR has faint yellow colour, which makes them suitable to reflecting colours, when used in as binders in paint formulations.

The chemical resistance for the resins were excellent in cold water, poor in base and fair in acid medium, showing that the resins has good coating when applied in surfaces that could be attacked if exposed to acidic or alkaline medium.

The Fourier Transform Infra-red spectroscopy (FTIR) test was used for identification of compositions of the alkyd resin samples. The absorption spectrum revealed the different functional groups and characteristic bonds between atoms in their various wavelengths within the molecules as shown in Figure 3(a) and Figure 3(b) , for MSOAR and POAR respectively.

The spectrum finger-prints profile of the raw mango seed oil sample revealed the

functional groups and bonds, as represented in Figure 3(a) Some of the characteristic peaks in the Infra-Red (IR) spectra of the mango seed oil alkyd resin (MSOAR) are represented in Figure 3(b) . The spectrum of strong peaks at 1698 cm⁻¹ shows formation of an ester bonds C=O, with stretching frequency to 1240 cm⁻¹, 1221 cm⁻¹, 1188 cm⁻¹, indicating the presence of a carbon single bonded to oxygen C-O. [28] This is in conformation to the findings of absorption wavelength of alkyd resin from Albizia lebbeck (Fry wood) seeds, according to [1] . They observed the peak within the range from 2930.30 to 2933.83 cm⁻¹ for the alkyd resin and concluded that the peak height of 1727 cm⁻¹ was due to the formation of carbon double bonded to oxygen C=O, and, stretch of unsaturated cyclic ester of monoglycerides. The stretching of 939 cm⁻¹ in aromatic carbon bond, C=C indicates the presence of phthalic group in the alkyd resin chain. A complete disappearance of the peak at 2920 per centimeter in the alkyd resin, and the appearance of the peak at 1240, 1221, and 1188 per centimeter indicates that a modification of oil had taken place.

1) FTIR of Raw Palm Oil

The FTIR spectra of raw palm oil is represented in Figure 3(c) . The peak at 3600 cm⁻¹ corresponds to the hydroxyl (O-H) of the unsaturated fatty acid in the palm oil molecule. The carboxyl group (C=O) is indicated at 1747 cm⁻¹. The straight chain of -CH- stretch in aliphatic compound is found at band 2854 cm⁻¹. Alkene group (CH=CH) is attributed to band at 3000 cm⁻¹.

2) FTIR of Raw Palm Oil Alkyd Resin

The Figure 3(d) represents the IR spectra of the prepared alkyd resin. The absorption spectra exhibited a characteristic straight chain at 1738.64 cm⁻¹ and aromatic (C=C) ring ester at 1730.09 cm⁻¹. The absorption band at 3008.99 cm⁻¹ is characteristic of alkene group and is in conformation to the findings of [29] . They discovered the peak for their three types of alkyd resins around 1740 cm⁻¹ and the stretching vibration for the carbonyl group around 1120 cm⁻¹ and 1250 cm⁻¹. The presence of O=C-O-C also exhibited characteristics of ester band at 1125.62 cm⁻¹. The ring ester band at 1730.09 cm⁻¹ confirms the esterification of palm oil monoglyceride with phthalic anhydride.

The results from some properties of the research alkyd resin displayed the suitability of the sample to be used as binding material in surface coatings, adhesives, varnishes, printing ink industries, etc. Alkyd resin from natural source materials had been proved to be eco-friendly, sustainable, low cost, than those from petrochemical sources, such as urea resins, epoxy resins, phenolic resins, urethanes resin, etc.

Our target in using under-utilized palm oil and mango seed seeds in the production of alkyd resin has necessitated to extract mango seed oil and palm oil, and synthesize them to alkyd resin.

The characterization of the sample alkyd resin and various results obtained had proved bio-resins suitable alternative as a binding resin for paints, papers, concretes, etc. and binding technology for beautiful architectural appearance and improved life style had increased the over-dependency on the use of synthetic resins from petrochemical compounds.

Limitation of the chemical equation in Figure 2 :