<?xml version="1.0" encoding="UTF-8"?><!DOCTYPE article  PUBLIC "-//NLM//DTD Journal Publishing DTD v3.0 20080202//EN" "http://dtd.nlm.nih.gov/publishing/3.0/journalpublishing3.dtd"><article xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink" dtd-version="3.0" xml:lang="en" article-type="research article"><front><journal-meta><journal-id journal-id-type="publisher-id">MSA</journal-id><journal-title-group><journal-title>Materials Sciences and Applications</journal-title></journal-title-group><issn pub-type="epub">2153-117X</issn><publisher><publisher-name>Scientific Research Publishing</publisher-name></publisher></journal-meta><article-meta><article-id pub-id-type="doi">10.4236/msa.2022.1311035</article-id><article-id pub-id-type="publisher-id">MSA-121478</article-id><article-categories><subj-group subj-group-type="heading"><subject>Articles</subject></subj-group><subj-group subj-group-type="Discipline-v2"><subject>Chemistry&amp;Materials Science</subject></subj-group></article-categories><title-group><article-title>
 
 
  Study of Physical, Chemical and Thermo-Mechanical Properties of Talc Filled Polyester Resin Composite Using Styrene Monomer
 
</article-title></title-group><contrib-group><contrib contrib-type="author" xlink:type="simple"><name name-style="western"><surname>Sharmina</surname><given-names>Yeasmin</given-names></name><xref ref-type="aff" rid="aff1"><sup>1</sup></xref></contrib><contrib contrib-type="author" xlink:type="simple"><name name-style="western"><surname>Suraya</surname><given-names>Sabrin Soshi</given-names></name><xref ref-type="aff" rid="aff2"><sup>2</sup></xref></contrib><contrib contrib-type="author" xlink:type="simple"><name name-style="western"><surname>Md.</surname><given-names>Abdul Gafur</given-names></name><xref ref-type="aff" rid="aff3"><sup>3</sup></xref><xref ref-type="corresp" rid="cor1"><sup>*</sup></xref></contrib><contrib contrib-type="author" xlink:type="simple"><name name-style="western"><surname>Mansurul</surname><given-names>Murad</given-names></name><xref ref-type="aff" rid="aff4"><sup>4</sup></xref></contrib><contrib contrib-type="author" xlink:type="simple"><name name-style="western"><surname>Shams</surname><given-names>Tania Afroza Islam</given-names></name><xref ref-type="aff" rid="aff1"><sup>1</sup></xref></contrib></contrib-group><aff id="aff4"><addr-line>Renata Limited, Dhaka, Bangladesh</addr-line></aff><aff id="aff3"><addr-line>Pilot Plant and Process Development Centre, Bangladesh Council of Scientific and Industrial Research (BCSIR), Dhaka, Bamngladesh</addr-line></aff><aff id="aff1"><addr-line>Department of Applied Chemistry &amp;amp; Chemical Engineering, University of Dhaka, Dhaka, Bangladesh</addr-line></aff><aff id="aff2"><addr-line>Department of Mechanical and Production Engineering, Ahsanullah University of Science and Technology, Dhaka, Bangladesh</addr-line></aff><pub-date pub-type="epub"><day>25</day><month>11</month><year>2022</year></pub-date><volume>13</volume><issue>11</issue><fpage>569</fpage><lpage>585</lpage><history><date date-type="received"><day>3,</day>	<month>October</month>	<year>2022</year></date><date date-type="rev-recd"><day>25,</day>	<month>November</month>	<year>2022</year>	</date><date date-type="accepted"><day>28,</day>	<month>November</month>	<year>2022</year></date></history><permissions><copyright-statement>&#169; Copyright  2014 by authors and Scientific Research Publishing Inc. </copyright-statement><copyright-year>2014</copyright-year><license><license-p>This work is licensed under the Creative Commons Attribution International License (CC BY). http://creativecommons.org/licenses/by/4.0/</license-p></license></permissions><abstract><p>
 
 
  Fiber Reinforced Thermoplastic (FRTP) composites are emerging as potential materials in many engineering fields. In this research, the compression-molding process was used as the fabrication technique for producing talc-filled reinforced polyester composite. The weight percentage of these composites was varied, like 30 wt%, 40 wt%, 45 wt%, and 50 wt% talc, respectively. Besides, different percentages of styrene monomer, such as 0 wt%, 20 wt%, and 30 wt%, were also used in this study. Different types of physical, chemical, mechanical, and thermal properties were investigated. The water absorption percentage is increased for composites having a higher percentage of talc filler, while the elasticity of the composites shows a decreasing nature with the increase of talc content. Compressive strength is increased with higher talc content. After a certain limit, with the increase of talc content, it decreases and remains more or less constant. The flexural properties (flexural strength, tangent modulus, and flexural strain) of polyester-talc composites are higher initially, and as the percentage of talc increases, the flexural properties decrease or remain constant. The rate of water absorption is very low with the increase in soaking time. The thermal analysis of polyester-talc composites shows that the thermal stability of the composites is better than that of polyester.
 
</p></abstract><kwd-group><kwd>Talc</kwd><kwd> Composite Material</kwd><kwd> Polyester-Resin</kwd><kwd> Thermal Conductivity</kwd><kwd> TGA</kwd><kwd> DTA</kwd></kwd-group></article-meta></front><body><sec id="s1"><title>1. Introduction</title><p>Minerals are being used as fillers in plastic compounds to reduce material costs by replacing a portion of the polymer with less expensive material. However, nowadays many functional fillers or minerals modifiers are required to modify processing characteristics or finished part properties. Many of them are also being used to reduce the level of more expensive additives such as pigments, flame-retardants and impact modifiers [<xref ref-type="bibr" rid="scirp.121478-ref1">1</xref>]. A wide variety of minerals are employed as plastics additives, including graphite, calcium carbonate (CaCO<sub>3</sub>), talc, alumina hydrate, silica, mica, kaolin, diatomite, dolomite and wollastonite [<xref ref-type="bibr" rid="scirp.121478-ref2">2</xref>]. Since 1980, demand for these additives has increased on average by 7% a year in volume terms, compared to an annual increase in the US demand for plastics of only 4% - 5%. In 1980, 9% of all plastic compounds were incorporated with minerals but this percentage had grown to 15% by 2002 [<xref ref-type="bibr" rid="scirp.121478-ref3">3</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref4">4</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref5">5</xref>].</p><p>The use of composites in all products—from sporting goods to bridges to satellites is increasing also outside of the profession, though, many people would be hard-pressed to identify a composite, and this article presents a simple definition of composite materials. Composite materials consist of two or more materials combined in such a way that the individual materials are easily distinguishable. A common example of a composite is concrete which consists of a binder and reinforcement [<xref ref-type="bibr" rid="scirp.121478-ref4">4</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref5">5</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref6">6</xref>]. Adding reinforcement transforms concrete into a three-phase composite. The individual materials that make up composites are called constituents; most composites have two constituent materials: a binder or matrix, and a dispersed phase for reinforcement. The reinforcement is usually much stronger and stiffer than the matrix [<xref ref-type="bibr" rid="scirp.121478-ref7">7</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref8">8</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref9">9</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref10">10</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref11">11</xref>], and gives the composite a good property. The matrix holds the reinforcements in an orderly pattern, because the reinforcements are usually discontinuous, the matrix also helps to transfer load among the reinforcements. Basically, reinforcements come in three forms: particulate, discontinuous fiber, and continuous fiber [<xref ref-type="bibr" rid="scirp.121478-ref12">12</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref13">13</xref>]. Gravel, micro balloons and resin powder are examples of particulate reinforcements.</p><p>A polymer is a versatile material [<xref ref-type="bibr" rid="scirp.121478-ref14">14</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref15">15</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref16">16</xref>] which is the most promising and comprehensive field in the present era of science. The development of polymer is a continuous process for achieving it in a specific application under certain environmental condition. The polymer materials that are biodegradable are now enjoying considerable popularity, especially from the standpoint of environmental protection [<xref ref-type="bibr" rid="scirp.121478-ref17">17</xref>].</p><p>Many of our modern technologies require materials with unusual combinations of properties that cannot be met by conventional metal alloys, ceramics, and polymeric materials. This is especially true for materials that are needed for aerospace, underwater, and transportation applications. For example aircraft engineers are increasingly searching for structural materials that have low densities, are strong, and abrasion and impact resistant, and are not easily corroded. Frequently, strong materials are relatively dense; also increasing the strength or stiffness generally results in a decrease in impact strength [<xref ref-type="bibr" rid="scirp.121478-ref18">18</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref19">19</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref20">20</xref>]. Composite materials [<xref ref-type="bibr" rid="scirp.121478-ref21">21</xref>] represent nothing but a giant step in the ever-constant endeavor of optimization in materials. Exactingly speaking, the idea of the composite is not a new or recent one; nature is full of examples wherein the idea of composite is worn [<xref ref-type="bibr" rid="scirp.121478-ref22">22</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref23">23</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref24">24</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref25">25</xref>].<sup> </sup></p><p>Besides naturally occurring composites, there are many other engineering materials that are composites in a very natural way. Among the modern structural materials, the history of fiber-reinforced composites is only three decades old. However, in this period of time, there are an incredible progression in the science and technology of the new classes of materials. The low density, high strength, high stiffness-to-weight ratio, excellent durability, and design flexibility of fiber reinforced polymers [<xref ref-type="bibr" rid="scirp.121478-ref26">26</xref>] are primary reasons for their use in many structural components in the aircraft, automotive, marine and other industries.</p><p>Composite technology utilizes the high stiffness and strength of filamentary material one common example includes straw-reinforced clay bricks from biblical times and today’s steel (fiber) braced radical tier [<xref ref-type="bibr" rid="scirp.121478-ref27">27</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref28">28</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref29">29</xref>]. The advantages of these materials lie in the high specific stiffness, which can be achieved, for example, carbon fibers by molecular and crystal orientation along their fiber length, such that the chemical carry a higher proportion of the load. Since the population of Griffith flaws controls the strength of a material [<xref ref-type="bibr" rid="scirp.121478-ref30">30</xref>], it follows that a fine filament will have a lower density of critical (strength reducing) flaws.</p><p>Polyester resin is an attractive candidate for many engineering applications because of its excellent chemical resistance, acceptable range of tensile strength and modulus, good impact strength and process ability, and low price. It is a versatile polymer that has many qualities like excellent chemical resistance, good mechanical properties, and low cost which making it the polymer of choice for various applications. There are many ways in which the mechanical properties of polyester resin can be modified to suit a wide variety of end-use applications. Various reinforcements, such as talc, graphite, and mica, are typical ingredients that are added to polyester to attain cost effective mechanical properties [<xref ref-type="bibr" rid="scirp.121478-ref31">31</xref>]. Fibrous materials tend to increase both mechanical and thermal properties, such as tensile and flexural strength, flexural modulus, heat deflection temperature, creep resistance, and even impact strength. Fillers, such as talc, are often used as extenders, thus reducing the final material cost [<xref ref-type="bibr" rid="scirp.121478-ref32">32</xref>].</p><p>Talc is water repellant and very soft in fact it is the softest material according to Mohs. Hardness scale, it can resist temperature up to 900˚C and unaffected by chemicals and will not harm living tissue [<xref ref-type="bibr" rid="scirp.121478-ref33">33</xref>]. Talc can be utilized as a medium filler of average whiteness in thermosetting as well as thermoplastic resins where improvements in electrical insulation, heat, and moisture resistance, chemical inertness and good machine ability are needed. Talc has low absorption rate and because of its plate-like structure, certain grades can improve flexural properties of moldings [<xref ref-type="bibr" rid="scirp.121478-ref34">34</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref35">35</xref>]. In this study, the effect of styrene monomer on chemical, thermo-mechanical, physical, and water absorption behavior of talc-polyester resin composites is studied.</p></sec><sec id="s2"><title>2. Materials and Methods</title><sec id="s2_1"><title>2.1. Raw Materials</title><p>The raw materials used for the preparation of the sample are talc, unsaturated polyester, methyl ethyl ketone peroxide (MEEK), and styrene monomer. Talc is supplied by Tekcast Industries, Inc. USA. Unsaturated polyester resin and styrene monomer were collected from the local market of Bangladesh.</p></sec><sec id="s2_2"><title>2.2. Machines Used for Fabrication and Testing of Composites</title><p>Several pieces of equipment were used in the fabrication of polymeric matrix composites. The main equipment and accessories were simple balance, press, molds, etc. A number of machines and equipment were used in the testing of polymeric matrix composites. The main equipment included universal testing machine, thermal analyzer, etc.</p><p>Molds:In this research work, mold which has the upper halve and lower halve but no cavity in any half of the mold were used. These two halves are completely plane with smooth surface platens which also act as a heater and cooler simultaneously. A ring with inside diameter of 146 mm and outside diameter of 158 mm, and two disc or plates of 7.5 mm thickness on each side were used as a die.</p><p>Hydraulic hot press machine:A Hot press (PW40, P/W/weber, Germany), was used for compression molding. In compression molding, the polymeric materials and the fiber are subjected to heat and pressure in a single stroke. This is accomplished by using a hydraulic press with heated platens, molding temperature and pressure can be as high as 300˚C and 450 KN, respectively.</p><p>Universal testing machine: Various mechanical properties such as tensile strength, elongation at break, tensile modulus, bending strength and bending modulus, etc. can be determined by using universal testing machine (H10KS, Hounsefield, UK).</p><p>TGA/DT Analyzer:The thermal properties (TGA and DTA) of the sample were accessed by thermal analyzer, TGDTA (EXSTAR 6300, Seiko Instrument Inc., Japan). A computer-controlled (Seiko Instrument Inc., Japan) machine was used in the present research at a heating rate of 20˚K/min and gas flow of 100 mL/min.</p></sec><sec id="s2_3"><title>2.3. Preparation of the Composite</title><p>Talc was dried at 100˚C for 24 hours in a preheated oven. Different percentage of talc and polyester resin with styrene monomer was taken to prepare composite. Talc was taken from 30 to 50 wt% and unsaturated polyester resin was taken according to <xref ref-type="table" rid="table1">Table 1</xref>. The amount of styrene content was kept constant. The following table shows different percentages of samples.</p><p>A bowl was taken to mix up the raw materials of the composite. Definite amount of various percentages of talc, polyester resin and styrene monomer was weighed in the bowl and mixed very carefully with a stirrer for about half a hour. Ethyl Methyl Ketone Peroxide (MEKP) was used as initiator, as an amount of 1.5 wt% of polyester resin and styrene weight. The mixer was then poured into the mold and kept it 4 - 5 hours for setting. After setting up the composite is released from the mold by applying low load. Millot paper was used as separator up the sides of the composite. Another set of composite was prepared taking various percentage of styrene monomer as shown in <xref ref-type="table" rid="table2">Table 2</xref>.</p></sec><sec id="s2_4"><title>2.4. Properties of the Composites</title><sec id="s2_4_1"><title>2.4.1. Water Absorption</title><p>Water absorption specimen was prepared according to ASTM designation: C 67 - 91. Specimen dimension 25 mm &#215; 7 mm &#215; 8 mm accordingly. A protective gel coat (araldite) was applied on the cut sides to prevent penetration of water from cut sides. The water absorption was calculated by the following equation-</p><p>% Wa = 100 ( W f − W i ) / W i</p><p>W<sub>f</sub> = final weight after water absorption.</p><p>W<sub>i</sub> = initial weight before immersion.</p></sec><sec id="s2_4_2"><title>2.4.2. Compressive Properties</title><p>Compressive strength: Compression sample was prepared according to ASTM D638. Then the sample was subjected to compression testing. The sample was 10 &#215; 10 &#215; (6 – 8) mm. The compression strength and strain are defined as:</p><p>σ e = F A 0</p><p>A<sub>0</sub> = Original cross sectional area [m<sup>2</sup>].</p><p>ϵ e = l − l 0 l 0</p><p>where, l = specimen length [m] and l<sub>0</sub> = original specimen length [m].</p></sec><sec id="s2_4_3"><title>2.4.3. Flexural Properties</title><p>Flexural strength: Flexural specimen was prepared according to ASTM D790M,</p><table-wrap id="table1" ><label><xref ref-type="table" rid="table1">Table 1</xref></label><caption><title> Talc-Polyester resin composite with constant wt% of styrene monomer</title></caption><table><tbody><thead><tr><th align="center" valign="middle" >Talc %</th><th align="center" valign="middle" >Polyester resin (with 20% styrene monomer) %</th></tr></thead><tr><td align="center" valign="middle" >50</td><td align="center" valign="middle" >50</td></tr><tr><td align="center" valign="middle" >40</td><td align="center" valign="middle" >60</td></tr><tr><td align="center" valign="middle" >45</td><td align="center" valign="middle" >55</td></tr><tr><td align="center" valign="middle" >30</td><td align="center" valign="middle" >70</td></tr></tbody></table></table-wrap><table-wrap id="table2" ><label><xref ref-type="table" rid="table2">Table 2</xref></label><caption><title> Talc-polyester resin composite with variable percentage of styrene with polyester</title></caption><table><tbody><thead><tr><th align="center" valign="middle" >Talc %</th><th align="center" valign="middle" >50% polyester resin containing styrene, wt%</th></tr></thead><tr><td align="center" valign="middle" >50</td><td align="center" valign="middle" >20</td></tr><tr><td align="center" valign="middle" >50</td><td align="center" valign="middle" >30</td></tr><tr><td align="center" valign="middle" >50</td><td align="center" valign="middle" >0</td></tr></tbody></table></table-wrap><p>3 point loading. The specimen dimension was 125 &#215; 10 &#215; (6 – 8) mm and support span was 96 mm. The test speed was taken as 2.6 mm/min.</p><p>The strength and strain is calculated by means of the following equations</p><p>S = 3 P L / 2 b d 2</p><p>ε f = 6 b d / L 2</p><p>where, S = Stress in the outer fibers at mid-span, MPa, P = Load at a given point on the load – deflection curve, N,L = Support span, mm, b = Width of specimen tested, mm, D = Depth of tested specimen, mm.<sup> </sup></p></sec></sec></sec><sec id="s3"><title>3. Results and Discussion</title><p>Various properties such as physical and mechanical properties of polyester-talc composite using styrene monomer were observed. The results of these properties are discussed below.</p><sec id="s3_1"><title>3.1. Physical Properties</title><p>The effect of soaking time on water absorption of polyester-talc composites prepared with different wt% (30 wt%, 40 wt%, 45 wt%, and 50 wt%) of talc is shown in <xref ref-type="fig" rid="fig1">Figure 1</xref>. It reveals that the water absorption depends on talc addition and immersion time. It can be seen that the percentage of water absorption for all percent of talc content increases with time as it is a diffusion phenomenon. The rate of water absorption is high initially; after that, it decreases with the increase of soaking time. The hydrophilic nature of talc fiber and the hydrophobic nature of polyester control the absorption of composites. For this reason, there is a very low amount of water intake in the composites.</p><p>The water absorption of these composites was measured by soaking the composites in water contained in a static bath for different period of time.</p><p><xref ref-type="fig" rid="fig2">Figure 2</xref> shows that water absorption is decreased with the addition of styrene</p><p>percentage. The figure shows that the percentage of water intake increases slowly initially with the increase of time due to slow absorption of polystyrene.</p></sec><sec id="s3_2"><title>3.2. Mechanical Properties</title><p>The performance and durability of composites are dependent on the mechanical properties. Mechanical properties of the composites were measured in terms of compressive strength (CS), E-modulus, flexural strength, flexural strain, and tangent modulus.</p><p>Compressive strength for polyester-talc composites is shown in <xref ref-type="fig" rid="fig3">Figure 3</xref>. It can be seen that the maximum value of the compressive strength of the polyester-talc composite was found at a percentage of 40 wt% talc, but for a further increase in the percentage of talc, the compressive strength decreases. The compressive strength of the composite was very well; it was higher than brick [<xref ref-type="bibr" rid="scirp.121478-ref36">36</xref>].</p><p>The changes in compressive strength of the polyester-talc composites with the addition of different percentages of styrene monomer are shown in <xref ref-type="fig" rid="fig4">Figure 4</xref>. The CS increases with the increase of styrene addition and reaches maximum, then</p><p>decreases. The maximum compressive strength was found at the percentage of 20 wt% styrene monomer content [<xref ref-type="bibr" rid="scirp.121478-ref36">36</xref>].</p><p><xref ref-type="fig" rid="fig5">Figure 5</xref> shows E-modulus of talc reinforced composites of different wt% of talc. It reveals that the E-modulus increases with increase in addition of talc from 30 wt% to more. It shows the maximum value at 40 wt% talc content, for more addition of talc like 45 wt%, 50 wt% E-modulus decreases. The E-modulus is a measure of stiffness of a material. Thus, the stiffness of polyester-talc composites increases with increase of talc addition initially and then decreases with increases percentage [<xref ref-type="bibr" rid="scirp.121478-ref37">37</xref>].</p><p>The following figure shows the variation of E-modulus with change of percentage of talc:</p><p><xref ref-type="fig" rid="fig6">Figure 6</xref> shows the effect of E-modulus of talc reinforced composites of different percentage of styrene. It reveals that E-modulus increases with increase of styrene percentage, reaches maximum and then remains more or less constant [<xref ref-type="bibr" rid="scirp.121478-ref37">37</xref>].</p><p>Flexural strength for polyester-talc composites is shown in <xref ref-type="fig" rid="fig7">Figure 7</xref>. It shows flexural strength decreases with the increase of talc addition [<xref ref-type="bibr" rid="scirp.121478-ref37">37</xref>].</p><p>The change of flexural strength due to the addition of different percentage of styrene for the polyester-talc composites is shown in <xref ref-type="fig" rid="fig8">Figure 8</xref>. From the figure it</p><p>is shown that the highest value of flexural strength is obtained at 20 wt% Styrene, increasing from this value the flexural property is decreased [<xref ref-type="bibr" rid="scirp.121478-ref37">37</xref>] [<xref ref-type="bibr" rid="scirp.121478-ref38">38</xref>].</p><p><xref ref-type="fig" rid="fig9">Figure 9</xref> shows flexural E-modulus of talc reinforced composites of different wt% of talc. It reveals that the E-modulus increase with increase of talc addition. The E-modulus is a measure of stiffness of a material. Thus, the stiffness of polyester-talc composites increases with increase of talc addition initially and then decreases [<xref ref-type="bibr" rid="scirp.121478-ref39">39</xref>].</p><p><xref ref-type="fig" rid="fig9">Figure 9</xref> shows that E-modulus of talc reinforced composites of different percentage of talc. It reveals that E-modulus increases with increase of conc. of talc due to increase E-modulus of the talc and the polyester are well distributed. After 45 wt% of styrene monomer the value of E-modulus decreases [<xref ref-type="bibr" rid="scirp.121478-ref39">39</xref>].</p><p><xref ref-type="fig" rid="fig1">Figure 1</xref>0 shows the effect of the styrene addition on flexural modulus of composites. It reveals that modulus decreases with the increase styrene addition. It decreases to minimum value, then increases [<xref ref-type="bibr" rid="scirp.121478-ref40">40</xref>].</p></sec><sec id="s3_3"><title>3.3. Thermal Analysis</title><p><xref ref-type="fig" rid="fig1">Figure 1</xref>1 shows the TG curves of talc, polyester and composite. The top one is for talc, bottom one is for polyester and middle one is for composite. The figure reveals that the TG of composites is the average of the two curves of talc and polyester. The figure shows that major degradation occurs for both the polyester and talc at a single stage, but it occurs at two for the composite. The initial stage/1<sup>st</sup> stage is related to talc, whereas the second stage is related to polyester [<xref ref-type="bibr" rid="scirp.121478-ref37">37</xref>].</p><p><xref ref-type="fig" rid="fig1">Figure 1</xref>2 and <xref ref-type="fig" rid="fig1">Figure 1</xref>3 show the DTG and DTA curves for talc, polyester and composite. In <xref ref-type="fig" rid="fig1">Figure 1</xref>2, the above black curve is for polyester, the bottom one is for talc and the middle one is for composite. As usual, the value of DTG of composite is in between the raw materials [<xref ref-type="bibr" rid="scirp.121478-ref40">40</xref>].</p><p>From <xref ref-type="fig" rid="fig1">Figure 1</xref>4 and <xref ref-type="fig" rid="fig1">Figure 1</xref>5, the graph shows that TG/DTA value decreases if the percentage of talc decreases. For 30 wt% talc addition TG/DTA of the composite is lower than for 50 wt% talc addition.</p><p><xref ref-type="fig" rid="fig1">Figure 1</xref>6 and <xref ref-type="fig" rid="fig1">Figure 1</xref>7 of the following shows the variation of TG/DTA of the composite due to the addition of 30 wt% styrene monomer and without adding styrene monomer. Addition of styrene shows degradation of the TG value. The highest slope is at 412.7˚C which is for 30 wt% styrene monomer addition and the highest slope for the sample without styrene is at 406.7˚C.</p></sec><sec id="s3_4"><title>3.4. Chemical Attack</title><p>The composite was subjected to 97% sulfuric acid. At the lower concentration, the composite was merely attacked by the acid but when the composite was kept in concentrated sulfuric acid for about several hours it was badly attacked by the acid. The raw material of the composite such as talc, polyester resin and styrene monomer reacts with concentrated sulfuric acid and the composite becomes soft and also the color of the composite degraded.</p></sec></sec><sec id="s4"><title>4. Conclusions</title><p>The results of the present study revealed that composites with good strength could be successfully developed using talc as the reinforcing agent. According to</p><p>the present work on the development of the mineral filler reinforced polymer composite the following conclusions can be made.</p><p>Varying amount of matrix and talc filler is the most important parameter of this fabricated process. A percentage of talc (30 wt%, 40 wt%, 45 wt% and 50 wt%) and styrene monomer (0 wt%, 20 wt% and 30 wt%) have been taken for fabrication of the composite. The water absorption increases with increase in soaking time because the mineral fillers obey this behavior and the absorption of water was highest at 45 wt% talc then decreased.</p><p>Compressive strength of the composite was found very high and it was increased for addition of talc percentage from 30 wt% to 40 wt%, furthermore increase in the percentage of talc caused decrease in compressive strength. Flexural strength of the composite found to be highest at 30 wt% talc content, which decreased for 40 wt% talc addition, and it is again increased at 45 wt% talc content and at 50 wt% talc decreased again. At 20 wt% of styrene monomer, the compressive strength and flexural strength are highest and the values decrease with increasing the percentage of styrene monomer. It is found that TG, DTG and DTA curves of the composites were the average of the filler and the polyester. The degradation of composites was occurring in only one stage due to the polymer. The thermal stability of polyester-talc filler composites was higher than polyester. Chemical analysis showed that the composite was attacked by concentrated acid solution. The composite corroded in acid but did not dissolve in it. A good morphology presented by the studied samples was observed.</p></sec><sec id="s5"><title>Conflicts of Interest</title><p>The authors declare no conflicts of interest regarding the publication of this paper.</p></sec><sec id="s6"><title>Cite this paper</title><p>Yeasmin, S., Soshi, S.S., Gafur, M.A., Murad, M. and Islam, S.T.A. (2022) Study of Physical, Chemical and Thermo-Mechanical Properties of Talc Filled Polyester Resin Composite Using Styrene Monomer. Materials Sciences and Applications, 13, 569-585. https://doi.org/10.4236/msa.2022.1311035</p></sec></body><back><ref-list><title>References</title><ref id="scirp.121478-ref1"><label>1</label><mixed-citation publication-type="other" xlink:type="simple">Roiter, Y. and Minko, S. (2005) AFM Single Molecule Experiments at the Solid-Liquid Interface: In Situ Conformation of Adsorbed Flexible Polyelectrolyte Chains. Journal of the American Chemical Society, 127, 15688-15689.</mixed-citation></ref><ref id="scirp.121478-ref2"><label>2</label><mixed-citation publication-type="other" xlink:type="simple">McCrum, N.G., Buckley, C.P. and Bucknall, C.B. (1997) Principles of Polymer Engineering. Oxford University Press, Oxford, 1.</mixed-citation></ref><ref id="scirp.121478-ref3"><label>3</label><mixed-citation publication-type="other" xlink:type="simple">Sperling, L.H. (2005) Introduction to Physical Polymer Science. Wiley, Hoboken, 10.</mixed-citation></ref><ref id="scirp.121478-ref4"><label>4</label><mixed-citation publication-type="other" xlink:type="simple">Baeurle, S.A. (2009) Multiscale Modeling of Polymer Materials Using Field-Theoretic Methodologies: A Survey about Recent Developments. Journal of Mathematical Chemistry, 46, 363-342. https://doi.org/10.1007/s10910-008-9467-3</mixed-citation></ref><ref id="scirp.121478-ref5"><label>5</label><mixed-citation publication-type="other" xlink:type="simple">IUPAC, Kratochvíl, P., Stepto, R.F.T. and Suter, U.W. (1996) Glossary of Basic Terms in Polymer Science. Pure and Applied Chemistry, 68, 2287-2311. https://doi.org/10.1351/pac199668122287</mixed-citation></ref><ref id="scirp.121478-ref6"><label>6</label><mixed-citation publication-type="other" xlink:type="simple">De Gennes, P.G. (1979) Scaling Concepts in Polymer Physics. Cornell University Press, Ithaca.</mixed-citation></ref><ref id="scirp.121478-ref7"><label>7</label><mixed-citation publication-type="other" xlink:type="simple">Allcock, H.R., Lampe, F.W. and Mark, J.E. (2003) Contemporary Polymer Chemistry. 3rd Edition, Pearson Education, London, 546.</mixed-citation></ref><ref id="scirp.121478-ref8"><label>8</label><mixed-citation publication-type="other" xlink:type="simple">Jones, D. (1996) Engineering Materials. 2nd Edition, Butterworth-Heinemann, Oxford, 191-195.</mixed-citation></ref><ref id="scirp.121478-ref9"><label>9</label><mixed-citation publication-type="other" xlink:type="simple">Meyers, M.A. and Chawla, K.K. (1999) Composite Material-Science and Engineering. Cambridge University Press, Cambridge, 41.</mixed-citation></ref><ref id="scirp.121478-ref10"><label>10</label><mixed-citation publication-type="other" xlink:type="simple">Brandrup, J., Immergut, E.H. and Grulke, E.A. (1999) Polymer Handbook. 4th Edition, Wiley-Interscience, Hoboken.</mixed-citation></ref><ref id="scirp.121478-ref11"><label>11</label><mixed-citation publication-type="other" xlink:type="simple">IUPAC (1976) Nomenclature of Regular Single-Strand Organic Polymers. Pure and Applied Chemistry, 48, 373-385. https://doi.org/10.1351/pac197648030373</mixed-citation></ref><ref id="scirp.121478-ref12"><label>12</label><mixed-citation publication-type="other" xlink:type="simple">U.S. Patent 6,052,184 and Other Patents Pending.</mixed-citation></ref><ref id="scirp.121478-ref13"><label>13</label><mixed-citation publication-type="other" xlink:type="simple">Florenzano, F.H., Strelitzki, R. and Reed, W.F. (1998) Absolute, Online Monitoring of Polymerization Reactions. Macromolecules, 31, 7226-7238. https://doi.org/10.1021/ma980876e</mixed-citation></ref><ref id="scirp.121478-ref14"><label>14</label><mixed-citation publication-type="other" xlink:type="simple">Alb, A.M., Drenski, M.F. and Reed, W.F. (2008) Automatic Continuous Online Monitoring of Polymerization Reactions (ACOMP). Polymer International, 57, 390-396.</mixed-citation></ref><ref id="scirp.121478-ref15"><label>15</label><mixed-citation publication-type="other" xlink:type="simple">National Toxicology, Program (1993) NTP Toxicology and Carcinogenesis Studies of Talc (Non-Asbestiform) in Rats and Mice (Inhalation Studies). National Toxicology Program Technical Report Series 421, 1-287.</mixed-citation></ref><ref id="scirp.121478-ref16"><label>16</label><mixed-citation publication-type="other" xlink:type="simple">NIOSH Worker Notification Program. Health Effects of Mining and Milling Talc.</mixed-citation></ref><ref id="scirp.121478-ref17"><label>17</label><mixed-citation publication-type="other" xlink:type="simple">Harlow, B.L., Cramer, D.W., Bell, D.A. and Welch, W.R. (1992) Perineal Exposure to Talc and Ovarian Cancer Risk. Obstetrics and Gynecology, 80, 19-26.</mixed-citation></ref><ref id="scirp.121478-ref18"><label>18</label><mixed-citation publication-type="other" xlink:type="simple">Henderson, W.J., Joslin, C.A., Turnbull, A.C. and Griffiths, K. (1971) Talc and Carcinoma of the Ovary and Cervix. The Journal of Obstetrics and Gynaecology of the British Commonwealth, 78, 266-272. https://doi.org/10.1111/j.1471-0528.1971.tb00267.x</mixed-citation></ref><ref id="scirp.121478-ref19"><label>19</label><mixed-citation publication-type="other" xlink:type="simple">U.S. Food and Drug Administration (2009) Code of Federal Regulations.</mixed-citation></ref><ref id="scirp.121478-ref20"><label>20</label><mixed-citation publication-type="book" xlink:type="simple">James, D.H. and Castor, W.M. (2005) Styrene. In: Ullmann, F., et al., Eds., Ullmann’s Encyclopedia of Industrial Chemistry, Wiley-VCH, Weinheim, 684-688.</mixed-citation></ref><ref id="scirp.121478-ref21"><label>21</label><mixed-citation publication-type="other" xlink:type="simple">Harris, G. (2011, June 10) Government Says 2 Common Materials Pose Risk of Cancer. New York Times. http://www.nytimes.com/2011/06/11/health/11cancer.html</mixed-citation></ref><ref id="scirp.121478-ref22"><label>22</label><mixed-citation publication-type="other" xlink:type="simple">National Toxicology Program (2011) 12th Report on Carcinogens. National Toxicology Program.</mixed-citation></ref><ref id="scirp.121478-ref23"><label>23</label><mixed-citation publication-type="other" xlink:type="simple">Abbott, T.W. and Johnson, J.R. (1941) Phenylethylene (Styrene). Organic Syntheses, 14-16.</mixed-citation></ref><ref id="scirp.121478-ref24"><label>24</label><mixed-citation publication-type="other" xlink:type="simple">Fittig, R. and Binder, F. (2020) Ueber die Additionsproducte der Zimmtssaure. In Untersuchungenüber die ungesattigtenSauren. I.</mixed-citation></ref><ref id="scirp.121478-ref25"><label>25</label><mixed-citation publication-type="other" xlink:type="simple">Fittig, R., Petri, C. and Liebigs, J. (1879) Weitere Beitragezur Kenntnifs der Fumarsaure und Maleinsaure. Annalen der Chemie, 195, 56-179. https://doi.org/10.1002/jlac.18791950103</mixed-citation></ref><ref id="scirp.121478-ref26"><label>26</label><mixed-citation publication-type="other" xlink:type="simple">Yashima, T., Sato, K., Hayasaka, T. and Hara, N. (1972) Alkylation on Synthetic Zeolites: III. Alkylation of Toluene with Methanol and Formaldehyde on Alkali Cation Exchanged Zeolites. Journal of Catalysis, 26, 303-312. https://doi.org/10.1016/0021-9517(72)90088-7</mixed-citation></ref><ref id="scirp.121478-ref27"><label>27</label><mixed-citation publication-type="other" xlink:type="simple">Taffe, P. (2008) Based on an Paper Given at the 6th European Aromatics &amp; Derivatives Conference—Antwerp, Belgium—14-15 November, 2007.https://www.icis.com/explore/resources/news/2008/01/21/9093889/new-process-may-rescue-styrenics-industry/</mixed-citation></ref><ref id="scirp.121478-ref28"><label>28</label><mixed-citation publication-type="other" xlink:type="simple">Ritter, S.K. (2007, March 19) Styrene. Chemical &amp; Engineering News, 46.</mixed-citation></ref><ref id="scirp.121478-ref29"><label>29</label><mixed-citation publication-type="other" xlink:type="simple">Amusa, A.A. (2009, March) Styrene/Ethylbenzene 07/08-4 Report, ChemSystems, 64-73.</mixed-citation></ref><ref id="scirp.121478-ref30"><label>30</label><mixed-citation publication-type="other" xlink:type="simple">MSDS (2010, November 1) Material Safety Data Sheet Styrene (Monomer) MSDS. MSDS.</mixed-citation></ref><ref id="scirp.121478-ref31"><label>31</label><mixed-citation publication-type="other" xlink:type="simple">US EPA (1994, December) OPPT Chemical Fact Sheets (Styrene) Fact Sheet: Support Document (CAS No. 100-42-5). US EPA, Washington DC. http://www.epa.gov/chemfact/styre-sd.pdf</mixed-citation></ref><ref id="scirp.121478-ref32"><label>32</label><mixed-citation publication-type="other" xlink:type="simple">U.S. Environmental Protection Agency (2004) EPA Settles Case against Phoenix Company for Toxic Chemical Reporting Violations.</mixed-citation></ref><ref id="scirp.121478-ref33"><label>33</label><mixed-citation publication-type="other" xlink:type="simple">U.S. Environmental Protection Agency (2003) EPA Fines California Hot Tub Manufacturer for Toxic Chemical Release Reporting Violations.</mixed-citation></ref><ref id="scirp.121478-ref34"><label>34</label><mixed-citation publication-type="other" xlink:type="simple">Talc at Mindat.org. https://www.mindat.org/min-3875.html</mixed-citation></ref><ref id="scirp.121478-ref35"><label>35</label><mixed-citation publication-type="other" xlink:type="simple">Talc at Webmineral. http://webmineral.com/data/Talc.shtml#.Y3hksnZBzIU</mixed-citation></ref><ref id="scirp.121478-ref36"><label>36</label><mixed-citation publication-type="other" xlink:type="simple">Murali Mohan Rao, K. and Mohana Rao, K. (2007) Extraction and Tensile Properties of Natural Fibers: Vakka, Date and Bamboo. Composite Structures, 77, 288-295. https://doi.org/10.1016/j.compstruct.2005.07.023</mixed-citation></ref><ref id="scirp.121478-ref37"><label>37</label><mixed-citation publication-type="other" xlink:type="simple">Kuriger, R.J. and Khairul Alam, M. (2001-2002) BSME-ASME International Conference on Thermal Engineering, Dhaka, Bangladesh, December.</mixed-citation></ref><ref id="scirp.121478-ref38"><label>38</label><mixed-citation publication-type="other" xlink:type="simple">Chandrasekhar, S., Satyanarayana, K., Pramada, P. and Majeed, J. (2006) Effect of Calcinations Temperature and Heating Rate on the Optical Properties and Reactivity of Rice Husk Ash. Journal of Materials Science (Norwell), 41, 7926-7933. https://doi.org/10.1007/s10853-006-0859-0</mixed-citation></ref><ref id="scirp.121478-ref39"><label>39</label><mixed-citation publication-type="other" xlink:type="simple">Glória, G.O., Teles, M.C.A., Lopes, F.P.D., et al. (2017) Tensile Strength of Polyester Composites Reinforced with PALF. Journal of Materials Research and Technology, 6, 401-405. https://doi.org/10.1016/j.jmrt.2017.08.006</mixed-citation></ref><ref id="scirp.121478-ref40"><label>40</label><mixed-citation publication-type="other" xlink:type="simple">Wilson, J.E. (1974) Radiation Chemistry of Monomers, Polymers and Plastics. Marcel-Dekker, Inc., New York. https://doi.org/10.1063/1.3128702</mixed-citation></ref></ref-list></back></article>