Over the recent years, the global increase of electronic wastes from electrical and electronic devices (e-wastes) has been on an alarming trend in quantity and toxicity and e-waste s are non-biodegradable resulting in its cumulative increase over time. Changes in technology and unrestricted regional movement of electrical devices have facilitated the generation of more e-wastes leading to high levels of air, soil and water pollution. To address these challenges, biodegradable organic components such as chitosan have been used to replace their inorganic counterparts for optoelectronic device applications. However, in-depth knowledge on how such materials can be used to tune the optical properties of their hybrid semiconductors is unrivaled. Thus, systematic studies of the interplay between the preparation methods and optical band gap and Urbach energy of such organic components are vital. This study has thus been dedicated to map out the effect of acid concentrations during chitosan extraction on the corresponding optical band gap and Urbach energy with a view to improving its applications in optoelectronic devices. The, 1.0 to 2.5 molar hydrochloric acid (HCl) was used for 12 hours at room temperature during demineralization and 2.0 molar sodium hydroxide (NaOH) during deprotonation processes. The absorbance spectrum of the samples was collected by UV-Vis spectrophotometer and band gap energies were analyzed by performing Tauc’s plot. This study revealed that the energy band gap of chitosan extracted from 1 M HCl, 1.5 M HCl, 2.0 M HCl and 2.5 M HCl were 3.72 eV, 3.50 eV , 3.45 eV and 3.36 eV respectively. Furthermore, the Urbach energy of chitosan extracted from 1 M HCl, 1.5 M HCl, 2.0 M HCl and 2.5 M HCl were 0.60496 eV, 0.5292 eV, 4724 eV and 0.2257 eV, respectively.
The current global availability of millions of electrical and electronic devices has led to a new environmental pollution of electrical and electronic equipment or devices which are beyond their lifespan (e-wastes) [
Chitosan is one of the most promising natural polymer on earth used in a wide range of applications with excellent film forming abilities, non-toxic, high mechanical strength, metal ion adsorption, and susceptible to chemical modification due to the presence of the reactive hydroxyl and amino functional group. Chitosan is a large structural homo-polysaccharide made up of N-acetyl-D-glucose amine molecules linked with beta (1 - 4) bonds [
The optical absorbance and band gap energy plots of semiconductors and that of chitosan can effectively be figured out by the analysis of the optical band gaps [
α = 2.303 d × absorbance (1)
The absorption coefficient (α) can be used to calculate the optical energy band gap; E g by performing Tauc’s plot [
α h v = B ( h v − E g ) r (2)
Here B is constant that is dependent on the transition probability and r depends on the type of electronic transition. r takes values of 1 2 for direct allowed or 2 for indirect allowed transitions [
The photon energy is quantized through plank’s law:
Energy, h v = h c λ = 1240 λ (3)
From Equation (3), h is planks constant; c is the speed of light and λ is the wavelength. Chitosan samples have shown high absorption of UV light about 90% - 99% between 200 - 400 nm with very little transmission in the absence of reflection. From previous work darkness has also been recorded between 600 nm to 800 nm [
The localized defect states in an optical band gap region of chitosan have been represented by the Urbach energy Eu which is responsible for the formation of absorption tail in the absorption spectra [
ln α = ln α O + h v E u (4)
where α is the absorption coefficient α = 2.303 d × absorbance .
The incident photon energy
h v = h c λ = 1240 λ (5)
The Eu is estimated from ln α versus hν plot from which the reciprocal of the slope obtained by fitting the linear part of the curve gives the value of Eu [
E u = 1 slope (6)
Previous studies have revealed that the Urbach energy (Eu) of chitosan has shown a remarkable increase from 1.11 eV to about 2.22 eV with increasing acid concentrations and this determines the electronic disorder which further affects the degree of disorder in the chitosan sample. These values are however expected to vary depending on the various extraction conditions of chitosan [
In the present study, an in-depth analysis of the microstructure of chitosan solution prepared using different acid concentrations has been investigated using spectrophotometer. The underlying dependence of microstructure on the acid concentrations and the evolution of Eg are addressed by assessing Urbach energy tail (Eu) and associated weak absorption tail energy (Et). This was achieved by extracting chitosan from shrimp by chemical method using 1 M HCl, 1.5 M HCl, 2 M HCl and 2.5 M HCl for 12 hours during demineralization and optical band gap and Urbach energy determined. The quantitative measurement of these optical parameters may help in tailoring and modeling the properties of chitosan composites for use in optical and optoelectronic components and devices.
Chitosan was chemically extracted from shrimp obtained from the shores of Lake Victoria in Kenya. Hydrochloric acid; acetic acid, sodium hydroxide, and deionized water (DI), were purchased from school lab agencies Kisumu (Kenya). All chemicals were of laboratory grade and used without further purification.
To extract chitosan, four major steps were followed: pre-treatment, demineralization, de-protonation and de-acetylation:
Step 1: Pretreatment stage
This was carried out by washing the collected shrimps to remove the external matter and sun dried for four days. 100 g of the dry shrimp was soaked in 50 ml of 2.5 M NaOH to dissolve the non-chitin organic matter.
Step 2: De-protonation stage
This pretreated shrimp shell was washed and dried for two days then grounded into fine powder (approximately 1.5 mm diameter). The chitosan powder was divided into four beakers each of 10 grams. Each of the samples was soaked into 1.5 M NaOH for 24 hours at room temperature to remove the proteins.
Step 3: Demineralization
This process was achieved by soaking them in 1 M, 1.5 M, 2 M and 2.5 M molar hydrochloric acid respectively to eliminate the minerals for another 12 hours. The obtained chitin was washed then filtered to obtain chitin powder and heated in an oven at 60˚C for 5 hrs.
Step 4: De-acetylation
De-acetylation (conversion of chitin to chitosan) was achieved by boiling each of the samples in 1.25 M NaOH at 100˚C for six hours. The powder was then washed severally in distilled water. A white solid chitosan was obtained. The extracted chitosan was dissolved in 1 M acetic acid and left to shake for 5 hours [
Absorption spectra were recorded on Perkin Elmer Lambda 3 B UV-V is spectrometer of wavelength range between 200 - 800 nm at 0.1 nm interval. The optical band gap and Urbach energy were analyzed using origin software by performing Tauc plots.
Absorbance spectra as functions of wavelength, for chitosan prepared by hydrochloric acid of varied concentrations were recorded within wavelength range of 200 nm to 900 nm and the results displayed as shown in Figures 1(a)-(d). The black color shows the experimentally measured data of absorbance spectrum while the red color shows the Gaussian fits of the curves.
From the graphs, the maximum absorbance peaks for chitosan extracted by 1 M HCl was at 279.6674 nm, 1.5 M HCl was at 281.3584 nm, 2.0 M HCl at 282.5032 nm and 2.5 M HCl at 283.598 nm respectively showing steady increase with concentration as shown in the inset of
FWHM was 42.41 nm for 1.0 M HCl, 41.02 nm for 1.5 M HCl, 38.90 nm for 2.0 M HCl and 36.85 nm for 2.5 M HCl showing systematic decrease respectively. The wider peaks could be as a result of the stretching vibrations of hydroxyl, amino and amide groups [
λ max = 283.60 nm ) was observed in the spectra of chitosan extracted by different concentrations of hydrochloric acid which can be attributed to the removal of impurities. This is in consistence with absorption spectrum reported in literature
[
The optical band gap for various samples was obtained by performing Tauc’s plot as shown in Figures 3(a)-(d).
The comparison of energy band gap of chitosan prepared by dilute and concentrated hydrochloric acid within wavelength a range of 200 nm to 800 nm are shown in
From
The important features of
above the valence band to the extended states in the conduction band and/or from the extended states in the valence band to the localized states below the conduction band [
The Urbach energy (Eu) and the associated weak absorption tail energy (Et) for chitosan prepared by 1 M, 1.5 M, 2 M and 2.5 M HCl within wavelength range of 200 nm to 800 nm were obtained by the gradients of the Urbach energy tail and the weak absorption tail energy and are shown in
From the graph, chitosan prepared by 2.5 M HCl shows Eu at 0.2257 eV and Et at 7.0472 eV, for chitosan by 2.0 M HCl, Eu was at 0.47248 eV and Et at 5.1838 eV, for chitosan at 1.5 M HCl, Eu was 0.5292 eV and Et 3.5448 eV and for chitosan extracted by 1 M HCl, Eu was 0.60496 eV and Et 2.3632 eV. The electronic disorder in the crystal (Urbarch energy) was found to be highest for chitosan extracted by dilute hydrochloric acid and lowest when a concentrated acid was used as shown in
This difference could be due to the variations in the disorder or delocalized state of each sample. The defect in chitosan structures increases after de-protonation and demineralization leading to an increase in the electronic disorder for chitosan extracted by lower acid concentrations. The result shows that as the acid concentration increases, the chitosan solutions become more crystalline with increased band gap and reduced Urbach tail. It is noted from
From
| Hydrochloric Acid concentration (M) | Maximum absorbance Wavelength λmax (nm) | Optical energy band gap (Eg) | Eubach energy (Eu) (eV) | Weak absorption tail Et (eV) |
|---|---|---|---|---|
| 1.0 | 279.667 | 3.7567 | 0.2642 | 2.3632 |
| 1.5 | 281.3584 | 3.6887 | 0.2824 | 3.6448 |
| 2.0 | 282.50 | 3.5700 | 0.3537 | 5.1838 |
| 2.5 | 283.598 | 3.4964 | 0.3795 | 7.0472 |
From the results of this study, the energy gap Eg of chitosan extracted by 1, 1.5, 2 and 2.5 molar HCl was found to be 3.7567 eV, 3.67887 eV, 3.5700 eV and 3.4964 eV respectively. The Urbach energy Eu was noted to increase from 0.2642 eV, 0.2824 eV, 0.3537 eV and 0.3795 eV within the range of 1 - 2.5 Molar HCl concentration. From the analysis the weak absorption tails increased systematically from 2.3 eV to 7.0 eV. It can be concluded that optical properties of chitosan are influenced by the acid concentrations used during demineralization. The maximum absorption peaks are observed to be shifted to longer wavelengths as the concentrations of the acid were raised. Consequently, the energy band gaps reduced with increase in acid concentration due to complete removal of impurities which implies lower excitation energy. The electronic disorder consequently decreases with increase in acid concentrations. These findings serve as a fundamental proof of concept that optical properties of chitosan can be tuned by varying the extraction parameters especially acid concentrations for potential applications in bio-semiconductors which can be of great impact on reducing e-waste pollution.
The authors would like to acknowledge the Physical Sciences department of JOOUST for availing equipment required for research. We also take this opportunity to thank all the colleagues in the department for support and encouragement during the entire period of this work.
Authors have no conflict of interest to declare.