1. Introduction

JMMCE

Journal of Minerals and Materials Characterization and Engineering

2327-4077

Scientific Research Publishing

10.4236/jmmce.2021.96038

JMMCE-113030

Articles

Chemistry&Materials Science Engineering

Monazite Recovery by Magnetic and Gravity Separation of Medium Grade Zircon Concentrate from Senegalese Heavy Mineral Sands Deposit

Moumar

Dieye

¹Mohamadou

Moustapha Thiam

¹Anthony

Geneyton

²Mamadou

Gueye

Eramet Ideas, Trappes, France

Earth Science Institute, Cheikh Anta Diop Dakar University, Dakar, Senegal

05112021

09065906085, October 20217, November 2021 10, November 2021

2014

This work is licensed under the Creative Commons Attribution International License (CC BY). http://creativecommons.org/licenses/by/4.0/

Gravity, magnetic and electrostatic separation methods allowed to obtain different titanium oxide concentrates (ilmenite, leucoxene, rutile) and different varieties of zircon concentrates (premium zircon, standard zircon, medium grade zircon standard) from Senegal’s heavy mineral sands. During mining separation, monazite, which is a paramagnetic mineral, was found in a non-negligible concentration of 0.57 wt% on average in the medium grade zircon standard which also contains 37.96 wt% zircon and 44.46 wt% titanium oxides. Magnetic and gravity separation tests were carried out on the Medium grade zircon standard (MGZS) to produce a monazite concentrate at Eramet Ideas laboratory. Magnetic separation at 1.5 teslas intensity resulted in the recovery of 94.8% of the monazite from the MGZS. Gravity separation also recovered 76.6% of the monazite from the MGZS. The combination of these two treatment methods can thus produce three concentrates from MGZS (a monazite concentrate, a zircon concentrate, and a titanium oxide concentrate).

Monazite Heavy Mineral Sands Separation Gravity Magnetic

1. Introduction

Heavy mineral sands (HMS) have great economic interest. They are exploited to extract mainly minerals such as titanium oxides (ilmenite, rutile and leucoxene), and zircon. In some mining operation, monazite (Ce, La, Nd, Th) PO₄ is also recovered as a by-product. It is a mineral which therefore contains rare earth elements. In 2010, the European Commission classified rare earths as critical metals because of their importance for high-tech industry (especially green industries, e.g. lithium for batteries, rare earths for photovoltaics) coupled with the vulnerability of their exploitation (few large deposits in geopolitically unstable areas). Monazite is already recovered as a by-product in some heavy mineral sands operations, notably on beaches and alluvial deposits in India, Malaysia, Sri Lanka, Thailand and Brazil. Indian beach placers are an important source of monazite [1].

GCO mining on the great coast of Senegal focuses on titanium oxides and zirconia without concern for the presence of monazite. This study aims to quantify the amount of monazite in heavy mineral sands and to attempt recovery tests by gravity and magnetic separation.

2. Mining Operation at GCO

The exploitation of the deposit on the great coast of Senegal started in 2014 by Grande Côte Operations (GCO). At the end of 2017, the proven and probable reserves were re-estimated at 24.7 million tons of heavy minerals with 72 wt% of ilmenite, 10.7 wt% of zircon, 3.2 wt% of leucoxene and 2.5 wt% of rutile, i.e. 17.8 million tons of ilmenite, 2.6 million tons of zircon, 790 thousand tons of leucoxene and 617 thousand tons of rutile. The total of titanium minerals amounts to about 19 million tons. The duration of the exploitation has been re-evaluated at 35 years.

The exploitation of heavy mineral sands has many advantages compared to the exploitation of hard rock. Extraction does not require blasting. Fragmentation is absent and processing in this case requires no chemicals. It is carried out on the basis of the physical properties of the minerals such as their density, magnetism, surface electrical conductivity [2].

This mining technique at GCO consists of dredging a continuous channel, called dredge path through the dunal orebody with the dredge and the wet concentrator plant (WCP) floated on the water table. While the dredge removes the material at the front of the mine path, the tailings generated by the mineral separation process in the WCP are stacked at the back by the boom stacker and tailings lines. The tailings represent 98% of the material mined. The suction cutter dredge and the WCP progress about 15 to 30 meters per day depending on the height of the dune and the dredge pond dimensions which range between 500 m to 550 m long and between 200 m to 220 m wide [3]. The dredge pumps the slurry to the WCP, where the mineral is separated by gravity methods (spirals and cyclones). Several stages of cleaner and recleaner operation are necessary to produce heavy mineral concentrate (HMC) at 98% of heavy mineral (Figure 1). The sand tailings are pumped and deposited directly behind the WCP where the rehabilitation of the mined area proceeds.

The heavy mineral concentrate is then transported by truck to the dry process unit (MSP) where it will undergo a high intensity magnetic separation which will

separate the concentrate into two products: a magnetic product (WHMag) containing ilmenite which is a ferromagnetic mineral and a non-magnetic product (WHNM) which contains most of the other heavy minerals such as zircon, rutile, leucoxene and other related minerals such as silicates and others (Figure 2). Non-magnetic products may still contain ilmenite. Indeed, altered ilmenite loses iron and becomes semi-magnetic with the possibility of being found in the non-magnetic product concentrate [4].

These two products (magnetic and non-magnetic) will be processed in two different circuits in parallel.

The ilmenite concentrate (WHMag) will undergo a series of dry electrostatic and magnetic separations to first obtain a pure ilmenite concentrate (ilmenite 1) which is highly conductive and highly magnetic. In this process the non-conductive and non-magnetic particles are also reprocessed by electrostatic separation to produce a second ilmenite concentrate (ilmenite 2). These two concentrates produced differ in their content of titanium oxide and impurities which will define their final use. Generally, ilmenite 1 contains more than 58% titanium oxide and ilmenite 2 contains 54% titanium oxide. All of these separations generate rejects that will be recycled in the separation process.

The non-magnetic product (WHNM) is then treated to produce zircon, rutile and leucoxene concentrates. An electrostatic separation is first done. The conductive minerals are leucoxene and rutile and the non-conductive minerals are zircon.

Different categories of zirconia products will be produced using a series of magnetic and electrostatic separation (Figure 2). The categories of zirconia produced

are: premium grade zirconia and standard grade zirconia, magnetic zirconia and standard medium grade zirconia which differ in the purity of the zirconia minerals which are often coloured by iron oxide coatings. This can greatly influence for example their magnetic properties. In other operations, a sulphuric acid etch is used to strip these surface coatings of zircon particles to make them more acceptable for use in ceramic glazes.

Conductive minerals such as leucoxene and rutile are treated by magnetic separation. Leucoxene which is an altered ilmenite is more magnetic than rutile which is non-magnetic.

3. Materials and Methods3.1. Raw Material

In the study of the mineralogical characterization of heavy mineral concentrates [5], the results of QEMSCAN analyses showed an average concentration of 0.5 wt% monazite in the Medium Grade Zircon Standard Concentrate (MGZS). Monazite is a non-electrically conductive and paramagnetic mineral. This explains why it is found in the MGZS product.

A 200 kg batch of MGZS was taken. Four samples from this batch were taken and mounted in a polished section for mineralogical analysis to confirm their monazite composition. The rest of the batch is used for recovery tests by magnetic and gravity separation.

3.2. Mineralogical Characterization3.2.1. QEMSCAN

QEMSCAN is an automated technique for the fast characterization of mineral and non-crystalline phases, on polished sections, by means of SEM (Scanning Electron Microscope)-EDS (Energy Dispersive Spectrometer). QEMSCAN analyses for this project were carried out at the ERAMET Ideas mineralogical service, using a FEI Quanta 650F SEM platform with two Bruker Xflash 30 mm silicon drift energy dispersive X-ray detectors. The software used included iMeasure v. 5.4 for the data acquisition and iDiscover v. 5.4 for the spectral interpretation and data processing. The “BMA (Bulk Mineral Analyses) measurement mode” was used for mineralogical characterizations of samples with collecting X-ray data every 2.5 μm across the polished sample surfaces, with X-rays acquired at 2000 total X-ray counts per spectrum. The “Field Image measurement mode” was also used to perform mineral mapping of the samples in order to observe alteration textures on a micron scale. The spectrum obtained after analysis of each point within the fields is associated with an experimental EDS spectrum using the system software. From this simulated spectrum, the software determines the relative mass concentrations of the elements present. It is thus necessary to have to fill in the database with information relating to chemical concentrations. At Eramet Ideas, this information comes from microprobe measurements. It is an innovative technology increasingly used in the rapid determination of the mineralogical compositions of sand samples. It is an innovative technology increasingly used in the rapid determination of the mineralogical compositions of sand samples [6] [7] [8] [9].

3.2.2. Scanning Electron Microscopy

The backscattered images of the monazite particles were taken using a JEOL JSM 6360LV scanning electron microscope equipped with a silicon drift detector analysis system at the Géosciences Environnement Toulouse (GET) laboratory in Toulouse. The compositions of the monazite grains were determined using wavelength dispersive spectrometers in the GET laboratory. The operating conditions were: an acceleration voltage of 15 kV, a beam current of 20 nA and a beam diameter of 3 μm for all the elements. Normalization was carried out using: NdPO₄ (Nd), SmPO₄ (Sm), GdPO₄ (Gd), PrPO1 (Pr), DyPO₄ (Dy), Woll (Ca, Si), LaPO₄ (La, P), CePO₄ (Ce), YPO₄ (Y), PbJMM (Pb), ThO₂ (Th), UO₂ (U).

3.2.3. Inductively Plasma Optical Emission and Mass Spectrometry

The samples were analysed at the rock and mineral analysis department of the petrographic and geochemical research center in Nancy (France). The major elements were determined by ICP-OES (Optical Emission Spectrometry) using a Thermo Fischer ICap 6500 and the trace elements by ICP-MS (Mass Spectrometry) using a Thermo Elemental X7.

3.3. Gravity and Magnetic Separation

The gravity separation tests were done with a Holman Wilfley Model 800 laboratory shaker table with 75 kg/hour treatment capacity continuously.

The magnetic separation tests were done with a Pilot Induced Roll Magnetic Separator Mineral Technologies model RL 9011 from Eramet Ideas, which can generate a magnetic field of up to 2 teslas by adjusting an electric current.

4. Results4.1. QEMSCAN Analysis of the Medium Grade Zircon Standard Product

The results of the QEMSCAN® analyses are shown in Table 1. The MGZS concentrate contains on average 38% zircon, 48.8% titanium oxide, 0.57% monazite (Figure 3).

The QEMSCAN processing software was used to isolate some monazite grains shown in blue in Figure 4. The blue particles represent monazite, the purple particles are zircon and the brown particles represent titanium oxides. These monazite particles are mostly free and also show variations in color within the grains themselves, suggesting a variation in their chemical composition.

Monazite is a solid solution between 3 pure poles: pure rare earth monazite (2REEPO₄), cheralite (CaTh(PO₄)₂) and huttonite 2Th(SiO)₄.

Variations in monazite composition are explained by the following substitutions [10] [11] [12] [13]:

2REE 3 + ↔ ( Th , U ) 4 + + Ca 2 + corresponding to substitution by cheralite.

REE 3 + + P 5 + ↔ ( Th , U ) 4 + + Si 4 + corresponding to huttonite substitution.

Table 1 MGZS minerals composition by QEMSCAN

Minerals (wt%)	Sample A	Sample B	Sample C	Sample D	Average
Zircon	37.79	38.04	38.29	37.75	37.9675
Pseudorutile	34.16	34.72	33.39	33.73	34
Rutile	9.37	9.45	9.81	9.84	9.6175
Staurotide	6.3	5.48	5.86	6.08	5.93
Anatase	4.72	4.67	4.77	4.81	4.7425
Grenat	1.21	1.2	1.35	1.32	1.27
Epidote	1.02	0.97	1.16	1.06	1.0525
Tourmaline	0.97	0.96	0.98	0.77	0.92
Quartz	0.72	0.56	0.7	0.63	0.6525
Disthéne	0.58	0.6	0.57	0.64	0.5975
Monazite	0.52	0.59	0.54	0.64	0.5725
Ilménite	0.48	0.54	0.54	0.53	0.5225
Kaolinite	0.41	0.42	0.41	0.39	0.4075
Ilmenorutile	0.34	0.31	0.32	0.33	0.325
Muscovite	0.19	0.18	0.2	0.17	0.185
Priderite	0.18	0.18	0.17	0.18	0.1775
Chromite	0.18	0.24	0.19	0.22	0.2075
Spinelle	0.17	0.18	0.15	0.24	0.185
Oxyde de Fe-Cr	0.16	0.17	0.15	0.14	0.155
Amphibole	0.13	0.1	0.11	0.15	0.1225
Corindon	0.13	0.12	0.1	0.07	0.105
Magnetite	0.04	0.05	0.04	0.04	0.0425
Titanite/Sphene	0.02	0.02	0.02	0.02	0.02
Apatite	0.02	0.02	0.02	0.02	0.02
Others	0.04	0.06	0.03	0.04	0.0425
Total	99.85	99.83	99.87	99.81	99.84

Furthermore, monazite inclusions are also observed in zircon and rutile particles and also xenotime inclusions in zircon.

4.2. Monazite Texture

About 69 particles on a polished section of the MGZS sample were observed under a scanning electron microscope. If the morphology is generally random for all the grains, there are however quite significant textural variations.

The BSE (black Scattered Electron) images of monazite observed with the SEM (scanning electron microscope) make it possible to classify the monazites into 3 textural varieties with relatively homogeneous grains (Figure 5(a)), grains which have a strong zonation (5b) and very weathered grains (Figure 5(c)). These texture variations generally suggest different (magmatic, metamorphic) origins and ages [10] [14] [15] [16] (Dawood & Abd-El Naby, 2007; Spear, 2010; Zhu & O’Nions, 1999). The presence of fractures and more or less extensive alterations could indicate that the monazite particles have undergone alteration and transport processes from the source rock

4.3. Monazite Recovery from MGZS

Monazite concentration from beach placers has been studied by various authors [17] [18] [19] [20]. The separation methods used are the same as for the concentration of zircon and titanium oxides, i.e. magnetic and gravitational separation,

sometimes combined with electrostatic separation. The chemical composition of the feed guides the choice of separation methods. Figure 6 shows the density differences between the different heavy minerals in the sands of Senegal revealed by the QEMSCAN software. Titanium oxides density is 4.5, zircon and monazite are 4.5. Concentration by gravity separation is therefore possible.

Table 2 shows the magnetic susceptibility differences between the different minerals in the sands. Zircon has a low magnetic susceptibility, titanium oxides have a high magnetic susceptibility and monazite has a medium magnetic susceptibility. The magnetic susceptibility values of these different minerals can

Table 2 Physical properties of heavy mineral sand

Mineral	Magnetic susceptibility	Electrical conductivity	SG (g/cm³)	Chemical formula
Ilmenite	high	High	4.5 - 5	Fe∙TiO₃
Rutile	low	High	4.2 - 4.3	TiO₂
Zircon	low	Low	4.7	ZrSiO₄
Leucoxene	Semi	High	3.5 - 4.1	Fe∙TiO₃∙TiO₂
Monazite	Semi	Low	4.9 - 5.3	(Ce, La, Th, Nd, Y)PO₄
Staurolite	Semi	Low	3.6 - 3.8	Fe₂Al₉Si₄O₂₂∙(OH)₂
Kyanite	Low	Low	3.6 - 3.7	Al₂SiO₅
Garnet	Semi	Low	3.4 - 4.2	(Fe, Mn, Ca)₃∙Al₂(SiO₄)₃
Quartz	low	low	2.7	SiO₂

nevertheless vary according to the modification of their composition during the alteration process from the source rock. Thus a magnetic separation between these different products is possible.

According the different separation methods used for monazite recovery, gravity and magnetic separation were chosen to do tests on the MGZS concentrate produced by GCO at Senegalese deposit.

4.4. Magnetic Concentration

The magnetic separation tests were done according to various indications in the literature. Monazite is a paramagnetic mineral that can react in a magnetic field at an intensity of about 1.5 teslas. In order to achieve maximum recovery, the magnetic separation treatment scheme in Figure 7 was adopted. All magnetic separations were performed at 1.5 teslas intensity.

A primary magnetic separation produced 3 products: Magnetic, mids and non-magnetic. The non-magnetic product still undergoes magnetic separation in order to recover the magnetic particles in sterile product. A tertiary magnetic separation is done on the magnetic and mixed concentrates. The non-magnetic resulting from this separation will undergo further magnetic separation and release final steriles. Finally the magnetic and mids concentrates are combined to form the final magnetic concentrate.

At end, three products are obtained from the feed:

A magnetic concentrate C

A sterile S1

A sterile S2

Table 3 shows the analysis results by ICP-OES and ICP-MS of the samples from the magnetic separation. Product C is the magnetic separation concentrate and products S1 and S2 are the sterile.

These results show a high concentration of rare earths and titanium oxides in the magnetic separation concentrate. Zircon is more concentrated in sterile S1 and S2. The magnetic separation appears to have concentrated the rare earth minerals and titanium oxides which are more magnetic than zircon (Figure 8).

4.5. Gravity Concentration

Mineral gravity concentration depends on the specific densities of the different minerals present.

The optimization of monazite recovery by gravity concentration with shaking table required numerous tests. Indeed, the adjustment of the different operation parameters (table incline, solid feed flow, water flow) can only be optimized through tests and a visual rendering of separation between dense and light minerals. Furthermore, the efficiency of a density separation depends greatly on the difference in density between the minerals to be separated. In general, this difference should be at least 1 g/cm³. The small difference in density between the heavy minerals present here (monazite, zircon; titanium oxides) leads us to consider an optimization of the shaking table settings (increase in slope, washing water etc.).

Table 3 Result of chemical analyzes of magnetic separation samples

	SiO₂	Al₂O₃	Fe₂O₃	MnO	MgO	CaO	Na₂O	K₂O	TiO₂	P₂O₅	REE	Zr	Others
	%	%	%	%	%	%	%	%	%	%	ppm	ppm	ppm
MGZS	15.54	6.07	14.92	0.37	0.35	0.64	0.03		35.21	0.32	3479.66	151,030	10,858.9
C	12.31	6.98	18.15	0.47	0.46	0.74	0.04	0.04	39.88	0.36	3794.56	101,893	10,963.5
S1	29.08	1.73	0.16			0.06		0.03	11.26	0.13	743.40	349,112	9838.0
S2	21.21	1.71	0.59			0.12		0.05	32.55	0.19	1446.05	263,609	10,121.3

The multiple tests carried out have made it possible to determine the settings shown in Figure 9.

The following parameters allowed a good separation based on visual observation. Indeed zircon and monazite have a light shade compared to titanium oxides and have a fluorescence under UV lamp:

Solid flow rate: 23.6 kg/h

Liquid supply flow rate: 2.89 L/min

Liquid flow rate of the table: 14.91 L/min

Shaking frequency: 300 Hz

Longitudinal tilt of the table: 3 degrees

Lateral table tilt: 7.8 degrees

Thus 4 products are recovered:

A concentrate of clear products (C)

A concentrate of Mixed 1 (M1)

A concentrate of Mixed 2 (M2)

A sterile (S)

Table 4 shows the analysis results by ICP-OES and ICP-MS of the samples from the gravimetric separation. Product C is the shaking table concentrate.

Table 4 Overall result of gravimetric separation sample analyses

	SiO₂	Al₂O₃	Fe₂O₃	MnO	MgO	CaO	Na₂O	K₂O	TiO₂	P₂O₅	REE	Zr	Others
	%	%	%	%	%	%	%	%	%	%	ppm	ppm	ppm
MGZS	15.54	6.07	14.92	0.37	0.35	0.64	0.03		35.21	0.32	3479.7	151,030	10,859
C	26.66	0.62	2.74	0.03		0.124			6.042	1.72	26202	356,203	17,627
M1	19.02	1.99	11.14	0.28	0.15	0.20			25.39	0.34	3639.9	230,553	11,909
M2	16.72	3.32	12.58	0.32	0.24	0.33			31.23	0.28	2564.5	200,992	11,917
S	13.15	8.65	17.33	0.44	0.51	0.90	0.045	0.037	41.29	0.22	1307.6	79,162	8917.8

Products M1 and M2 are mixed and Product S is the waste rock from this concentration operation.

These results show a high concentration of rare earths and zirconium in concentrate C (Figure 10). The sterile product S is low in these elements. Products M1 and M2 show higher concentrations of zircon and less rare earth minerals.

5. Discussions

The results of the analyses below give the compositions in rare earths and also in zirconium. From these analyses it is possible to reconstitute the monazite and zircon content of the different products obtained. Indeed, the microprobe analyses carried out by the GET laboratory in Toulouse have shown that the monazites in the MGZS product were made up of an average of 58.14% rare earths. Furthermore, the zircon of formula ZrSiO₄ is 43.14% zirconium (Zr). QEMSCAN® analyses of this product showed that monazite is free and virtually the only rare earth bearing mineral.

It is therefore possible to reconstitute the monazite and zirconium contents of the different products from the rare earth and zirconium analyses by applying the following formulas:

Monazite Grade: totalREE REEinmonazite ;

Zircon Grade: totalZr Zrinzircon .

Following Table 5 shows the concentration of monazite and zircon after magnetic separation in the different products as well as the recoveries by weight of concentrate and mineral.

The results in this table show that almost 95% of the monazites were found in the concentrate (C), which constitutes a very good recovery rate. Magnetic separation at an intensity of 1.5 teslas therefore made it possible to concentrate them. The concentrate (C) then has a content of 0.65% monazite and 23.62% zircon. In addition, product S1 has a high concentration of zircon at a content of 80.93%.

Table 5 Monazite and zircon distribution after magnetic separation

	Mass (g)	Mass (%)	Monazite (wt%)	Zircon (wt%)	Monazite recovery (%)	zircon recovery (%)
C	802	80.20%	0.65%	23.62%	94.80%	55.05%
S1	170	17.00%	0.13%	80.93%	3.94%	39.98%
S2	28	2.80%	0.25%	61.11%	1.26%	4.97%
MGZS reconstituted	1000	100%	0.55%	34.41%	100%	100%

Table 6 shows the distribution of monazite and zircon after gravity separation in the different products as well as the recovery by weight and mineral.

The results in this table show that about 40.13% of the monazites in the MGZS were found in the concentrate (C). The monazite in this product has then a content of 4.51% with 82.57% zircon. In addition, mixed product 1 and mixed product 2 have respectively contents of 0.63% and 0.44% monazite with 53.44% and 46.59% zircon.

From the results of the shaking table separation it is interesting to make combinations between the different products to follow the evolution of the recovery and the contents of monazite and zircons according to the weights of the different products.

Following Table 7 and Table 8 give the contents and recovery of the different shaking table products combined.

Figure 11 and Figure 12 show the evolution of monazite and zircon grades and recoveries as a function of weight yields. The recoveries of monazite and zircon evolve inversely to their grades. It is important to note that the more monazite is recovered, the lower the grade of the concentrate obtained.

Taking concentrate C as the final product, the monazite recovery is 40.1% with a content of 4.51%; the zircon recovery is 11.9% with a content of 82.57%. Taking C + M1 + M2 as the final concentrate, monazite recovery would be 76.62% with a grade of 0.62%; zircon recovery is 69.1% with a grade of 52.76%. A magnetic separation of the table top concentrate by shaking allows an optimal recovery of monazite with the possibility to obtain a very high grade zircon concentrate.

It is important to note that these processing operations are carried out in a single step. It is perfectly possible to plan two to three additional treatment stages by recycling the waste rock in order to maximise the recovery of monazite and zircon.

A combination of shake table separation and then magnetic separation can be established through the treatment scheme in Figure 13.

The sterile material from the first shaking table operation is therefore enriched in titanium oxides with a certain amount of zircon and monazite. A magnetic separation of this product at a medium intensity can be envisaged to obtain a zircon and monazite concentrate on the one hand and a titanium oxide concentrate

Table 6 Monazite and zircon distribution after gravity separation

	Mass (%)	Monazite (%)	Zircon (%)	monazite recovery (%)	zircon recovery (%)
C	4.82%	4.51%	82.57%	40.13%	11.92%
M1	14.05%	0.63%	53.44%	16.24%	22.48%
M2	24.85%	0.44%	46.59%	20.25%	34.68%
S	56.28%	0.22%	18.35%	23.38%	30.92%
MGZS reconstituted	100%	0.54%	33.40%	100%	100%

Table 7 Monazite distribution in the different samples combined

Monazite	Mass (%)	Grade (%)	Recovery (%)
C	4.82%	4.51%	40.1%
C + M1	18.87%	1.29%	56.4%
C + M1 + M2	43.72%	0.62%	76.6%
C + M1 + M2 + S	100.00%	0.32%	100%

Table 8 Zircon distribution in the different samples combined

Zircon	Mass (%)	Grade (%)	Recovery (%)
C	4.82%	82.57%	11.9%
C + M1	18.87%	60.88%	34.4%
C + M1 + M2	43.72%	52.76%	69.1%
C + M1 + M2 + S	100.00%	33.40%	100%

on the other hand. Monazite and zircon can then be separated by high intensity magnetic separation. The diagram in Figure 13 therefore proposes a two-stage treatment in parallel allowing the recovery of monazite and zircon to be optimised with the possibility of obtaining a titanium oxide concentrate.

6. Conclusions

QEMSCAN and ICPMS analysis confirmed the monazite concentration in Medium Grade Zircon Standard. Tests to recover monazite from the Medium Grade Zircon Standard concentrate gave interesting results. Magnetic and gravity separation was proved to be effective. It was possible to produce a monazite + titanium oxides concentrate and a zircon concentrate with magnetic separation. In addition, it was possible to produce a zircon + monazite concentrate and a titanium oxide concentrate.

The combination of magnetic and gravity separation can be considered to produce a monazite, zircon and titanium oxide concentrate from MGZS. The MGZS concentrate is today sold as a low zircon concentrate. Its valorization can be of definite economic interest. With a production of 28291 tonnes of MGZS produced in 2018 [21], GCO can consider reprocessing this product in order to better valorise it and increase its profit. However, an economic assessment taking into account the treatment costs must be considered.

Acknowledgements

We graciously thank the Institute for Research and Development (IRD) for funding a large part of the work, as well as the French Embassy, which funded stays in France through a grant. We appreciate the strong participation of the company Grande Côte Opérations (GCO) who accepted this study and provided the necessary information and equipment. We would like to thank the Petro-structural laboratory of the Dakar Institute of Earth Sciences for making and preparing the samples. Finally, we would like to thank the GET laboratory (Georessource environment Toulouse) and Eramet Ideas for carrying out all of the analyses and their expertise in this study.

Conflicts of Interest

The authors declare no conflicts of interest regarding the publication of this paper.

Cite this paper

Dieye, M., Thiam, M.M., Geneyton, A. and Gueye, M. (2021) Monazite Recovery by Magnetic and Gravity Separation of Medium Grade Zircon Concentrate from Senegalese Heavy Mineral Sands Deposit. Journal of Minerals and Materials Characterization and Engineering, 9, 590-608. https://doi.org/10.4236/jmmce.2021.96038

References1

Van Gosen, B.S., Fey, D.L., Salah, A.K., Verplank, P.L. and Hoefen, T.M. (2014) Deposit Model for Heavy-Mineral Sands in Coastal Environments: Scientific Investigations Report 2010-5070-L. U.S. Geological Survey, Reston, VA, 51 p.https://doi.org/10.3133/sir20105070L

Chakhmouradian, A.R and Wall, F. (2012) Rare Earth Elements: Minerals, Mines, Magnets (and More). Elements, 8, 333-340.https://doi.org/10.2113/gselements.8.5.333

Seck, M., Faye, S., Robertson, M. and Rose, M. (2018) Recycling Tailings Seepage Water for Diogo Heavy Minerals Mine Sustainability (Northern Senegal). Journal of Water Resource and Protection, 10, 121-144. https://doi.org/10.4236/jwarp.2018.101008

Delaporte, A., Blancher, S., Goncalves, P. and Wallmach, T. (2018) Physical Property Changes of Fe-Ti Oxides along Their Alteration: A Geometallurgical Study to Improve the Yield of a Mineralurgical Plant. IMPC Conference, Moscow, 17-21 September 2018, 1-22.

Dieye, M., Van Lichtervelde, M., Ndiaye, A.A., Gueye, M. and Blancher, S.B. (2020) Mineralogical Characterization of Heavy Mineral Concentrates from Senegalese Great Cost by Using QEMSCAN and SEM. International Journal of Geosciences, 11, 800-817. https://doi.org/10.4236/ijg.2020.1112041

Edahbi, M., Benzazoua, M., Plante, M., Doire, S. and Kormos, L. (2018) Mineralogical Characterization Using QEMSCAN® and Leaching Potential Study of REE within Silicate Ores: A Case Study of the Matamec Project, Québec, Canada. Journal of Geochemical Exploration, 185, 64-73. https://doi.org/10.1016/j.gexplo.2017.11.007

Guanira, K., Valente, T., Rios, C., Castellanos, O., Salazar, L., Lattanzi, D. and Jaime, P. (2020) Methodological Approach for Mineralogical Characterization of Tailings from a Cu(Au,Ag) Skarn Type Deposit Using QEMSCAN (Quantitative Evaluation of Minerals by Scanning Electron Microscopy). Journal of Geochemical Exploration, 209, Article ID: 106439. https://doi.org/10.1016/j.gexplo.2019.106439

Mackay, D., Simandl, G., Ma, W., Redfearn, M. and Gravel, J. (2016) Indicator Mineral-Based Exploration for Carbonatites and Related Specialty Metal Deposits—A QEMSCAN® Orientation Survey, British Columbia, Canada. Journal of Geochemical Exploration, 165, 159-173. https://doi.org/10.1016/j.gexplo.2016.03.005

Smyte, D., Lombard, A. and Coetzee, L. (2013) Rare Earth Element Deportment Studies Utilising QEMSCAN Technology. Minerals Engineering, 52, 52-61.https://doi.org/10.1016/j.mineng.2013.03.010

Dawood, Y.H. and Abd-El Naby, H.H. (2007) Mineral Chemistry of Monazite from the Black Sand Deposits, northern Sinaï, Egypt: A Provenance Perspective. Mineralogical Magazine, 71, 389. https://doi.org/10.1180/minmag.2007.071.4.389

Harlov, D.E., Wirth, R. and Hetherington, C.J. (2007) Replacement of Monazite by a Huttonite Component: Nature and Experiment. American Mineralogist, 92, 1652-1664. https://doi.org/10.2138/am.2007.2459

Linthout, K. (2007) Tripartite Division of the System 2REEPO4-CaTh(PO4)2-2ThSiO4, Discreditation of Brabantite, and Recognition of Cheralite as the Name for Members Dominated by CaTh(PO4)2. The Canadian Mineralogist, 45, 503-508.https://doi.org/10.2113/gscanmin.45.3.503

Breiter, K. and Förster, H.J. (2021) Compositional Variability of Monazite-Cheralite-Huttonite Solid Solutions, Xenotime, and Uraninite in Geochimically Distinct Granites with Special Emphasis to the Strongly Fractionated Peraluminous Li-F-P-Rich Podlesi Granite System (Erzgebirge/Krušné Hory Mts., Central Europe). Minerals, 11, Article No. 127. https://doi.org/10.3390/min11020127

Spear, F.S. (2010) Monazite-Allanite Phase Relations in Metapelites. Chemical Geology, 279, 55-62. https://doi.org/10.1016/j.chemgeo.2010.10.004

Zhu, X. and O’Nions, R.K. (1999) Zonation of Monazite in Metamorphic Rocks and Its Implications for High Temperature Thermochronology: A Case Study from the Lewisian Terrain. Earth and Planetary Science Letters, 171, 209-220.https://doi.org/10.1016/S0012-821X(99)00146-6

Turlin, F., André-Mayer, A.S., Moukhsil, A., Vanderhaeghe, O., Gervais, F., Solgadi, F. and Pujol, M. (2017) Unusual LREE-Rich, Peraluminous, Monazite- or Allanite-Bearing Pegmatitic Granite in the Central Grenville Province, Québec. Ore Geology Reviews, 89, 627-667. https://doi.org/10.1016/j.oregeorev.2017.04.019

Zhang, J. and Edwards, C. (2013) A Review of Rare Earth Mineral Processing Technology. Mineral Processing CIM Journal, 4, 38-52.

Jordens, A., Sheridan, R., Rowson, N. and Waters, K. (2014) Processing a Rare Earth Mineral Deposit Using Gravity and Magnetic Separation. Minerals Engineering, 62, 9-18. https://doi.org/10.1016/j.mineng.2013.09.011

Moustafa, M.I. and Abdelfattah, N.A. (2010) Physical and Chemical Beneficiation of the Egyptian Beach Monazite. Resource Geology, 60, 288-299.https://doi.org/10.1111/j.1751-3928.2010.00131.x

Kim, K. and Jeong, S. (2019) Separation of Monazite from Placer Deposit by Magnetic Separation. Minerals, 9, Article No. 149. https://doi.org/10.3390/min9030149

CN-ITIE (2019) Rapport de conciliation 2018. ITIE Senegal. Comité national de l'Initiative pour la Transparence dans les Industries Extractives du Sénégal (CN-ITIE). https://itie.sn/rapport-itie-2019/