A. Kljun, et al., “Comparative Analysis of Crystallinity Changes in Cellulose I Polymers Using ATR-FTIR, X-Ray Diffraction, and Carbohydrate-Binding Module Probes,” Biomacromolecules, Vol. 12, No. 11, 2011, pp. 4121-4126. http://dx.doi.org/10.1021/bm201176m

has been cited by the following article:

• TITLE: Homogeneous Isolation of Nanocellulose from Cotton Cellulose by High Pressure Homogenization

  AUTHORS: Yihong Wang, Xiaoyi Wei, Jihua Li, Qinghuang Wang, Fei Wang, Lingxue Kong

  KEYWORDS: Ionic Liquid; Particle Size; High Pressure Homogenization; Thermal Stability; Crystallinity

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.1 No.5, November 7, 2013

  ABSTRACT: Nano-cellulose materials are widely believed to have the potential to push polymer mechanical properties. The cotton cellulose was dissolved in ionic liquid (1-butyl-3-methylimidazolium chloride ([Bmim]Cl)), and then was isolated by high pressure homogenization in a homogeneous media. The nano-cellulose was obtained at 80MPa for 30 cycles. The geometry and microstructure of the cellulose nano-fibres were observed by SEM and their particle size analysis. FTIR, XRD and TGA were used to characterize changes to chemical functionality. Particular emphasis is given to the physical and chemical characterization of these nano-fibres together with their thermal stability and crystallinity, in order to develop their suitability.