M. A. Hamza, F. Saiof, A. Al-ithawi, M. Ameen and H. Yaseen, “Prepared of Nd: TiO2 Nano Particles Powder as IR Filter via Sol-Gel,” Advances in Materials Physics and Chemistry, Vol. 3, No. 2, 2013, pp. 174-177. doi:10.4236/ampc.2013.32024

has been cited by the following article:

• TITLE: Synthesis of Yb3+ Doped TiO2 Nano Particles Powder as IR Filter via Sol-Gel

  AUTHORS: Mohammed A. Hamza, Asmaa Sh. Khalil, Hanna M. Yaseen

  KEYWORDS: Sol-Gel; Nano Technology; TiO2; MID IR Optical Filter

  JOURNAL NAME: Advances in Materials Physics and Chemistry, Vol.3 No.4, August 21, 2013

  ABSTRACT: Ytterbium doped TiO2 nano-particles were prepared via Sol-Gel Technique under varying conditions to investigate the effects of Ytterbium ion doping on the Titania optical properties in MID IR range. X-ray diffraction analyses show that prepared Yb3+ doped TiO2 samples have polycrystalline structure in Anatas phase. FTIR spectrums for pure and doped samples after annealing process show a single transmission peak at wave number around 1145 cm-1. Transmission rate of this peak depends on Yb3+ concentrations and its value rises from 1.82% (for pure TiO2) to 58.1% (for doped with 1.13 wt% Yb3+). Slightly peak shift occurs at a lower doping rate with no further response to higher concentration rate. FTIR spectra gives a good indication in direction of preparation of optical band-pass filter at a wavelength around 8.733 μm (~1145 cm-1).