W. Lin, K.-S. Moon and C. P. Wong, “A Combined Process of in Situ Functionalization and Microwave Treatment to Achieve Ultrasmall Thermal Expansion of Aligned Carbon Nanotube-Polymer Nanocomposites: Toward Applications as Thermal Interface Materials,” Advanced Materials, Vol. 21, No. 23, 2009, pp. 2421-2424. doi:10.1002/adma.200803548

has been cited by the following article:

• TITLE: Enhanced Thermal Conductivity of Carbon Nanotube Arrays by Carbonizing Impregnated Phenolic Resins

  AUTHORS: Dongmei Hu, Hongyuan Chen, Zhenzhong Yong, Minghai Chen, Xiaohua Zhang, Qingwen Li, Zhen Fan, Zhihai Feng

  KEYWORDS: Carbon Nanotube; Phenolic Resin; Pyrolysis; Thermal Conductivity

  JOURNAL NAME: Materials Sciences and Applications, Vol.4 No.8, July 29, 2013

  ABSTRACT: A carbonization method is reported to improve the thermal conductivity of carbon nanotube (CNT) arrays. After being impregnated with phenolic resins, CNT arrays were carbonized at a temperature up to 1400°C. As a result, pyrolytic carbon was formed and connected non-neighboring CNTs. The pyrolysis improved the room temperature conductivity from below 2 W/m·K up to 11.8 and 14.6 W/m·K with carbonization at 800°C and 1400°C, respectively. Besides the light mass density of 1.1 g/cm3, the C/C composites demonstrated high thermal stability and a higher conductivity up to 21.4 W/m·K when working at 500°C.