A. M. Marconnet, N. Yamamoto, M. A. Panzer, B. L. Wardle and K. E. Goodson, “Thermal Conduction in Aligned Carbon Nanotube-Polymer Nanocomposites with High Packing Density,” ACS Nano, Vol. 5, No. 6, 2011, pp. 4818-4825. doi:10.1021/nn200847u

has been cited by the following article:

• TITLE: Enhanced Thermal Conductivity of Carbon Nanotube Arrays by Carbonizing Impregnated Phenolic Resins

  AUTHORS: Dongmei Hu, Hongyuan Chen, Zhenzhong Yong, Minghai Chen, Xiaohua Zhang, Qingwen Li, Zhen Fan, Zhihai Feng

  KEYWORDS: Carbon Nanotube; Phenolic Resin; Pyrolysis; Thermal Conductivity

  JOURNAL NAME: Materials Sciences and Applications, Vol.4 No.8, July 29, 2013

  ABSTRACT: A carbonization method is reported to improve the thermal conductivity of carbon nanotube (CNT) arrays. After being impregnated with phenolic resins, CNT arrays were carbonized at a temperature up to 1400°C. As a result, pyrolytic carbon was formed and connected non-neighboring CNTs. The pyrolysis improved the room temperature conductivity from below 2 W/m·K up to 11.8 and 14.6 W/m·K with carbonization at 800°C and 1400°C, respectively. Besides the light mass density of 1.1 g/cm3, the C/C composites demonstrated high thermal stability and a higher conductivity up to 21.4 W/m·K when working at 500°C.