J. A. Gonzalez, A. C. Carreras and M. del C. Ruiz, “Phase Transformation in Clays and Kaolins Produced bu Thermal Treatment in Chlorine and Air Atmospheres,” Latin American Applied Research, Vol. 37, No. 2, 2007, pp. 133- 139.

has been cited by the following article:

• TITLE: Production of Refractory Lining for Diesel Fired Rotary Furnace, from Locally Sourced Kaolin and Potter’s Clay

  AUTHORS: Fatai Olufemi Aramide, Saliu Ojo Seidu

  KEYWORDS: Refractory; Chamotte; Raw Kaolin; Potter’s Clay

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.1 No.3, May 24, 2013

  ABSTRACT: This research was conducted to formulate a refractory lining recipe for lining diesel fired rotary furnace from locally sourced kaolin, using locally sourced potter’s clay as binder. Six samples (A-F) of kaolin clay mined locally from Apata II area, Ondo road, in Ile-Ife,Nigeria, were roasted at 1200oC held for 8 hours, mixed with different percentages of raw kaolin and appropriately made into briquettes using potter’s clay of good plasticity as binder. The samples were tested for various refractory properties. The result showed that sample mixes A (100% chamotte), B (80% chamotte, 20% rawkaolin) and C (60% chamotte, 40% raw kaolin) are considered to have good properties. However, the optimum material-mix for the refractory bricks lining, with particular reference to the highest thermal shock resistance was found to be 80% chamotte mixed with 20% raw kaolin.