TITLE:
Synthesis of Polyfluorene-Polytriarylamine Block Copolymer with Emitting Part at Junction Point for Light Emitting Applications
AUTHORS:
Mehdi Jahanfar, Kenta Suwa, Kousuke Tsuchiya, Kenji Ogino Ogino
KEYWORDS:
Polyfluorene; Polytriarylamine; Block Copolymer; Junction Point; Polymer Light-Emitting Diode
JOURNAL NAME:
Open Journal of Organic Polymer Materials,
Vol.3 No.2,
April
29,
2013
ABSTRACT: A block copolymer consisting of polyfluorene (PF) and polytriarylamine (PTAA) functionalized with green emitting phenoxazine moiety at the junction point of two blocks was designed and prepared for electroluminescent application. PF homopolymer was synthesized by Suzuki coupling polymerization, and was reacted with brominated phenoxazine. In the presence of the resulting PF functionalized with phenoxazine, C-N coupling polymerization of 4-(4’-bromophenyl)-4’’-butyldiphenylamine was carried out to afford a triblock copolymer, PTAA-phenoxazine-PF-phenoxazine-PTAA (PF-Ph-PTAA). Two types of random copolymers were also synthesized with fluorene and phenoxazine (PF2) by Suzuki coupling polymerization for comparison. All the polymers were soluble in common organic solvents and readily formed thin films by a solution processing. Prepared polymers exhibited similar UV absorption and PL emission in chloroform solutions. In a film state, the existence of phenoxazine unit drastically changed PL spectra. Although the content of phenoxazine unit in PF-Ph-PTAA was relatively high (13 mol%), it showed similar PL spectrum to that of PF2(phenoxazine content, 0.2 mol%) indicating that phenoxazine unit is isolated in single polymer chain nevertheless the high content. EL device based on PF-Ph-PTAA showed green-emission, suggesting that emission sites predominantly located in the vicinity of phenoxazine moiety because of its shallow HOMO level.