L. Zong, S. Zhou, R. Sun, L. C. Kempel and M. C. Hawley, “Dielectric Analysis of a Crosslinking Epoxy Resin at a High Microwave Frequency,” Journal of Polymer Science Part B: Polymer Physics, Vol. 42, No. 15, 2004, pp. 2871-2877. doi:10.1002/polb.20154

has been cited by the following article:

• TITLE: Microwave Absorption Properties of Carbon Nanotubes-Epoxy Composites in a Frequency Range of 2 - 20 GHz

  AUTHORS: Zhou Wang, Guang-Lin Zhao

  KEYWORDS: Microwave Absorption; Multi-Walled Carbon Nanotubes; Epoxy Composites; Absorption Ratio; Dielectric Loss

  JOURNAL NAME: Open Journal of Composite Materials, Vol.3 No.2, April 12, 2013

  ABSTRACT: In this work, multi-walled carbon nanotubes (MWCNTs)-epoxy composites with MWCNTs (outer diameter less 8 nm) loadings from 1 to 10 wt% were fabricated. The microstructures, dielectric constant, and microwave absorption properties of the MWCNTs-epoxy composite samples were investigated. The measurement results showed that the microwave absorption ratio of the MWCNTs-epoxy composite strongly depend on the MWCNT loading in the composites. The microwave absorption ratio up to 20%-26% around 18-20 GHz was reached for the samples with 8-10 wt% MWCNT loadings. The high absorption performance is mainly attributed to the microwave absorption of MWCNTs and the dielectric loss of MWCNTs-epoxy composites.