C. H. Caceres, M. B. Djurdjevic, T. J. Stockwell and J. H. Sokolowski, “The Effect of Cu Content on the Level of Microporosity in Al-Si-Cu-Mg Alloys,” Scripta Materialia, Vol. 40, No. 5, 1999, pp. 631-637. doi:10.1016/S1359-6462(98)00492-8

has been cited by the following article:

• TITLE: On the Role of Copper and Cooling Rates on the Microstructure, Defect Formations and Mechanical Properties of Al-Si-Mg Alloys

  AUTHORS: Salem Seifeddine, Emma Sjölander, Toni Bogdanoff

  KEYWORDS: Aluminium-Silicon Alloys; Microstructure; Mechanical Properties; Gradient Solidification

  JOURNAL NAME: Materials Sciences and Applications, Vol.4 No.3, March 29, 2013

  ABSTRACT: This paper aims to assess the role of Cu on Al-Si-Mg alloys, in a range of 0 - 5 wt%, qualitatively on microstructure, defect formation, in terms of porosity, and strength in the as-cast conditions. The ternary system of Al-Si-Mg, using the A356 alloy as a base material, were cast using the gradient solidification technique; applying three different solidification rates to produce directional solidified samples with a variety of microstructure coarsenesses. Microstructural observations reveal that as the Cu levels in the alloys are increased, the amounts of intermetallic compounds as well as the Cu concentration in the α-Al matrix are increased. Furthermore, the level of porosity is unaffected and the tensile strength is improved at the expense of ductility.