J. J. Ge, M. Guo, Z. Zhang, P. S. Honigfort, S.-Y. Wang, F. W. Harris, et al., “Phase Structures, Transition Behavior, and Surface Alignment in Polymers Containing Rigid-Rod Backbones with Flexible Side Chains. 4. Solid-State 13C NMR Studies of Molecular Motions in PEFBPs(n) (n = 10 and 11),” Macromolecules, Vol. 33, No. 11, 2000, pp. 3983-3992. doi10.1021/ma981970y

has been cited by the following article:

• TITLE: Liquid Crystalline Polymers XIII Main Chain Thermotropic Copoly (Arylidene-Ether)s Containing 4-Teriary Butyl-Cyclohexanone Moiety Linked with Polymethylene Spacers

  AUTHORS: Nayef S. Al-Muaikel, Kamal I. Aly

  KEYWORDS: Liquid Crystal; Thermotropic; Synthesis; Characterization; Poly(Arylidene-Ether)s

  JOURNAL NAME: Open Journal of Organic Polymer Materials, Vol.3 No.1, January 28, 2013

  ABSTRACT: A new homologous series of thermotropic liquid crystalline copoly(arylidene-ether)s based on 4-teriary butyl cyclohexanone moiety were synthesized by solution polycondensation of 4,4’-diformyl-α,ω-diphenoxyalkanes, Ia-d or 4,4’- diformyl-2,2’-dimethoxy-α,ω-diphenoxyalkanes IIa-d with the 4-teriary butyl-cyclohexanone III and cyclopentanone. A model compound IV was synthesized from the monomer III with benzaldehyde and characterized by elemental and spectral analyses. The inherent viscosities of the resulting polymers were in the range 0.22 - 0.92 dI/g. All the copoly(arylidene-ether)s were insoluble in common organic solvents but dissolved completely in concentrated H2SO4 and formic acid. The mesomorphic properties of these polymers were studied as a function of the diphenoxyalkane space length. Their thermotropic liquid crystalline properties were examined by DSC and optical polarizing microscopy and demonstrated that the resulting polymers form nematic mesophases over wide temperature ranges. The thermogravimetric analyses of those polymers were evaluated by TGA and DSC measurements and correlated to their structural units. X-Ray analysis showed that copolymers having some degree of crystallinity in the region 2q = 5° -60°. In addition, the morphological properties of selected examples were tested by Scanning electron microscopy.