Article citationsMore>>

Y. Ding, Y. Wan, Y. L. Min, W. Zhang and S. H. Yu, “General Synthesis and Phase Control of Metal Molybdate Hydrates MMoO4?nH2O (M = Co, Ni, Mn, n = 0, 3/4, 1) Nano/Microcrystals by a Hydrothermal Approach: Magnetic, Photocatalytic, and Electrochemical Properties,” Inorganic Chemistry, Vol. 47, No. 17, 2008, pp. 7813-7823. doi:10.1021/ic8007975

has been cited by the following article:

• TITLE: Photoluminescent Properties of CoMoO4 Nanorods Quickly Synthesized and Annealed in a Domestic Microwave Oven

  AUTHORS: Ana P. de Moura, Larissa H. de Oliveira, Paula F. S. Pereira, Ieda L. V. Rosa, Máximo S. Li, Elson Longo, José A. Varela

  KEYWORDS: Photoluminescence; Nanorods; Molybdates; Microwave-Hydrothermal Method

  JOURNAL NAME: Advances in Chemical Engineering and Science, Vol.2 No.4, November 1, 2012

  ABSTRACT: A simple way to prepare α- and β-CoMoO4 nanorods is reported in this paper. CoMoO4xH2O nanorod precursors were obtained using the microwave-assisted hydrothermal (MAH) method. By annealing the as-prepared CoMoO44xH2O precursor at 600℃ for 10 min in a domestic microwave oven, α- and β-CoMoO4 nanorods were prepared. These powders were analyzed by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), Fourier transform Raman microscopy and ultraviolet visible absorption spectroscopy (UV-vis spectra) as well as photoluminescence (PL) measurements. Based on the results, these materials revealed nanorod morphology. PL spectra obtained at room temperature for α- and β-CoMoO4 particles exhibited maximum components around the blue light emission. The results show that the domestic microwave oven has been successfully employed to obtain α- and β-CoMoO4 nanoparticles.