K. Rajesh, P. Shajesh, O. Seidei, P. Mukundan and K. G. K. Warrier, “A Facile Sol-Gel Strategy for the Synthesis of Rod-Shaped Nanocrystalline High-Surface-Area Lan- thanum Phosphate Powders and Nanocoatings,” Advan- ced Functional Materials, Vol. 17, No. 10, 2007, pp. 1682-1690. doi:10.1002/adfm.200600794

has been cited by the following article:

• TITLE: Synthesis and Fluorescence Properties of Europium-Lanthanum-Calcium Orthophosphates and Condensed Phosphates

  AUTHORS: Hiroaki Onoda, Takehiro Funamoto

  KEYWORDS: Condensed Phosphate; Europium; Fluorescence; Resistance against Hydrofluoric Acid

  JOURNAL NAME: Advances in Materials Physics and Chemistry, Vol.2 No.4, December 28, 2012

  ABSTRACT: Mixtures of lanthanum oxide, europium oxide, calcium carbonate, and phosphoric acid were heated with various ratios of P/(Eu + La + Ca) and La/Ca. Europium ratio was settled at Eu/(Eu + La + Ca) = 0.03. The obtained phosphates were estimated using X-ray diffraction (XRD) patterns, Fourier transform infrared spectroscopy (FT-IR) spectra, and scanning electron micrograph (SEM) images. The fluorescence spectra and resistance against hydrofluoric acid were estimated as functional properties of these phosphate materials. The mixture of lanthanum and calcium phosphates were formed from XRD patterns and IR spectra. Samples prepared in P/(Eu + La + Ca) = 2 and 3 had large particles in SEM images. The condensed phosphates showed a strong peak at 615 nm and high resistance against hydrofluoric acid.