Keggin Structure and Surface Acidity of 12-Phosphotungstic Acid Grafted Zr-MCM-48 Mesoporous Molecular Sieves
AUTHORS:
Zhiqi Wang, Juan Navarrete
KEYWORDS:
Zr-MCM-48; Surface Acidity; Heteropolyacid; Spectroscopic Characterization
JOURNAL NAME:
World Journal of Nano Science and Engineering,
Vol.2 No.3,
September
28,
2012
ABSTRACT: A zirconium modified MCM-48 mesoporous material was synthesized by surfactant-templated method. Surface grafting Zr-MCM-48 with tungstophosphoric acid led to a great enhancement of both the number of the Br?nsted acid sites and acidity strength in comparison with the bare support. At 100°C, the 30 wt% H3PW12O40/Zr-MCM-48 contained 174 μmol/g Br?nsted acid sites which were 14.5 times greater than that of Zr-MCM-48. The Keggin structure of the grafted heteropolyacid was rather stable after calcination at 400°C for 2 h, approximately 93.3% of Keggin structure in the dispersed heteropolyacid were remained without destruction but slightly distorted in some degree, as evidenced by FTIR characterization and 31P NMR-MAS analysis. This H3PW12O40/Zr-MCM-48 solid with three dimensional mesoporous system, large surface area and very strong Br?nsted acidity will be a promising catalyst for acid catalytic reactions.