K. Kondo, T. Chiba, H. Ono, S. Yoshida, Y. Shimada, N. Matsushita and M. Abe, “Conducted Noise Suppression Effect up to 3 GHz by Ni-Zn Ferrite Film Plated at 90?C Directly onto Printed Circuit Board,” Journal of Applied Physics, Vol. 93, No. 10, 2003, pp. 7130-7132.

has been cited by the following article:

• TITLE: Synthesis, XRD & SEM Studies of Zinc Substitution in Nickel Ferrites by Citrate Gel Technique

  AUTHORS: K. Rama Krishna, D. Ravinder, K. Vijaya Kumar, Ch. Abraham Lincon

  KEYWORDS: Ni-Zn Ferrite; Citrate Precursor Auto Combustion; Saturation Magnetization; Magnetic Moment

  JOURNAL NAME: World Journal of Condensed Matter Physics, Vol.2 No.3, August 31, 2012

  ABSTRACT: Ni-Zn ferrite with a nominal composition of Ni1–XZnXFe2O4 (X = 0, 0.2, 0.6, 0.8, 0.9 & 1.0) ferrite powders have been successfully prepared at a very low temperature (180℃) by a novel auto combustion process using citric acid as a coordinating agent. Phase purity of the solid solutions has been confirmed by X-ray diffraction. Morphological, elemental composition characterizations of the prepared samples were performed by high resolution scanning electron microscopy and energy dispersive spectroscopy (EDS). Magnetic properties of all samples are obtained by using VSM (Vibrating Sample Magnetometer) in the range of 10 K oe. The saturation magnetization values of the samples are carried out from the B-H loop. The effect of composition on saturation magnetization and magnetic moment are studied in this paper. The results showed that Saturation magnetization and magnetic moment values increases gradually as Zn2+ composition increases, it reaches maximum value 70.28 emu/gm for (X = 0.6) and decreases further with increasing Zn2+ composition.