Article citationsMore>>

Y.-Q. Song, H.-W. Zhang, Q.-Y. Wen, L. Peng and J. Q. Xiao, “Direct Evidence of Oxygen Vacancy Mediated Ferromagnetism of Co Doped CeO2 Thin Films on Al2O3 (0001) Substrates,” Journal of Physics: Condensed Matter, Vol. 20, No. 25, 2008, Article ID 255210. doi:10.1088/0953-8984/20/25/255210

has been cited by the following article:

• TITLE: Co-Precipitation Synthesis and Characterization of Nanocrystalline Zinc Oxide Particles Doped with Cu2+ Ions

  AUTHORS: Mergoramadhayenty Mukhtar, Lusitra Munisa, Rosari Saleh

  KEYWORDS: Cu-Doped ZnO; Structural Properties; Room Temperature Ferromagnetism

  JOURNAL NAME: Materials Sciences and Applications, Vol.3 No.8, August 22, 2012

  ABSTRACT: Nanocrystalline Cu-doped ZnO particles were synthesized by the co-precipitation method. The composition, structural, optical and magnetic characterizations were performed by energy dispersive X-Ray spectroscopy, X-Ray diffraction, UV-Visible spectrometer, and vibrating sample magnetometer. The results confirmed that nanocrystalline Cu-doped ZnO particles have a hexagonal wurtzite structure with a high degree of crystallization and a crystallite size of 10 - 16 nm. For Cu above 11 at%, the X-Ray diffraction pattern possessed CuO secondary phase which shows the solubility limit of Cu in the ZnO lattice. Up to 11% at Cu, the presence of Cu in the ZnO lattice as Zn substitution indicated by an in- crease in lattice parameter values. Nanoparticles showed weak ferromagnetic characteristics at room temperature. The absence of secondary phase related to magnetic precipitate shown intrinsic ferromagnetic behaviour.