Article citationsMore>>

R. M. Munoz, L. C. Casteletti, L. C. F. Canale and G. E. Totten, “Improved Wear Resistance of P/M Tool Steel Alloy with Different Vanadium Contents after Ion Nitriding,” Wear Journal, Vol. 50, No. 12, 2007, pp. 57-64.

has been cited by the following article:

• TITLE: A Study on Wear Resistance, Hardness and Impact Behaviour of Carburized Fe-Based Powder Metallurgy Parts for Automotive Applications

  AUTHORS: Ali Emamian

  KEYWORDS: Carburizing; Wear Resistance; Powder Metallurgy

  JOURNAL NAME: Materials Sciences and Applications, Vol.3 No.8, August 22, 2012

  ABSTRACT: In order to study the mechanical and triboloical properties of powder metallurgy (PM) parts under different process parameters, the specimens were used in pack carburizing processes. These specimens made from industrial test pieces were carburized in a powder pack for about two to five hours at a temperature of about 850?C - 950?C. The effects of austenitization and quenching are investigated on some specimens. Also the wear tests are performed by means of a pin-on-disc tribotester using roll bearing steel as the counterface material. The results indicate that by appropriate selection of process parameters, it is possible to obtain high wear resistance along with moderate toughness. It is concluded that surface treatments increases the wear resistance and performance of PM parts in service conditions. By increasing the role of PM in industry which resulted from their ability to produce the complex shapes, high production rate, and dimension accuracy of final products, they need to be heat treated. Carburizing method was selected as a surface hardening method for PM parts. Results of wear and hardness show considerable enhancement in mechanical properties of PM parts.