• TITLE: High Temperature Oxidation and Hot Corrosion Behaviour of 9Cr 1Mo Ferritic Cold Rolled Steel in Air at 900°C under Cyclic Condition

  AUTHORS: Amarish K. Shukla, Dinesh Gond, M. Bharadwaj, D. Puri

  KEYWORDS: Hot corrosion; cold rolling; cyclic oxidation.

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.10 No.11, September 12, 2011

  ABSTRACT: The oxidation behaviour of 10%, 30%, and 50% cold rolled and unprocessed 9Cr 1Mo ferritic steels in air have been studied under isothermal conditions at a temperature of 900°C in a cyclic manner. Oxidation kinetics was established for all samples on which experiment was conducted in air at 900°C under cyclic conditions for 50 cycles by thermogravimetric technique. Each cycle consisted of 1 hour heating at 900°C followed by 20 min of cooling in air. 10% cold rolled sample followed parabolic rate of oxidation while 30% cold rolled sample showed accelerated rate of weight gain. X-ray diffraction (XRD) and scanning electron microscopy/energy dispersive X-ray (SEM/EDAX) techniques were used to characterise the oxidized sample and their scales. 10% cold rolled steel was found to be more corrosion resistance than other in air oxidation for 50 cycles.