• TITLE: Nitriding of Medium Carbon Ferromanganese Alloy in Gas Solid Reaction

  AUTHORS: Saeed N. Ghali

  KEYWORDS: Nitriding, Gas Solid Reaction

  JOURNAL NAME: Journal of Minerals and Materials Characterization and Engineering, Vol.10 No.4, March 28, 2011

  ABSTRACT: Nitriding process of medium carbon ferromanganese was carried out in the solid state, on lab and bench scale at temperature range 1023-1323 K using different nitrogen and hydrogen pressures. The influence of H2/N2 gas ratio, temperature and time on nitriding process of fine (-2 mm) medium carbon ferromanganese were investigated. Nitrogen content, in weight percent ranging from 2.1 to 9.7 could be obtained. The optimum temperature and time of nitriding process was found to be 1223 K and 21.6 ks respectively. The results showed that nitrogen content is mainly depending on time and temperature of nitriding process. The comparison between results of lab and bench scale, at optimum conditions, showed good coincidence. At optimum conditions; 1223 K, 21.6 ks and at 2/8 of H2/N2, nitrogen content of fine medium carbon ferromanganese was 9.5%.