T. Takahagi, I. Shimada, M. Fukuhara, K. Morita and A. Ishitani, “XPS Studies on the Chemical Structure of the Stabilized Polyacrylonitrile Fiber in the Carbon Fiber Production Process,” Journal of Polymer Science Part A: Polymer Chemistry, Vol. 24, No. 11, 1986, pp. 3101-3107.

has been cited by the following article:

• TITLE: Structural Evolution of Polyacrylonitrile Fibers in Stabilization and Carbonization

  AUTHORS: Sungho Lee, Jihoon Kim, Bon-Cheol Ku, Junkyung Kim, Han-Ik Joh

  KEYWORDS: Polyacrylonitrile; Stabilization; Carbonization; XRD; Tensile Properties; Carbon Fibers

  JOURNAL NAME: Advances in Chemical Engineering and Science, Vol.2 No.2, April 27, 2012

  ABSTRACT: The effect of structural evolution polyacrylonitrile (PAN) on mechanical properties was investigated in stabilization and carbonization. PAN spun fibers were stabilized in a convection oven with a constant tension for various times at 250℃. Fourier Transform Infrared spectroscopy (FTIR) and gel fraction results suggested that intra and intermolecular stabilization reactions occurred simultaneously. X-ray diffractograms revealed a disruption of crystalline structure and an appearance of pre-graphitic structure of PAN fibers due to stabilization. These structural changes by stabilization resulted in the significant decrease of tensile properties of fibers. In Raman spectra with heat treated fibers from 400℃ up to 1200℃, the intensity ratio of the D to G bands (ID/IG) decreased as heat treatment temperature increased, indicating an increase of basal plane of graphitic layer of heat treated fibers. Tensile strength of heat treated fibers at 1200℃ was found to be as high as 2.2 GPa.