N. Kawahara, H. Enami, T. Sinohara, H. Hoshizaki, et al., “Destruction and Recovery of Superconductivity in Bi-Pb-Sr-Ca-Cu-O Synthesized under High Pressure,” Japanese Journal of Applied Physics, Vol. 31, No. 8, 1992, pp. 2427-2431. doi:10.1143/JJAP.31.2427

has been cited by the following article:

• TITLE: Preparation and Characterization of Hot-Pressed and Sintered BiPbSrCaCuO Superconductor

  AUTHORS: Mohamed Mohamed Ibrahim, Nassar Mahmoud Megahid, Mostafa Mohamed Abd El-Raheem, Sayed Mohammed Khalil

  KEYWORDS: Electrical Resistivity; Superconductors; Hot Pressing; Sintering

  JOURNAL NAME: New Journal of Glass and Ceramics, Vol.2 No.2, April 23, 2012

  ABSTRACT: Powder compacts of the system Bi2–xPbxSr2Ca2Cu3Oy with 0 ≤ x ≤ 0.5 molar ratio using both techniques; isothermal hot pressing and the solid state reaction (sintering). The XRD of the hot pressed powder compacts of the nominal compositions Bi2–xPbxSr2Ca2Cu3Oy showed 2212 and 2223 phases. The resistivity temperature variations belonging to the composition Bi1.8Pb0.2Sr2Ca2Cu3Oy showed metal-superconducting transition at Tons = 143 K for the annealed sample for 24 h. The annealed nominal composition Bi1.5Pb0.5Sr2Ca2Cu3Oy for 18 h showed metal to superconducting transition at 80 K.