Article citationsMore>>

Ahmad, J., Purbolaksono, J. and Beng, L.C. (2010) Thermal Fatigue and Corrosion Fatigue in Heat Recovery Area Wall Side Tubes. Engineering Failure Analysis, 17, 334-343.
https://doi.org/10.1016/j.engfailanal.2009.06.014

has been cited by the following article:

• TITLE: Metallurgical Forensics: Investigating a Superheater Tube Failure in Industrial Process Plants

  AUTHORS: Kok Toong Leong

  KEYWORDS: Superheater Tubes, Thermal Degradation, Corrosion-Erosion, Embrittlement, Stress Rupture

  JOURNAL NAME: World Journal of Engineering and Technology, Vol.12 No.3, August 21, 2024

  ABSTRACT: A metallurgical forensic investigation was conducted to determine the cause of a failed superheater tube. Analysis techniques by Visual Examination, Energy Dispersive X-ray Analysis, Mechanical Testing and Metallographic Investigation were conducted, together with a comparative study from an inlet elbow section that did not fail. The superheater tube suffered premature failure after being in service for about two years. It was concluded that the failed tube underwent overheating, corrosion-erosion, embrittlement, and eventual failure under its internal pressure by stress rupture. The analysis revealed intergranular cracks, window fracture features and spheroidization of pearlite with grain growth. A possible contribution to embrittlement was from copper. Follow-ups and recommendations were provided, as well as covering materials, inspection, and operational considerations.