V. D. Patake, S. M. Pawar, V. R. Shinde, et al., “The Growth Mechanism and Supercapacitor Study of Anodically Deposited Amorphous Ruthenium Oxide Films,” Current Applied Physics , Vol. 10, No. 1, 2010, pp. 99- 103. doi:10.1016/j.cap.2009.05.003

has been cited by the following article:

• TITLE: Poorly Crystalline Ru0.4Sn0.6O2 Nanocomposites Coated on Ti Substrate with High Pseudocapacitance for Electrochemical Supercapacitors

  AUTHORS: Yanqun Shao, Zhonghua Yi, Fenghua Lu, Fenyong Deng, Beibei Li

  KEYWORDS: Specific Capacitance; Supercapacitor; RuO2-SnO2; Electrode; Thermal Decomposition

  JOURNAL NAME: Advances in Chemical Engineering and Science, Vol.2 No.1, December 31, 2011

  ABSTRACT: Poorly crystalline Ru0.4Sn0.6O2 solid solution with size about 2 nm coated on Ti substrate was prepared by thermal decomposition at 260°C. The electrodes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) for structural and morphological studies. The Capacitance properties of the electrodes were tested by cyclic voltammetry and charge-discharge tests. The results show that the electrodes have mud-cracks structure with cracks 0.2 μm in width. The electrode has stable electrochemical capacitor properties with a maximum specific capacitance of 648 F/g within a scan potential window –0.1 - 1.0 V in 0.5 M H2SO4 electrolyte solution.