TITLE:
A Comparison of Hydrothermal Aging, SO2 and Propene Poisoning Effects on NH3-SCR over Cu-ZSM-5 and Cu-SAPO-34 Catalysts
AUTHORS:
Kouadio Brou Albert, Koffi Konan Martin, Zran Van Eric-Simon, Horo Kone
KEYWORDS:
Hydrothermal Aging, Propene and SO2 Poisoning, Ammonia-Selective Catalytic Reduction (NH3-SCR), Cu-SAPO-34, Cu-ZSM-5
JOURNAL NAME:
Journal of Materials Science and Chemical Engineering,
Vol.12 No.5,
May
28,
2024
ABSTRACT: This study was aimed to investigate the effects of hydrothermal aging, propene and SO2 poisoning on the ammonia-selective catalytic reduction (NH3-SCR) performance of both Cu-SAPO-34 and Cu-ZSM-5. The catalytic activities of fresh, aged and poisoned samples were tested in ammonia-selective catalytic reduction (NH3-SCR) of NOx conditions. The XRD, TG and N2-desorption results showed that the structures of the Cu-SAPO-34 and Cu-ZSM-5 remained intact after 750˚C hydrothermally aged, SO2 and propene poisoned. After hydrothermal aging at 750˚C for 12 h, the NO reduction performance of Cu-ZSM-5 was significantly reduced at lower temperatures, while that of Cu-SAPO-34 was less affected. Moreover, Cu-SAPO-34 catalyst showed high NO conversion with SO2 or propene compared to Cu-ZSM-5. However, Cu-ZSM-5 showed a larger drop in catalytic activity with SO2 or propene compared to Cu-SAPO-34 catalyst. The H2-TPR results showed that Cu2 ions could be reduced to Cu and Cu0 for Cu-ZSM-5, while no significant transformation of copper species was observed for Cu-SAPO-34. Meanwhile, the UV-vis DRS results showed that CuO species were formed in Cu-ZSM-5, while little changes were observed for the Cu-SAPO-34. Cu-SAPO-34 showed high sulfur and hydrocarbon poison resistance compared to Cu-ZSM-5. In summary, Cu-SAPO-34 with small-pore zeolite showed higher hydrothermal stability and better hydrocarbon and sulfur poison resistant than Cu-ZSM-5 with medium-pore.