Zheng, M., Zheng, Y., Zha, J., Yang, Y., Han, P., Wen, Y. and Dang, Z. (2018) Improved Dielectric, Tensile and Energy Storage Properties of Surface Rubberized BaTiO3/Polypropylene Nanocomposites. Nano Energy, 48, 144-151.
https://doi.org/10.1016/j.nanoen.2018.03.049

has been cited by the following article:

• TITLE: The Impact of the Inclusion of MgO Nano-Fillers in a Polyethylene Matrix on Dielectric Strength and Resistance to Partial Discharges

  AUTHORS: Virginie Griseri, Dominique Mary, David Malec, Eric David

  KEYWORDS: Low Density Polyethylene, MgO Nanofillers, Dielectric Strength, Partial Discharges Resistance

  JOURNAL NAME: Open Journal of Applied Sciences, Vol.14 No.3, March 15, 2024

  ABSTRACT: One commonly used strategy to enhance polymers specific properties such as the resistance to partial discharges erosion is the incorporation into the polymeric matrix of inorganic micro or nanoparticles. This study focused on the dielectric properties of Low-Density Polyethylene (LDPE) filled with nano-sized Magnesium Oxide (MgO) particles compounded by thermo-mechanical process and one of the purposes was to establish appropriate processing parameters in order to reach the desired dielectric properties. LDPE was used as a matrix and was reinforced by MgO particles having a nominal average size of 30 nm. The MgO nanoparticles were treated with a silane coupling agent (3-Glycidyloxypropyl Trimethoxysilane). The samples were initially prepared in a melt-mixing chamber with a MgO content of 1% wt. These pre-mixed samples were further treated by the means of thermo-mechanical mixing in a conical co-rotating twin-screw extruder in order to improve the dispersion and distribution of the MgO particles. In this report, both lifetime under a PD activity and AC dielectric strength of pure and nano-filled LDPE samples have been measured and compared. Nano-filled LDPE samples were found to exhibit an improve lifetime, without any detrimental impact on their short-term dielectric strength. This suggests that nano-filled LDPE may be for electric applications for which the dielectric materials may be exposed to partial discharge activities. This is significant result for the use of MgO-reinforced PE as an insulating material for HV cables since the resistance to PD is closely related to treeing resistance which is the main electrical degradation mechanism that leads to failure for shielded extruded power cables.