Baudet, D. M., Fernandez-Alonso, F., Kabalu, K., Tack, L., Theunissen, K., Dewaele, S., Eekelers, K., Kadja, G., Mujinga, E., Nseka, P., Phambu, J., Kitambala, N., Kongota, E., Matungila, J., Muanza, M., & Tshibwabwa, A. M. (2013). Notice explicative de la carte géologique de la Province du Bas-Congo et Carte géologique à l’échelle du 1/500.000, Version 1.0, MRAC-CRGM, Inédit.

has been cited by the following article:

• TITLE: Production of an Eco-Cement by Clinker Substitution by the Mixture of Calcined Clay and Limestone, Songololo (DR Congo)

  AUTHORS: Guyghens Bongwele Onanga, Eric Kisonga Manuku, Riadh Ben Khalifa, Daddy Patrick Ilito Lofongo, Alain Preat, Valentin Kanda Nkula, Dominique Wetshondo Osomba

  KEYWORDS: Clay, Calcined Clay, Limestone, Cement, Eco-Cement, Songololo

  JOURNAL NAME: Journal of Geoscience and Environment Protection, Vol.11 No.7, July 14, 2023

  ABSTRACT: Ordinary Portland Cement (OPC) is by mass the largest manufactured product on Earth, responsible for approximately 6% - 8% of global anthropogenic carbon dioxide emissions (CO2) and 35% of industrial CO2 emissions. On average 0.8 to 0.9 ton of CO2 is emitted to produce one ton of OPC. In this paper, partial substitution of clinker (30% - 35%) by the calcined clay-limestone mixture was investigated in order to produce an eco-cement (LC3). Analyzes by XRF, XRD and ATG/ATD have characterized different components, determined the calcination temperature and selected the right clay which can act as effective Supplementary Cementitious Material (SCM). Mechanical tests on mortar carried out over a period of 90 days. The WBCSD/WRI “Greenhouse Gas Protocol” methodology then allowed the calculation of CO2 emissions into the atmosphere. Three types of clay are available in the Songololo Region. The kaolinite is the principal clay mineral and its content varies from 27% to 34%. The sum of kaolinite and amorphous phase which enable clay to react with cementitious material ranges from 57% to 60%. The SiO2 content ranges from 33% to 76%, the Alumina content from 12% to 20% so that the ratio Al2O3/SiO2 is on the higher side (0.17 - 0.53). The calcination window is between 750°C and 850°C and the best clay which can act as SCM identified. The clinker’s substitution reduced CO2 emissions from 0.824 ton of CO2 for one ton of OPC to 0.640 ton of CO2 for one ton of LC3, means 22% less emissions. The compressive strengths developed by LC3 vary from 8.91 to 57.6 MPa (Day 1 to Day 90), exceed those of references 32.5 cement and are close to 42.5 cement. In view of the results, LC3 cement can be considered for industrial trials.