Zhukov, I., et al. (2019) The Impact of Particle Reinforcement with Al2O3, TiB2, and TiC and Severe Plastic Deformation Treatment on the Combination of Strength and Electrical Conductivity of Pure Aluminum. Metals (Basel), 9, Article 65.
https://doi.org/10.3390/met9010065

has been cited by the following article:

• TITLE: Development and Characterization of Aluminium-Based Metal Matrix Composites

  AUTHORS: M. A. Gafur, Al Fahad Ahmed, Raisul Abrar, Surya Sabrin Soshi

  KEYWORDS: Al, AA-6061, AA-4032, SiC, Al2O3, Stir-Casting, Metal Matrix Composite, MMC, Nanocomposites

  JOURNAL NAME: Materials Sciences and Applications, Vol.14 No.1, January 29, 2023

  ABSTRACT: Aluminum based metal matrix composites were fabricated using stir casting where silicon carbide and alumina were the reinforcements. Different types of properties (physical-density, mechanical-tensile, hardness, chemical-corrosion etc.) were measured and compared with base metals/alloys. The properties were significantly varied. The highest density was obtained for pure aluminium with 5% Al2O3 whereas the lowest was obtained for AA-4032 alloy. The highest hardness was obtained for AA-4032 with 5% Al2O3 whereas the lowest was obtained for pure Al with 5% Al2O3. The highest strength was obtained for AA-6061 with 5% coarse SiC whereas the lowest was obtained for pure Al. The highest impact strength was obtained for AA-4032 with 5% Al2O3 whereas the lowest was obtained for AA-6061. The corrosion resistance of all composites was lower than that of the base materials.