Prabu, S.B., Karunamoorthy, L., Kathiresan, S. and Mohan, B. (2006) Influence of Stirring Speed and Stirring Time on Distribution of Particles in Cast Metal Matrix Composite. Journal of Materials Processing Technology, 171, 268-273.
https://doi.org/10.1016/j.jmatprotec.2005.06.071

has been cited by the following article:

• TITLE: Development and Characterization of Aluminium-Based Metal Matrix Composites

  AUTHORS: M. A. Gafur, Al Fahad Ahmed, Raisul Abrar, Surya Sabrin Soshi

  KEYWORDS: Al, AA-6061, AA-4032, SiC, Al2O3, Stir-Casting, Metal Matrix Composite, MMC, Nanocomposites

  JOURNAL NAME: Materials Sciences and Applications, Vol.14 No.1, January 29, 2023

  ABSTRACT: Aluminum based metal matrix composites were fabricated using stir casting where silicon carbide and alumina were the reinforcements. Different types of properties (physical-density, mechanical-tensile, hardness, chemical-corrosion etc.) were measured and compared with base metals/alloys. The properties were significantly varied. The highest density was obtained for pure aluminium with 5% Al2O3 whereas the lowest was obtained for AA-4032 alloy. The highest hardness was obtained for AA-4032 with 5% Al2O3 whereas the lowest was obtained for pure Al with 5% Al2O3. The highest strength was obtained for AA-6061 with 5% coarse SiC whereas the lowest was obtained for pure Al. The highest impact strength was obtained for AA-4032 with 5% Al2O3 whereas the lowest was obtained for AA-6061. The corrosion resistance of all composites was lower than that of the base materials.