TITLE:
Preparation of Flax Residue Activated Carbon by KOH Method and Its Electrode Performance
AUTHORS:
Bing Wang, Shujun Li, Wenying Tan
KEYWORDS:
Flax Residue, Activated Carbon, Activation, Electrochemical Performance, Electrode Material
JOURNAL NAME:
Materials Sciences and Applications,
Vol.12 No.9,
September
26,
2021
ABSTRACT: In this study, activated carbon was prepared by the potassium hydroxide activation method with flax residues as raw materials. High-quality activated carbon was prepared by single factor and orthogonal experiments. Iodine adsorption and methylene blue adsorption were used as performance indicators. As prepared activated carbon was characterized by XRD, XPS and SEM. The results showed that the optimized electrode material was prepared under an impregnation ratio of 1:2, activation temperature of 800°C and activation time of 100 min. The yield of activated carbon was 49.48%, the iodine value was 1667.13 mg/g and the methylene blue value was 429 mg/g. The specific surface area measured by the automatic porosity analyzer is 1221 m2/g, and the mass-specific capacitance is 215.7 F/g under current density of 0.1 A/g.