Assmann, J., Crihan, D., Knapp, M., Lundgren, E., Löffler, E., Muhler, M., Narkhede, V., Over, H., Schmid, M., Seitsonen, A.P. and Varga, P. (2005) Understanding the Structural Deactivation of Ruthenium Catalysts on an Atomic Scale under both Oxidizing and Reducing Conditions. Angewandte Chemie International Edition, 44, 917-920.
https://doi.org/10.1002/anie.200461805

has been cited by the following article:

• TITLE: Ruthenium Catalyst Supported on Multi-Walled Carbon Nanotubes for CO Oxidation

  AUTHORS: Camila Emilia Kozonoe, Reinaldo Giudici, Martin Schmal

  KEYWORDS: Multi-Walled Carbon Nanotubes, Ruthenium, CO Oxidation

  JOURNAL NAME: Modern Research in Catalysis, Vol.10 No.3, July 26, 2021

  ABSTRACT: This work proposes the synthesis of the 5%wt Ru on MWCNT catalyst and the influence of feed rate and testing variables for low-temperature oxidation affecting the CO2 yield. Morphology and incorporation of the nanoparticles in carbon nanotubes were investigated by specific surface area (BET method); thermogravimetric analyses (TGA); X-ray diffraction; Raman spectroscopy, transmission electron microscopy (TEM) and XPS. The conversions of CO and O2 were mostly 100% in groups C1 and C2 (temperature between 200 and 500°C with low WHSV). In order to assess the effect of mass on catalytic activity, condition C3 was tested at even lower temperatures. In the tested catalyst, high activity (100% CO and O2 conversion) was observed, keeping it active under reaction conditions, suggesting oxi-reduction of the RuO2 at surface without affecting the MWCNT but Lewis acid influencing the CO2 yield.