Tchamba, A.B., Melo, U.C., Yongue, R. and Njopwouo, D. (2011) Phase and Microstructure Evolution during Densification of Bauxite of Haleo-Danielle (Minim-Martap, Cameroon) between 1000 and 1600 C. International Journal of Materials Science, 6, 89-100.

has been cited by the following article:

• TITLE: Physicochemical Characterisation for Potential Uses as Industrial Mineral of Bauxite from Débélé, Guinea

  AUTHORS: Mamadou Yaya Balde, Chantale Njiomou Djangang, Ramatoulaye Binta Diallo, Philippe Blanchart, Daniel Njopwouo

  KEYWORDS: Bauxite, Characteristics, Industrial Mineral, Guinea

  JOURNAL NAME: Journal of Materials Science and Chemical Engineering, Vol.9 No.3, March 22, 2021

  ABSTRACT: Assessing the potential uses as industrial mineral, bauxite from Débélé, Guinea, has been characterised by chemical and mineralogical analyses, the determination of the amorphous content, the rate of portlandite consumption in an aqueous solution, the strength activity index, and the thermal behaviour up to 1200°C. It was evidenced that the raw sample is gibbsite-rich type bauxite with about 45.06 wt% of alumina, 23.80 wt% of iron oxide, and 1.74 wt% of silica. It meets the chemical composition required for bauxites used for refractory cement. During heating, the raw bauxite undergoes high densification with low linear shrinkage, motivating a potential use in dense ceramic compositions with high thermal stability. Also, the heating at only 600°C gives a significant pozzolanic activity in combination with Portland cement. The correlation between the pozzolanicity, the amorphous phase content, and the specific surface area indicated that the raw and the calcined materials present an interesting reactivity for using them in alternative cement formulations.