He, H.B., Wang, Y., Long, J.J. and Chen, Z.H. (2013) Corrosion of NiFe2O4-10NiO-Based Cermet Inert Anodes for Aluminium Electrolysis. Transactions of Nonferrous Metals Society of China, 23, 3816-3821.
https://doi.org/10.1016/S1003-6326(13)62934-9

has been cited by the following article:

• TITLE: Electrochemical Degradation Mechanism of a Cermet Anode for Aluminum Production

  AUTHORS: P. Meyer, L. Massot, M. Gibilaro, S. Bouvet, V. Laurent, A. Marmottant, P. Chamelot

  KEYWORDS: Metal/Oxide Electrode, Aluminium Electrolysis, Oxidation Reaction Mechanism

  JOURNAL NAME: Materials Sciences and Applications, Vol.10 No.9, September 19, 2019

  ABSTRACT: Tests on (NixFeyO4 - Ni1?xFexO)/(CuxNiyFez) cermets, considered as promising anode for the aluminium production, were performed under electrolysis at 0.8 A·cm-2 in molten mixture of cryolite at 960°C. In order to predict phase compositions, a thermodynamic study was performed and experimentally verified by SEM-EDS analysis. The metallic phase oxidation leads to the formation of different phases such as FeF2, Ni0.90Fe0.10O, NiF2 and Cu2O phases, while NixFe3-xO4 spinel is continuously enriched up to x = 0.90, the thermodynamically stable nickel composition. When the cermet material is fully oxidized, metallic and oxide phases are converted into soluble or non-conductive phases, leading to the end of anode service life.