K. T. Park, J. H. Park, Y. S. Lee and W. J. Nam, “Comparison of Compressive Deformation of Ultrafine-Grain- ed 5083 Al Alloy at 77 and 298 K,” Metallurgical and Materials Transactions: A, Vol. 36, 2005, pp. 1365-1368. doi: 10.1007/s11661-005-0227-8

has been cited by the following article:

• TITLE: Effect of Hot Accumulative Roll Bonding Process on the Mechanical Properties of AA5083

  AUTHORS: Hassan Sheikh, Ebrahim Paimozd

  KEYWORDS: Grain refinement; Aaccumulative Roll Bonding; Mechanical Characterization; Aluminum Alloys

  JOURNAL NAME: Open Journal of Metal, Vol.1 No.1, September 28, 2011

  ABSTRACT: In this work, accumulative roll bonding (ARB) process as a severe plastic deformation was applied on an AA5083 sheet up to 6 cycles at the temperature of 300℃ and at the strain rate of 50 s­‐1. The results of tensile tests show that the values of the yield stress and the ultimate tensile strength don't change considerably after 4 cycles. Also, transmission electron microscopy (TEM) micrograph confirmed that the microstructure has fine (sub) grains with the size of 200 nm - 400 nm.