K. F. Zhang and H. H. Yan, “Deformation Behavior of Fine-Grained 5083 Al Alloy at Elevated Temperature,” Transactions of Non-ferrous Metals Society of China,Vol. 19, 2009, pp. 307-311. doi:10.1016/S1003-6326(10)60060-X

has been cited by the following article:

• TITLE: Effect of Hot Accumulative Roll Bonding Process on the Mechanical Properties of AA5083

  AUTHORS: Hassan Sheikh, Ebrahim Paimozd

  KEYWORDS: Grain refinement; Aaccumulative Roll Bonding; Mechanical Characterization; Aluminum Alloys

  JOURNAL NAME: Open Journal of Metal, Vol.1 No.1, September 28, 2011

  ABSTRACT: In this work, accumulative roll bonding (ARB) process as a severe plastic deformation was applied on an AA5083 sheet up to 6 cycles at the temperature of 300℃ and at the strain rate of 50 s­‐1. The results of tensile tests show that the values of the yield stress and the ultimate tensile strength don't change considerably after 4 cycles. Also, transmission electron microscopy (TEM) micrograph confirmed that the microstructure has fine (sub) grains with the size of 200 nm - 400 nm.