Shinohara, N., Okumiya, M., Hotta, T., Nakahira, K., Naito, M. and Uematsu, K. (1999) Formation Mechanisms of Processing Defects and Their Relevance to the Strength in Alumina Ceramics Made by Powder Compaction Process. Journal of Materials Science, 34, 4271-4277.
https://doi.org/10.1023/A:1004611105281

has been cited by the following article:

• TITLE: Green Microstructural Visualization of Dry-Pressed Spray-Dried Alumina (Al2O3)

  AUTHORS: Ian P. Maher, Richard A. Haber

  KEYWORDS: Spray-Dried Alumina, Uniaxial Dry-Pressing, SEM, Green Microstructural Imaging

  JOURNAL NAME: Materials Sciences and Applications, Vol.9 No.12, November 15, 2018

  ABSTRACT: Slurry parameters were controlled prior to spray-drying to visualize and govern an understanding of which parameters govern hollow coring and granule morphology during spray-drying. An aqueous alumina using a polyvinyl alcohol binder (PVA) system was analyzed and granules were processed by altering the slurry specific gravity and viscosity value prior to spray-drying. Spray-dried granules were uniaxial dry-pressed at varying moisture contents to show the plasticizing effects of moisture during compaction. A novel characterization method using a field emission electron microscope (FESEM) was implemented to image the green microstructures of the granules and compacted samples. Slurries with a higher specific gravity and viscosity resulted in denser granules with spherical shapes. Viscosity affected the binder segregation during the spray-drying process. Granules stored at higher moisture contents resulted in denser compacts with fewer intergranular pores and cracks along granule boundaries. Using a FESEM resulted in higher resolution for green microstructural characterization.