• TITLE: Magnetic and Electrical Properties of Gd Doped Ni-Cu-Zn-Fe2O4

  AUTHORS: P. Venkata Srinivasa Rao, T. Anjaneyulu, D. V. Krishna Reddy, M. Rami Reddy

  KEYWORDS: Ni-Cu-Zn-Gd Nanoferrites, Magnetic Properties, Electrical Properties

  JOURNAL NAME: Advances in Materials Physics and Chemistry, Vol.8 No.10, October 18, 2018

  ABSTRACT: Ni0.5Cu0.25Zn0.25GdxFe2-xO4 (x = 0.0, 0.025, 0.05, 0.075, 0.1) ferrites were synthesized using an oxalic-based precursor method. The TC for all the Ni0.5Cu0.25Zn0.25GdxFe2-xO4 (x = 0.0, 0.025, 0.05, 0.075, 0.1) samples was measured by using one of the double coil susceptibility setup. In all the samples it is observed that, at a certain temperature, susceptibility falls to zero indicating the Curie temperature (TC) and ferrimagnetic samples are converted into paramagnetic sample at that temperature. The electrical properties were investigated for these samples. Dielectric properties and ρdc properties were observed to decrease with the increase in the frequency for all the Gd doped ferrite samples.