Shi, H., McLaren, J., Sellars, C.M., Shahani, R. and Bolingbroke, R. (1997) Constitutive Equations for High Temperature Flow Stress of Aluminum Alloys. Materials Science and Technology, 13, 210-216.
https://doi.org/10.1179/mst.1997.13.3.210

has been cited by the following article:

• TITLE: High Temperature Deformation Behavior of TC17 Alloy

  AUTHORS: Chen Wang

  KEYWORDS: TC17 Alloy, High Temperature Deformation, Flow Stress Model, Microstructure, Dynamic Recovery

  JOURNAL NAME: Materials Sciences and Applications, Vol.9 No.9, August 13, 2018

  ABSTRACT: The high temperature deformation behavior and microstructures evolution of TC17 alloy in the temperature range of 820°C - 930°C, strain rate range of 0.01 s-1 - 10 s-1 and height direction reduction of 20% - 80% have been studied by hot compressing testing. The microstructures of TC17 alloy were observed and analyzed using Olympus/PMG3 optical microscope. The flow stresses were correlated with strain rate and the temperature by the constitutive equation. The results show that the flow stress of TC17 alloy increase quickly with the strain, then decrease with a steady value. The deformation activation energy obtained in the α + β region for TC17 was 407 kJ/mol, and in the β region was 155 kJ/mol. It was also found that the degree of dynamic globularization of α phase increases with increasing strains, increasing temperature and decreasing strain rate in α + β region, the dynamic re-crystallization is obvious at low strain rate and dynamic recovery is obvious at high strain rate in β region.